The photocatalytic degradation of 4-chlorophenol in water using Ru-doped ZnO mixed oxides (0, 0.5, 1, and 3 wt% RuO₂) synthesized by the one-pot homogeneous coprecipitation method is reported. ZnO with wurtzite structure was present in the mixed oxide as corroborated by Raman spectroscopy and X-ray diffraction analysis. All the samples showed nanorod morphological features. The presence of Ru⁶⁺/Ru⁴⁺ couples on ZnO modified the band gap of the mixed oxides and led to a shift of the band gap energy from 3.20 eV to 3.07 eV. Ru addition increased the surface area and significantly promoted the formation of active surface oxygen species such as hydroradicals evidenced by the fluorescence spectroscopy measurement. In the photodegradation of 4-chlorophenol solution under UV irradiation, a notable increase in photoactivity was obtained as the amount of RuO₂ in the mixed oxides increased to 3 wt%. The charge transfer between Ru⁶⁺/Ru⁴⁺ couples and ZnO nanoparticles together with the formation of free radical oxidant species effectively inhibits electron-hole recombination rate, thus favoring the photodegradation of 4-chlorophenol.

This work investigates biodiesel production via transesterification of Mexican palm oil with methanol catalyzed by binary solid base core–shell catalysts with improved catalytic stability. A series of CaO–ZnO mixed solids were prepared using an inexpensive co–precipitation method by varying ZnO content from 5 to 20 mol%. Several factors, such as surface basicity, ZnO content, phase compositions, and thermal treatment of the catalysts, were all proven to be crucial for the production of biodiesel with good quality. Thermal treatment could effectively remove the surface adsorbed water and impurities and improved the catalytic activity. The addition of ZnO to CaO significantly enhanced the catalysts’ stability; however, it led to lower surface basicity and slightly diminished catalytic activity. ZnO doping inhibited the formation of surface Ca(OH)₂ and promoted the formation of Ca–Zn–O or CaZn₂(OH)₆ phase as the core and a surface CaCO₃ shell, which effectively decreased Ca²⁺ leaching by approximately 74% in methanol and 65% in a methanol–glycerol (4:1) mixture. A combined method of separation and purification for obtaining clean biodiesel with high quality was proposed. The biodiesel obtained under the control conditions exhibited properties which satisfied the corresponding standards well.