Environmentally friendly packaging is becoming more popular as the number of companies implementing more sustainable solutions continues to increase, and consumers become more aware and choose more environmentally friendly options. However, not all environmentally friendly packaging meets all desirable properties, as some are only partially made of renewable raw materials or degrade over a long period of time. Bioplastics constructed from blends of gelatine and starch are solely made from renewable raw materials. Combined with relatively short degradation times, these materials have the potential to replace currently used, non-biodegradable film and single-use plastics. However, despite these advantages, further research is required to identify the best combination of raw materials, selectively and collectively, and to then optimise the appropriate physicochemical properties of the resultant bioplastics. In this study, gelatine from different sources (piscine, porcine, bovine) combined with potato starch was used to generate home-compostable bioplastics. These bioplastics were assessed in terms of water solubility, water content, opacity, surface roughness, and key mechanical properties such as tensile strength. Significant differences were found, particularly for piscine gelatine blends. It was concluded that piscine gelatine is a promising protein with highly relevant properties for the bioplastics industry.

To combat the release of petroleum-derived plastics into the environment the European Commission has adopted the EU plastics strategy, which aims for a complete ban on single-use plastics by 2030. Environmentally friendly and sustainable packaging like bioplastic is being up taken at significant levels by companies and consumers. In this study, the environmental impact of novel gelatine–starch blend bioplastics is investigated. The assessments included ecotoxicology with different species that can be found in marine and soil environments to simulate natural conditions. Microalgae, plant, and nematode species were chosen as these are representative of their habitats and are known for their sensitivity to pollutants. Degradation rates of these novel bioplastics were assessed as well as microbiome analysis of the soil before and after bioplastic degradation. The main findings of this study are that (i) the bioplastic generated can be fully biodegraded in soil environments at moderate conditions (20 °C) leaving no physical traces; (ii) bioplastic did not exhibit significantly adverse effects on any organisms assessed in this study; (iii) microbiome analysis of the soil after biodegradation showed a decrease in alpha diversity and a significant increase of Actinobacteria and Firmicutes phyla, which were dominative in the soil.

Sol–gel coatings can provide anti-fouling and erosion resistance while being safe to use in the marine environment. MAPTMS/ZPO multilayer coatings deposited on the AA2024-T3 aluminium surface using the dip-coating method at three different thicknesses (2, 4, and 6 µm) are investigated in this work. The coatings are characterised in terms of physical and mechanical properties, and these properties are investigated in comparison to previously obtained cavitation erosion resistance levels of the coatings. Additionally, the efficiency of the coatings against biofouling was assessed using Phaeodactylum tricornutum, a marine diatom. The influence of the formation of organic–inorganic hybrid materials (OIHMs) from the prepared sols on the physical and mechanical properties of the coatings were analysed. A variety of techniques, including attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR), water contact angle (WCA) measurements, pencil hardness testing, cross-cut adhesion testing, a roughness profilometer, and nano-indentation, were performed on the bare and coated substrates. The results indicated that the thickness, hydrophobicity, and adherence of the coatings are strongly affected by the roughness. The elastic strain failure (H/E) and resistance to plastic deformation (H³/E²) coefficients were higher than those of the bare substrate before and after the cavitation erosion test, indicating that the coating had a higher ability to withstand deformation in comparison to the substrate alone. Furthermore, the microscopic analysis of a marine diatom, Phaeodactylum tricornutum, revealed that coated surfaces exhibited a decreased rate of bacterial adhesion and biofilm formation. The data show that sol–gel formed coatings outperform uncoated AA2024-T3 in terms of hardness, elastic strain, plastic deformation, and biofouling resistance. These characteristics are attributed to the coatings’ mechanical and adhesive capabilities, as well as their tribological behaviour.