ZnO and Aluminum doped ZnO nanoparticles (Al/ZnO NPs) were successfully synthesized by the sol-gel method. Together with the effect of calcination temperatures (200, 300 and 400 °C) and Al dosage (1%, 3%, 5% and 10%) on structural, morphological and optical properties of Al/ZnO NPs, their photocatalytic degradation of methyl orange (MO) dye was investigated. The calcination temperatures at 200, 300 and 400 °C in forming structure of ZnO NPs led to spherical nanoparticle, nanorod and nanoflake structures with a well-crystalline hexagonal wurtzite, respectively. The ZnO NPs calcined at 200 °C exhibited the highest specific surface area and light absorption property, leading to the MO removal efficiency of 80% after 4 h under the Ultraviolet (UV) light irradiation. The MO removal efficiency was approximately two times higher than the nanoparticles calcined at 400 °C. Furthermore, the 5% Al/ZnO NPs exhibited superior MO removal efficiency of 99% in only 40 min which was approximately 20 times enhancement in photocatalytic activity compared to pristine ZnO under the visible light irradiation. This high degradation performance was attributed to the extended light absorption, narrowed band gap and effective suppression of electron–hole recombination through an addition of Al metal.

A hybrid nanostructure Ag/TiO₂ photoelectrode for PEC water splitting with a remarkable high photocurrent density, 0.35 mA cm⁻² (5 fold higher than that of the pristine TiO₂ photoeletrode) was fabricated by a facile one-pot hydrothermal and electrodeposition method.

A dual-functional WO₃/BiVO₄ photoanode achieved remarkable photocurrent density, 6.85 mA cm⁻² at 1.23 V vs. RHE and high efficiency for glycerol degradation.

Palm oil mill effluent (POME) is a complex industrial wastewater containing high organic loads and persistent colored constituents that are not completely removed by conventional biological treatment processes.