A modified Ångström method was used to determine the thermal diffusivity and thermal conductivity of aqueous dispersions of multiwalled carbon nanotubes as a function of their weight fraction concentration and in the presence of an externally applied electric field. Measurements were performed in planar samples, with a fixed thickness of 3.18 mm applying an AC voltage in the range from 0 to 70 V R M S and for concentrations of carbon nanotubes from 0 to 2 wf%. It is shown that this field induces the formation of clusters followed by their alignment along the electric field, which can favor heat transfer in that direction. Heat transfer measurements show two regimes, in the first one under 0.5 wf%, voltages lower than 30 V R M S are not strong enough to induce the adequate order of the carbon nanostructures, and as a consequence, thermal diffusivity of the dispersion remains close to the thermal diffusivity of water. In contrast for higher concentrations (above 1.5 wf%), 10 V R M S are enough to get a good alignment. Above such thresholds of concentrations and voltages, thermal diffusivity and conductivity increase, when the electric field is increased, in such a way that for an applied voltage of 20 V R M S and for a concentration of 1.5 wf%, an increase of 49% of the thermal conductivity was obtained. It is also shown that this approach exhibits limits, due to the fact that the electric-field induced structure, can act as a heating element at high electric field intensities and carbon nanotubes concentrations, which can induce convection and evaporation of the liquid matrix.

In recent years, polymer engineering, at the molecular level, has proven to be an effective strategy to modulate thermal conductivity. Polymers have great applicability in the food packaging industry, in which transparency, lightness, flexibility, and biodegradability are highly desirable characteristics. In this work, a possible manner to adjust the thermal conductivity in cassava starch biopolymer films is presented. Our approach is based on modifying the starch molecular structure through the addition of borax, which has been previously used as an intermolecular bond reinforcer. We found that the thermal conductivity increases linearly with borax content. This effect is related to the crosslinking effect that allows the principal biopolymer chains to be brought closer together, generating an improved interconnected network favoring heat transfer. The highest value of the thermal conductivity is reached at a volume fraction of 1.40% of borax added. Our analyses indicate that the heat transport improves as borax concentration increases, while for borax volume fractions above 1.40%, heat carriers scattering phenomena induce a decrement in thermal conductivity. Additionally, to obtain a deeper understanding of our results, structural, optical, and mechanical characterizations were also performed.

Concentrating solar power (CSP) systems use solar absorbers to convert sunlight into thermal electric power. In CSP systems, a high reflective surface focuses sunlight onto a receiver that captures the solar energy and converts it into heat. The operation of high efficiency CSP systems involves improvements in the performance of the coatings of the solar absorption materials. To accomplish this, novel, more efficient selective coatings are being developed with high solar absorptance and low thermal losses at their operation temperature. Heat losses in a CSP system occur by three mechanisms: conduction, convection and radiation. It has been widely documented that energy losses increase with increasing operating temperature of CSP systems, and the precise knowledge of the thermophysical properties of the materials involved in CSP systems may allow us to increase the efficiency of systems. In this work, we applied the pulsed photoradiometry technique (PPTR) to evaluate the changes in the thermophysical properties of selective coatings on a variety of substrates as a function of temperature. Three types of coatings deposited with two different techniques on three types of substrate were examined: commercial coatings based on titanium oxynitride deposited by sputtering on substrates of copper and aluminum, coatings based on black nickel deposited by electrochemical methods on substrates of steel, and coatings based on black cobalt deposited by electrochemical methods on substrates of steel and copper. Values of the thermal diffusivity and thermal conductivity were obtained in the temperature range of 25 to 550 °C. Optical reflectance measurements have been performed in order to provide an estimate of the dependence of the thermal emittance on temperature using the black body radiation theory.