With the rapid progression of additive manufacturing and the emergence of new 3D printing technologies, accuracy assessment is mostly being performed on isosymmetric-shaped test bodies. However, the accuracy of anatomic models can vary. The dimensional accuracy of root mean square values in terms of trueness and precision of 50 mandibular replicas, printed with five common printing technologies, were evaluated. The highest trueness was found for the selective laser sintering printer (0.11 ± 0.016 mm), followed by a binder jetting printer (0.14 ± 0.02 mm), and a fused filament fabrication printer (0.16 ± 0.009 mm). However, highest precision was identified for the fused filament fabrication printer (0.05 ± 0.005 mm) whereas other printers had marginally lower values. Despite the statistically significance (p < 0.001), these differences can be considered clinically insignificant. These findings demonstrate that all 3D printing technologies create models with satisfactory dimensional accuracy for surgical use. Since satisfactory results in terms of accuracy can be reached with most technologies, the choice should be more strongly based on the printing materials, the intended use, and the overall budget. The simplest printing technology (fused filament fabrication) always scored high and thus is a reliable choice for most purposes.

Computer-assisted surgery with three-dimensional (3D) printed surgical guides provides more accurate results than free-hand surgery. Steam sterilization could be one of the factors that affect the dimensions of surgical guide resin materials, leading to inaccuracies during surgeries. The purpose of this study was to evaluate the effects of steam sterilization on the dimensional accuracy of indication-specific hollow cube test bodies, manufactured in-house using Class IIa biocompatible resin materials (proprietary and third-party). To evaluate the pre- and post-sterilization dimensional accuracy, root mean square (RMS) values were calculated. The results indicate that, in all the groups, steam sterilization resulted in an overall linear expansion of the photopolymeric resin material, with an increase in outer dimensions and a decrease in inner dimensions. The effects on the dimensional accuracy of test bodies were not statistically significant in all the groups, except PolyJet Glossy (p > 0.05). The overall pre- and post-sterilization RMS values were below 100 and 200 µm, respectively. The highest accuracies were seen in proprietary resin materials, i.e., PolyJet Glossy and SLA-LT, in pre- and post-sterilization measurements, respectively. The dimensional accuracy of third-party resin materials, i.e., SLA-Luxa and SLA-NextDent, were within a comparable range as proprietary materials and can serve as an economical alternative.

The most common three-dimensional (3D) printing method is material extrusion, where a pre-made filament is deposited layer-by-layer. In recent years, low-cost polycaprolactone (PCL) material has increasingly been used in 3D printing, exhibiting a sufficiently high quality for consideration in cranio-maxillofacial reconstructions. To increase osteoconductivity, prefabricated filaments for bone repair based on PCL can be supplemented with hydroxyapatite (HA). However, few reports on PCL/HA composite filaments for material extrusion applications have been documented. In this study, solvent-free fabrication for PCL/HA composite filaments (HA 0%, 5%, 10%, 15%, 20%, and 25% weight/weight PCL) was addressed, and parameters for scaffold fabrication in a desktop 3D printer were confirmed. Filaments and scaffold fabrication temperatures rose with increased HA content. The pore size and porosity of the six groups’ scaffolds were similar to each other, and all had highly interconnected structures. Six groups’ scaffolds were evaluated by measuring the compressive strength, elastic modulus, water contact angle, and morphology. A higher amount of HA increased surface roughness and hydrophilicity compared to PCL scaffolds. The increase in HA content improved the compressive strength and elastic modulus. The obtained data provide the basis for the biological evaluation and future clinical applications of PCL/HA material.

Additive manufacturing (AM) of patient-specific implants (PSIs) is gradually moving towards in-house or point-of-care (POC) manufacturing. Polyetheretherketone (PEEK) has been used in cranioplasty cases as a reliable alternative to other alloplastic materials. As only a few fused filament fabrication (FFF) printers are suitable for in-house manufacturing, the quality characteristics of the implants fabricated by FFF technology are still under investigated. This paper aimed to investigate PEEK PSIs fabricated in-house for craniofacial reconstruction, discussing the key challenges during the FFF printing process. Two exemplary cases of class III (Group 1) and class IV (Group 2) craniofacial defects were selected for the fabrication of PEEK PSIs. Taguchi’s L9 orthogonal array was selected for the following nonthermal printing process parameters, i.e., layer thickness, infill rate, number of shells, and infill pattern, and an assessment of the dimensional accuracy of the fabricated implants was made. The root mean square (RMS) values revealed higher deviations in Group 1 PSIs (0.790 mm) compared to Group 2 PSIs (0.241 mm). Horizontal lines, or the characteristic FFF stair-stepping effect, were more perceptible across the surface of Group 1 PSIs. Although Group 2 PSIs revealed no discoloration, Group 1 PSIs displayed different zones of crystallinity. These results suggest that the dimensional accuracy of PSIs were within the clinically acceptable range; however, attention must be paid towards a requirement of optimum thermal management during the printing process to fabricate implants of uniform crystallinity.

3D printed biomaterials have been extensively investigated and developed in the field of bone regeneration related to clinical issues. However, specific applications of 3D printed biomaterials in different dental areas have seldom been reported. In this study, we aimed to and successfully fabricated 3D poly (lactic-co-glycolic acid)/β-tricalcium phosphate (3D-PLGA/TCP) and 3D β-tricalcium phosphate (3D-TCP) scaffolds using two relatively distinct 3D printing (3DP) technologies. Conjunctively, we compared and investigated mechanical and biological responses on human dental pulp stem cells (hDPSCs). Physicochemical properties of the scaffolds, including pore structure, chemical elements, and compression modulus, were characterized. hDPSCs were cultured on scaffolds for subsequent investigations of biocompatibility and osteoconductivity. Our findings indicate that 3D printed PLGA/TCP and β-tricalcium phosphate (β-TCP) scaffolds possessed a highly interconnected and porous structure. 3D-TCP scaffolds exhibited better compressive strength than 3D-PLGA/TCP scaffolds, while the 3D-PLGA/TCP scaffolds revealed a flexible mechanical performance. The introduction of 3D structure and β-TCP components increased the adhesion and proliferation of hDPSCs and promoted osteogenic differentiation. In conclusion, 3D-PLGA/TCP and 3D-TCP scaffolds, with the incorporation of hDPSCs as a personalized restoration approach, has a prospective potential to repair minor and critical bone defects in oral and maxillofacial surgery, respectively.

Cranioplasty with freehand-molded polymethylmethacrylate implants is based on decades of experience and is still frequently used in clinical practice. However, data confirming the fracture toughness and standard biomechanical tests are rare. This study aimed to determine the amount of force that could be applied to virtually planned, template-molded, patient-specific implants (n = 10) with an implant thickness of 3 mm, used in the treatment of a temporoparietal skull defect (91.87 cm²), until the implant cracks and finally breaks. Furthermore, the influence of the weight and porosity of the implant on its force resistance was investigated. The primary outcome showed that a high force was required to break the implant (mean and standard deviation 1484.6 ± 167.7 N), and this was very strongly correlated with implant weight (Pearson’s correlation coefficient 0.97; p < 0.001). Secondary outcomes were force application at the implant’s first, second, and third crack. Only a moderate correlation could be found between fracture force and the volume of porosities (Pearson’s correlation coefficient 0.59; p = 0.073). The present study demonstrates that an implant thickness of 3 mm for a temporoparietal skull defect can withstand sufficient force to protect the brain. Greater implant weight and, thus, higher material content increases thickness, resulting in more resistance. Porosities that occur during the described workflow do not seem to reduce resistance. Therefore, precise knowledge of the fracture force of polymethylmethacrylate cranial implants provides insight into brain injury prevention and serves as a reference for the virtual design process.