Bamboo delignification is a common method for studying its functional value-added applications. In this study, bamboo samples were delignified by treatment with sodium chlorite. The effects of this treatment on the bamboo’s microstructure, surface chemical composition, and pyrolysis behaviour were evaluated. Field-emission scanning electron microscopy (FE-SEM), Fourier-transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD) were conducted to evaluate these parameters. The FTIR results demonstrated that the lignin peak decreased or disappeared, and some hemicellulose peaks decreased, indicating that sodium chlorite treatment effectively removed lignin and partly decomposed hemicellulose, although cellulose was less affected. The XPS results showed that, after treatment, the oxygen-to-carbon atomic ratio of delignified bamboo increased from 0.34 to 0.45, indicating a lack of lignin. XRD revealed increased crystallinity in delignified bamboo. Further pyrolysis analysis of treated and untreated bamboo showed that, although the pyrolysis stage of the delignified bamboo did not change, the maximum thermal degradation rate (R_max) and its corresponding temperature (from 353.78 to 315.62 °C) decreased significantly, indicating that the pyrolysis intensity of the bamboo was weakened after delignification. Overall, this study showed that delignified bamboo develops loose surfaces, increased pores, and noticeable fibres, indicating that alkali-treated bamboo has promising application potential due to its novel and specific functionalities.

Bamboo and its products are widely used in indoor and outdoor fields. Photodegradation occurs easily on the surface when bamboo is exposed to ultraviolet (UV) light from solar radiation. This induces surface discoloration and degrades the physical properties of bamboo, which not only negatively affects its utility and aesthetic characteristics but also restricts its application in outdoor environments. In this work, we review the mechanism of bamboo photodegradation, in which the behavior of lignin is key. The changes in bamboo's microstructure, surface color, and chemical composition during photodegradation are described in detail. Methods for enhancing its photostability, including the application of transparent coatings containing UV absorbers and hindered amine light stabilizer compounds on bamboo surfaces, are then systematically summarized, and potential approaches to combat the photodegradation of bamboo surfaces are discussed. On the basis of the recent advances of photodegradation and photostability of bamboo, this review provides new insights into the scientific application and protection of bamboo in the outdoor field.

In view of the long-term utilization history as a building and furniture making material in southeast Asian countries, Thyrsostachys oliveri is considered to have great utilization potential. However, little is known about the quantitative morphological characteristics and comprehensive material properties of its culm. In this study, we systematically investigated the morphological characteristics, the chemical components, and the physical–mechanical properties of the three-year-old culm of T. oliveri. The morphological analysis result showed that the internode length, the diameter of internodes and the wall thickness changed with the culm height. The volume of the culm wall of a single internode increased before the 10th internode, and then it decreased to a significant level at the 20th internode. The basic chemical compositions (cellulose, hemicellulose, lignin and silicon content) of the culm wall were 346.19 mg/g, 95.32 mg/g, 33.17%, and 3.39 mg/g, respectively. These component contents were relatively stable in the bottom and middle part of the culm, but changed significantly in the upper part of the culm. The moisture content and the base density of the culm wall were 73.01% and 0.64 g/cm³, respectively. The culm wall shrinkage rate in the radial, tangential direction as well as the volumetric shrinkage reached the minimum value in the middle part of the culm. The average compressive strength, modulus of rupture and modulus of elasticity of the culm wall were 67.03 MPa, 143.74 MPa, and 7.99 GPa, respectively. These results provide valuable reference data for more rational use of this bamboo resources.

Surface photostability strongly influences the usefulness of bamboo and bamboo-based polymer composites in outdoor environments. In this study, accelerated aging tests were conducted to investigate how UV irradiation affects the color, surface appearance, and chemical characteristics of outdoor bamboo-fiber-reinforced composite (OBFRC) prepared from moso bamboo (Phyllostachys pubescens Mazel) by a three-step process involving phenol-formaldehyde (PF) resin impregnation. The surface color of natural bamboo (NB) changes rapidly during irradiation, but that of OBFRC remains relatively stable: densification mitigates the negative effects of UV irradiation. More generally, OBFRC exhibits enhanced surface photostability caused by structural and chemical modifications.