Graphite/Al composites had attracted significant attention for thermal management applications due to their excellent thermal properties. However, the improvement of thermal properties was restricted by the insufficient wettability between graphite and Al. In this study, silicon carbide and titanium carbide coatings have been uniformly coated on the graphite by the reactive sputtering method, and Graphite/Al laminate composites were fabricated by a hot isostatic pressing process to investigate the influence on thermal conductivity and mechanical properties. The results show that carbide coating can effectively improve the interfacial thermal conductance of SiC@Graphite/Al and TiC@Graphite/Al composites by 9.8 times and 3.4 times, respectively. After surface modification, the in-plane thermal conductivity (TC) of the composites with different volume fractions are all exceeding the 90% of the predictions. In comparison, SiC is more conducive to improving the thermal conductivity of composite materials, since the thermal conductivity of the 28.7 vol.% SiC@Graphite/Al reached the highest value of 499 W/m·K, while TiC is favorable for improving the mechanical properties. The finding is beneficial to the understanding of carbide coating engineering in the Graphite/Al composites.

Graphite/Al composites have attracted much attrition due to their excellent thermal properties. However, the improvement of thermal conductivity (TC) is limited by the difficulty in controlling the orientation of graphite and the poor wettability between graphite and aluminum. In this study, a novel process for fabricating the Graphite/Al composites is proposed, which involves fabricating graphite film and aluminum foil into laminate material. Then, taking a rolling method, the fractured and well oriented graphite film can help the composite achieve high TC while maintaining a certain strength. The result reveals that both single and total reduction have a significant influence on the diameter and orientation of the graphite, and by adjusting the process parameters, composites with high TC can be acquired at a relatively low reinforcement volume. This near-net-forming process can directly meet the thickness requirements for electronic packaging and avoids the exposure of graphite to the surface during secondary processing, which is promising to promote the application for high TC Graphite/Al composites in thermal management.