[Pt(1.5 nm)/Co(t_Co)/W(1.5 nm)]_N multilayers of different Co thicknesses (t_Co) and number of repeats (N) have been grown by sputtering on Si substrates, and their magnetic properties have been studied. The x-ray reflectivity has been used to measure thicknesses of each layer as well as their roughness. The dependence of the magnetic moment on t_Co and N (as determined by vibrating sample magnetometry) indicates the existence of a magnetic dead layer, which increases with N and reaches its maximum values for N ≥ 3. A similar N dependence of the magnetization at saturation is found. Ferromagnetic resonance and Brillouin light scattering have been used to investigate perpendicular magnetic anisotropy, damping, and interfacial Dzyaloshinskii-Moriya interaction (iDMI) vs Co thickness and the number of Pt/Co/W sequence repeats. We show that these parameters result from interface contributions that vary in a similar way with N, confirming that the first two Pt/Co/W trilayers are of lower quality. We thus conclude that for these systems, the increase of N improves the quality of interfaces and the volume of the stack, leading to the enhancement of the magnetic properties. Moreover, the measured weak iDMI constant, even for the higher N values, suggests that most probably, this iDMI results mainly from the Pt/Co interfaces.

The impact of in-plane and perpendicular magnetic fields on the spatial arrangement of superparamagnetic nanospheres is explored. We utilize nanosphere self-organization methods like Spin Coating and Drop-Casting in the presence of magnetic fields. In this way, the additional parameter of the long range magnetic dipolar interactions is introduced to the competing nanosphere–surface and nanosphere–nanosphere interactions, which control order and agglomeration. We present a comparative analysis of the self-assembly characteristics with respect to the different methods and the effect of the applied field in different directions. Under zero field perfect hexagonal arrays can be obtained by spin coating. Parallel applied fields tend to create directional patterns, while perpendicular favor 3D-accumulation.

The current investigation shows a possible new pathway for more efficient and cost-effective energy-harvesting photovoltaic devices. Our approach could permit all emerging technologies that are currently used for indoors and smart buildings to go a step forward and could be used for outdoor applications. The investigated architecture is a very promising geometry especially for Dye-Sensitized Solar Cells (DSSCs). It turns their main drawback, the lowering of their efficiency and lifetime when operating at high solar irradiation density, into an asset by increasing the total active area per horizontal unit area for light harvesting, while preserving the active elements from degradation and extending durable lifetime. The investigated architecture is based on a symmetric “U” type geometry, which is constructed by a highly reflective material on the inner surface. Solar irradiation is reflected internally at the bottom of the construction and splits towards two opposite sided solar cells; the two cells form a cavity where the solar light multiplies and is successively absorbed. Consequently, the vertically incoming irradiation is reduced when reaching the vertical internal sides on which the DSSCs are mounted. Thus, the solar cells operate at low light intensities, which provide significant lifetime extension and efficiency enhancement. Interestingly, the electrical energy per effective surface unit, which is produced by the two vertical DSSCs, is at least equal to that of a standalone, vertically irradiated cell. The advantage of the new architecture is that protects DSSCs from their degradation and deterioration, although the entire system operates under high illumination. This makes the cells more efficient outdoors, with a comparable performance to indoor conditions.