Demineralized dentin matrix (DDM)-based materials have been actively developed and are well-known for their excellent performance in dental tissue regeneration. However, DDM-based bio-ink suitable for fabrication of engineered dental tissues that are patient-specific in terms of shape and size, has not yet been developed. In this study, we developed a DDM particle-based bio-ink (DDMp bio-ink) with enhanced three-dimensional (3D) printability. The bio-ink was prepared by mixing DDM particles and a fibrinogen–gelatin mixture homogeneously. The effects of DDMp concentration on the 3D printability of the bio-ink and dental cell compatibility were investigated. As the DDMp concentration increased, the viscosity and shear thinning behavior of the bio-ink improved gradually, which led to the improvement of the ink’s 3D printability. The higher the DDMp content, the better were the printing resolution and stacking ability of the 3D printing. The printable minimum line width of 10% w/v DDMp bio-ink was approximately 252 μm, whereas the fibrinogen–gelatin mixture was approximately 363 μm. The ink’s cytocompatibility test with dental pulp stem cells (DPSCs) exhibited greater than 95% cell viability. In addition, as the DDMp concentration increased, odontogenic differentiation of DPSCs was significantly enhanced. Finally, we demonstrated that cellular constructs with 3D patient-specific shapes and clinically relevant sizes could be fabricated through co-printing of polycaprolactone and DPSC-laden DDMp bio-ink.

3D printed biomaterials have been extensively investigated and developed in the field of bone regeneration related to clinical issues. However, specific applications of 3D printed biomaterials in different dental areas have seldom been reported. In this study, we aimed to and successfully fabricated 3D poly (lactic-co-glycolic acid)/β-tricalcium phosphate (3D-PLGA/TCP) and 3D β-tricalcium phosphate (3D-TCP) scaffolds using two relatively distinct 3D printing (3DP) technologies. Conjunctively, we compared and investigated mechanical and biological responses on human dental pulp stem cells (hDPSCs). Physicochemical properties of the scaffolds, including pore structure, chemical elements, and compression modulus, were characterized. hDPSCs were cultured on scaffolds for subsequent investigations of biocompatibility and osteoconductivity. Our findings indicate that 3D printed PLGA/TCP and β-tricalcium phosphate (β-TCP) scaffolds possessed a highly interconnected and porous structure. 3D-TCP scaffolds exhibited better compressive strength than 3D-PLGA/TCP scaffolds, while the 3D-PLGA/TCP scaffolds revealed a flexible mechanical performance. The introduction of 3D structure and β-TCP components increased the adhesion and proliferation of hDPSCs and promoted osteogenic differentiation. In conclusion, 3D-PLGA/TCP and 3D-TCP scaffolds, with the incorporation of hDPSCs as a personalized restoration approach, has a prospective potential to repair minor and critical bone defects in oral and maxillofacial surgery, respectively.

Autologous adipose tissue (AT) grafting is often compromised by insufficient early vascularization, leading to ischemia, fibrosis, and inconsistent long-term volume retention. Incorporating platelet-rich plasma (PRP) into AT bioinks offers a clinically accessible means to enhance vascular recruitment, but the in vivo impact of PRP dosage remains unclear. Here, we investigated how PRP concentration, uniformly integrated into a previously reported clinically relevant AT bioink, regulates vascular infiltration, tissue remodeling, and overall graft survival. High-dose PRP markedly improved graft performance, including an 8-fold increase in highly perfused regions, a 3.8-fold enhancement in adipocyte survival, a 1.67-fold reduction in fibrosis, and a 2.51-fold increase in collagen III deposition compared with PRP-free AT grafts. Histological analysis further demonstrated that PRP mitigates the adverse effects of poor perfusion, reducing regional disparities in survival and extracellular matrix (ECM) remodeling. High-dose PRP also maximized graft retention, preserving 103% of graft mass relative to 50.6% in native AT. Together, these results establish a clear in vivo dose–response relationship for PRP-enhanced AT grafts and highlight platelet concentration as a key design parameter for soft-tissue reconstruction. This work provides a translational framework for optimizing PRP-functionalized bioinks to improve clinical outcomes in reconstructive surgery.