We develop a new method using binary collision approximation simulating the Rutherford backscattering spectrometry in channeling conditions (RBS/C) from molecular dynamics atom coordinates of irradiated cells. The approach allows comparing experimental and simulated RBS/C signals as a function of depth without fitting parameters. The simulated RBS/C spectra of irradiated Ni and concentrated solid solution alloys (CSAs, NiFe and NiCoCr) show a good agreement with the experimental results. The good agreement indicates the damage evolution under damage overlap conditions in Ni and CSAs at room temperature is dominated by defect recombination and migration induced by irradiation rather than activated thermally. GRAPHICAL ABSTRACT IMPACT STATEMENT

Mechanical properties such as hardness and modulus of sodium borosilicate (NBS) glasses in irradiation conditions were studied extensively in recent years. With irradiation of heavy ions, a trend that the hardness of NBS glasses decreased and then stabilized with increase of dose has been reported. Variations in network structures were suggested for the decrease of hardness after irradiation. However, details of these variations in a network of glass are not clear yet. In this paper, molecular dynamics was applied to simulate the network variations in a type of NBS glass and the changes in hardness after xenon irradiation. The simulation results indicated that hardness variation decreased with fluence in an exponential law, which was consistent with experimental results. The origin of hardness decrease after irradiation might be attributed to the break of B^iv–O links that could be derived from the (1) decrease of average coordinate number of boron, (2) decrease of Si–O–B^iv bonds, and (3) increase of non-bridging oxygen.

In this work, we review current trends in China to investigate beam plasma interaction phenomena. Recent progresses in China on low energy heavy ions and plasma interaction, ion beam-plasma interactions under the influences of magnetic fields, high energy heavy ion radiography through marginal range method, energy deposition of highly charged ions on surfaces and Raman spectroscopy of surfaces after irradiation of highly charged ions are presented.