Mechanical properties such as hardness and modulus of sodium borosilicate (NBS) glasses in irradiation conditions were studied extensively in recent years. With irradiation of heavy ions, a trend that the hardness of NBS glasses decreased and then stabilized with increase of dose has been reported. Variations in network structures were suggested for the decrease of hardness after irradiation. However, details of these variations in a network of glass are not clear yet. In this paper, molecular dynamics was applied to simulate the network variations in a type of NBS glass and the changes in hardness after xenon irradiation. The simulation results indicated that hardness variation decreased with fluence in an exponential law, which was consistent with experimental results. The origin of hardness decrease after irradiation might be attributed to the break of B^iv–O links that could be derived from the (1) decrease of average coordinate number of boron, (2) decrease of Si–O–B^iv bonds, and (3) increase of non-bridging oxygen.

In this work, we review current trends in China to investigate beam plasma interaction phenomena. Recent progresses in China on low energy heavy ions and plasma interaction, ion beam-plasma interactions under the influences of magnetic fields, high energy heavy ion radiography through marginal range method, energy deposition of highly charged ions on surfaces and Raman spectroscopy of surfaces after irradiation of highly charged ions are presented.

Vitrification is widely recognized as a promising method for the geological disposal of high-level radioactive waste (HLW) worldwide. To ensure the safe disposal of radioactive waste, the borosilicate glass that vitrifies HLW must exhibit exceptional water resistance to prevent the possibility of groundwater corrosion and subsequent radioactive leaks. Radiation might change the water resistance of borosilicate glass. A series of zirconium-containing borosilicate glass with an irradiation dose of 0.3 dpa were utilized to examine the radiation effect on glass-water interaction. Scanning electron microscopy (SEM), Time-of-Flight Secondary ion mass spectrometry (ToF-SIMS), X-ray photoelectron spectroscopy (XPS), Inductively Coupled Plasma Optical Emission spectroscopy (ICP-OES) and Fourier transform infrared spectroscopy (FTIR) were used to investigate the leaching behavior of the non- and irradiated samples. The depth profile of the leached samples implied the interdiffusion dominated glass-water interaction. The results from FTIR and ICP-OES indicated that, after irradiation, the initial leaching rate increased by threefold. Additionally, the impact of different zirconium contents on the water resistance of borosilicate glass was also presented.