This work investigates biodiesel production via transesterification of Mexican palm oil with methanol catalyzed by binary solid base core–shell catalysts with improved catalytic stability. A series of CaO–ZnO mixed solids were prepared using an inexpensive co–precipitation method by varying ZnO content from 5 to 20 mol%. Several factors, such as surface basicity, ZnO content, phase compositions, and thermal treatment of the catalysts, were all proven to be crucial for the production of biodiesel with good quality. Thermal treatment could effectively remove the surface adsorbed water and impurities and improved the catalytic activity. The addition of ZnO to CaO significantly enhanced the catalysts’ stability; however, it led to lower surface basicity and slightly diminished catalytic activity. ZnO doping inhibited the formation of surface Ca(OH)₂ and promoted the formation of Ca–Zn–O or CaZn₂(OH)₆ phase as the core and a surface CaCO₃ shell, which effectively decreased Ca²⁺ leaching by approximately 74% in methanol and 65% in a methanol–glycerol (4:1) mixture. A combined method of separation and purification for obtaining clean biodiesel with high quality was proposed. The biodiesel obtained under the control conditions exhibited properties which satisfied the corresponding standards well.

Metal-organic frameworks (MOFs) have been an excellent platform for carbon dioxide reduction reactions (CO₂RR). In this work, the feasibility of electrochemical reduction of CO₂ to obtain C₂-deep value-added products was investigated by the preparation of Mg-containing MOF-74 samples combined with transition metal cations (Ni²⁺, Co²⁺ and Zn²⁺). The prepared MOFs were used as electrocatalysts in CO₂RR. Chronoamperometric analysis coupled to ATR-FTIR spectroscopy was employed to characterize the CO₂ reduction products and subsequently via ¹H NMR. Although an isostructural crystalline structure was observed in all synthesized MOFs, the pore diameter distribution was significantly affected due to the Mg coordination along with each transition metal nuclei with the organic ligand to form the MOF-74. Our results showed that Mg-containing MOF-74 electrocatalysts combined with Ni, Co and Zn ions successfully reduced CO₂ to C₂-deep products, while the monometallic Mg-MOF-74 showed only CO₂ mineralization. An ester acetate, isopropyl alcohol, and formic acid were produced by Mg/Ni-MOF-74; isopropyl alcohol was provided by Mg/Co-MOF-74, and ethanol was generated by Mg/Zn-MOF-74. We observed that the change of the transition cation was a key factor in the selectivity of the obtained products, while the degree of Mg ions effectively incorporated into the MOF structure tuned the porosity and the electrocatalytic activity. Among them, Mg/Zn-MFOF-74 showed the highest Mg content loaded after synthesis and thus the most favorable electrocatalytic behavior towards CO₂ reduction.

This study aimed to synthesize a multicationic hydrotalcite and transform it into mixed oxide nanostructures (ZnO/TiO₂/CeO₂/Al₂O₃, referred to as MixO) to serve as a heterogeneous photocatalyst for degrading various pollutants, including methylene blue (MB), methyl orange (MO), paracetamol (PA), and paraquat (PQ). The hydrotalcite was synthesized via an ultrasound-assisted method and calcined at 700 °C to obtain the corresponding mixed metal oxide. A comprehensive characterization of both the multicationic hydrotalcite (MC-LDH) and the mixed metal oxides (MixO) was performed using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), N₂ adsorption–desorption, Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, and pH_PZC analysis. The MixO sample exhibited an optical bandgap of 3.19 eV. Photocatalytic performance was evaluated during 240 min of UV irradiation, demonstrating high degradation efficiencies attributable to the synergistic interactions among ZnO, TiO₂, and CeO₂. Degradation efficiencies reached 99.3% for MO and 95.2% for MB, while PA and PQ showed moderate degradation rates of 60% and 15%, respectively. The degradation kinetics of all pollutant compounds followed the Langmuir–Hinshelwood model. Additionally, the MixO catalyst maintained consistent performance over four consecutive degradation cycles, highlighting its reusability and stability. These findings underscore the potential of MixO mixed oxide nanostructures as practical and recyclable photocatalysts for environmental remediation, particularly in wastewater treatment applications.