In this study, we report the self-healing ability of polyurethane (PU) nanocomposites based on the photothermal effect of polydopamine-coated graphene oxide (PDA–rGO). Polydopamine (PDA) was coated on the graphene oxide (GO) surface, while simultaneously reducing GO by the oxidation of dopamine hydrochloride in an alkaline aqueous solution. The PDA–rGO was characterized by Fourier-transform infrared spectroscopy, X-ray diffraction, Raman spectroscopy, thermogravimetric analysis, and scanning electron microscopy–energy-dispersive X-ray analysis. PDA–rGO/PU nanocomposites with nanofiller contents of 0.1, 0.5 and 1 wt% were prepared by ex situ mixing method. The photothermal effect of the PDA–rGO in the PU matrix was investigated at 0.1 W/cm² using an 808 nm near-infrared (NIR) laser. The photothermal properties of the PDA–rGO/PU nanocomposites were superior to those of the GO/PU nanocomposites, owing to an increase in the local surface plasmon resonance effect by coating with PDA. Subsequently, the self-healing efficiency was confirmed by recovering the tensile stress of the damaged nanocomposites using the thermal energy generated by the NIR laser.

In this study, high-crystallinity single walled carbon nanotubes (H-SWNTs) were prepared by high-temperature thermal annealing at 1800 °C and a self-heating shape memory polyurethane nanocomposite with excellent self-heating characteristics was developed within a few seconds by irradiation with near-infrared rays. With a simple method (heat treatment), impurities at the surface of H-SWNTs were removed and at the same time the amorphous structure converted into a crystalline structure, improving crystallinity. Therefore, high conductivity (electric, thermal) and interfacial affinity with PU were increased, resulting in improved mechanical, thermal and electric properties. The electrical conductivity of neat polyurethane was enhanced from ~10^–11 S/cm to 4.72 × 10⁻⁸ S/cm, 1.07 × 10⁻⁶ and 4.66 × 10⁻⁶ S/cm, while the thermal conductivity was enhanced up to 60% from 0.21 W/mK, 0.265 W/mK and 0.338 W/mK for the composites of 1, 3 and 5 wt%, respectively. Further, to achieve an effective photothermal effect, H-SWNTs were selected as nanofillers to reduce energy loss while increasing light-absorption efficiency. Thereafter, near-infrared rays of 818 nm were directly irradiated onto the nanocomposite film to induce photothermal properties arising from the local surface plasmon resonance effect on the CNT surface. A self-heating shape memory composite material that rapidly heated to 270 °C within 1 min was developed, even when only 3 wt.% of H-SWNTs were added. The results of this study can be used to guide the development of heat-generating coating materials and de-icing materials for the wing and body structures of automobiles or airplanes, depending on the molding method.