In view of the long-term utilization history as a building and furniture making material in southeast Asian countries, Thyrsostachys oliveri is considered to have great utilization potential. However, little is known about the quantitative morphological characteristics and comprehensive material properties of its culm. In this study, we systematically investigated the morphological characteristics, the chemical components, and the physical–mechanical properties of the three-year-old culm of T. oliveri. The morphological analysis result showed that the internode length, the diameter of internodes and the wall thickness changed with the culm height. The volume of the culm wall of a single internode increased before the 10th internode, and then it decreased to a significant level at the 20th internode. The basic chemical compositions (cellulose, hemicellulose, lignin and silicon content) of the culm wall were 346.19 mg/g, 95.32 mg/g, 33.17%, and 3.39 mg/g, respectively. These component contents were relatively stable in the bottom and middle part of the culm, but changed significantly in the upper part of the culm. The moisture content and the base density of the culm wall were 73.01% and 0.64 g/cm³, respectively. The culm wall shrinkage rate in the radial, tangential direction as well as the volumetric shrinkage reached the minimum value in the middle part of the culm. The average compressive strength, modulus of rupture and modulus of elasticity of the culm wall were 67.03 MPa, 143.74 MPa, and 7.99 GPa, respectively. These results provide valuable reference data for more rational use of this bamboo resources.

The enormous pressures of energy consumption and the severe pollution produced by non-renewable resources have prompted researchers to develop various environmentally friendly energy-saving materials. Transparent bamboo represents an emerging result of biomass material research that has been identified and studied for its many advantages, including light weight, excellent light transmittance, environmental sustainability, superior mechanical properties, and low thermal conductivity. The present review summarizes methods for preparing transparent bamboo, including delignification and resin impregnation. Next, transparent bamboo performance is quantified in terms of optical, mechanical, and thermal conductivity characteristics and compared with other conventional and emerging synthetic materials. Potential applications of transparent bamboo are then discussed using various functionalizations achieved through doping nanomaterials or modified resins to realize advanced energy-efficient building materials, decorative elements, and optoelectronic devices. Finally, challenges associated with the preparation, performance improvement, and production scaling of transparent bamboo are summarized, suggesting opportunities for the future development of this novel, bio-based, and advanced material.

Compared with wood, bamboo has a special fiber gradient structure. Bamboo fibers have attracted attention as reinforced polymer composites. This study investigated the effects of lamination and fiber volume on the physical and mechanical properties of bamboo laminated composites (BLCs). Six types of BLC were derived by parallel and cross laminating bamboo veneers with high, middle, and low fiber volumes. The results indicated that the laminated structure and fiber volume significantly influenced the BLC properties. Microstructural analysis showed that parallel lamination and low fiber volume were more conducive to resin penetration and enhanced the bonding strength. Both the bending and tensile strengths of the cross lamination were lower than those of the parallel lamination. BLCs made of veneers with high and middle fiber volumes and parallel lamination had the maximum bending and tensile strengths (145.1 and 101.53 MPa, respectively). When tested for water resistance, parallel and cross lamination inhibited expansion in the thickness (TSR, 0.56–2.14%) and width (WSR, 0.07–1.61%) directions, respectively. Laminated structures and veneers with varying fiber volume contents should be chosen according to the specific application scenarios. This study provides a reference for selecting an appropriate BLC structure and fiber volume based on application.

An important principle in rational manufacturing design is matching the properties of composites to their intended uses. Herein, six laminated composites (LCs) were manufactured using fibrous moso bamboo and poplar veneer units, and their pore structure, water resistance, and mechanical properties were evaluated. The LC density (640–1290 kg/m³) increased significantly with increasing bamboo veneer unit content. The LC surface texture and roughness depended on the density and type of surface layer. With increasing LC density, the water absorption rate (WAR), width swelling rate (WSR), and thickness swelling rate (TSR) decreased exponentially and the mechanical properties increased linearly. This behavior was closely related to the changes in pore structure caused by density. Notably, the water resistance and mechanical properties of the LCs with densities higher than 910 kg/m³ were superior to the highest levels specified in GB/T 20241–2006 for ‘‘laminated veneer lumber’’ and GB/T 30364–2013 for “bamboo scrimber flooring”. Thus, these engineered materials are promising for outdoor structures and flooring.