This research aimed to scale up the production of starch-based super water absorbent (SWA) and to validate the practical benefits of SWA for agricultural applications. SWA was successfully prepared in an up-scaling production by radiation-induced graft polymerization of acrylic acid onto cassava starch. Chemical characterization by FTIR and thermal characterization by TGA showed results that differentiated starting materials from the prepared SWA, thus confirming effective preparation of starch-based SWA via radiation-induced graft polymerization. SEM results visibly revealed a highly porous morphology of the synthesized SWA, substantiating its high swelling ability. Results from the field tests, performed for two seasons, revealed that the prepared SWA was able to increase the survival rate of young rubber trees planted in arid area by up to 40%, while simultaneously enhancing the growth characteristics of the young rubber trees.

Due to the increasing demands for improved radiation safety and the growing concerns regarding the excessive use of plastics, this work aimed to develop effective and eco-friendly thermal-neutron-shielding materials based on recycled high-density polyethylene (r-HDPE) composites containing varying surface-treated gadolinium oxide (Gd₂O₃) contents (0, 5, 10, 15, and 20 wt%). The results indicate that the overall thermal-neutron-shielding properties of the r-HDPE composites were enhanced with the addition of Gd₂O₃, as evidenced by large reductions in I/I₀, HVL, and TVL, as well as the substantial increases in ∑_t and ∑_t/ρ of the composites. Furthermore, the results reveal that the values for tensile properties initially increased up to 5–15 wt% of Gd₂O₃ and then gradually decreased at higher contents. In addition, the results show that the addition of Gd₂O₃ particles generally increased the density (ρ), the remaining ash at 600 °C, and the degree of crystallinity (%XC) of the composites. This work also determined the effects of gamma irradiation on relevant properties of the composites. The findings indicate that following gamma aging, the tensile modulus slightly increased, while the tensile strength, elongation at break, and hardness (Shore D) showed no significant (p < 0.05) differences, except for the sample containing 5 wt% of Gd₂O₃, which exhibited a noticeable reduction in elongation at break. Furthermore, by comparing the neutron-shielding and mechanical properties of the developed r-HDPE composites with common borated polyethylene (PE) containing 5 wt% and 15 wt% of boron, the results clearly indicate the superior shielding and tensile properties in the r-HDPE composites, implying the great potential of r-HDPE composites to replace virgin plastics as effective and more eco-friendly shielding materials.

This study presented a green, facile and efficient approach for a new combination of targeted gold nanohybrids functionalized with folate-hydrophobic-quaternized pullulan delivering hydrophobic camptothecin (CPT-GNHs@FHQ-PUL) to enhance the efficacy, selectivity, and safety of these systems. New formulations of spherical CPT-GNHs@FHQ-PUL obtained by bio-inspired strategy were fully characterized by TEM, EDS, DLS, zeta-potential, UV-vis, XRD, and ATR-FTIR analyses, showing a homogeneous particles size with an average size of approximately 10.97 ± 2.29 nm. CPT was successfully loaded on multifunctional GNHs@FHQ-PUL via intermolecular interactions. Moreover, pH-responsive CPT release from newly formulated-CPT-GNHs@FHQ-PUL exhibited a faster release rate under acidic conditions. The intelligent CPT-GNHs@FHQ-PUL (IC₅₀ = 6.2 μM) displayed a 2.82-time higher cytotoxicity against human lung cancer cells (Chago-k1) than CPT alone (IC₅₀ = 2.2 μM), while simultaneously exhibiting less toxicity toward normal human lung cells (Wi-38). These systems also showed specific uptake by folate receptor-mediated endocytosis, exhibited excellent anticancer activity, induced the death of cells by increasing apoptosis pathway (13.97%), and arrested the cell cycle at the G0-G1 phase. The results of this study showed that the delivery of CPT by smart GNHs@FHQ-PUL systems proved to be a promising strategy for increasing its chemotherapeutic effects.

In this research, benzoxazine (BA-a) and diamino polysiloxane (PSX750) blends were prepared at 0–50 wt% of BA-a. The interactions between two polymeric components were investigated via a Fourier Transform Infrared Spectrometer (FT-IR). The thermal properties of the blends were also determined with Dynamic Mechanical Analyzer (DMA) and Thermogravimetric Analyzer (TGA). The mechanical properties and shape memory behaviors of the blends were also investigated. The FTIR spectra exhibited the shift of the peak from 1672 to the range of 1634–1637 cm⁻¹, which could be identified as hydrogen bonds between two polymeric domains at the contents from 30 to 50 wt%. The DMA thermograms revealed two glass transition temperatures, which could indicate a partially miscible system. The char yield values were increased, while the decomposition temperatures were decreased with an increasing benzoxazine content. Interestingly, the blends at the contents of 10 and 20 wt% presented dual-shape memory behaviors, whereas triple- or multiple-shape memory behaviors were observed with benzoxazine contents of 30 to 50 wt%. For the high-temperature recovery state, a shape memory ratio of 97.5% with a recovery time of 65 s and a shape fixity ratio of 66.7% was recorded at the content of 50 wt%. For the low-temperature recovery state, a shape recovery ratio of 98.9% was observed at the same content. Moreover, the values of the recovery ratio for four shape-recovery cycles revealed multiple shape memory behaviors with high recovery ratios in the range of 95–98%.

In this research, blends of bio-based polybenzoxazine (V-fa) and polycaprolactone (PCL) with different molecular weights (M_n) (14,000, 45,000, and 80,000 Da) were prepared with varying PCL content from 10 to 95 wt%. The spectra measured using Fourier Transform Infrared Spectroscopy (FTIR) may indicate the presence of hydrogen bonding between two polymeric components. The thermograms obtained using a Differential Scanning Calorimeter (DSC) and dynamic mechanical analyzer (DMA) exhibited a shift in glass transition temperature (T_g), which indicated partial miscibility between V-fa and PCL. The thermograms obtained using a thermogravimetric analyzer (TGA) revealed that the addition of PCL led to an increase in the maximum decomposition temperature (T_dmax). The tensile strength and modulus decreased with an increase in PCL, thus indicating a decrease in brittleness. Interestingly, only the samples with an M_n of 80,000 Da were bendable. The blends with 80 wt% PCL were revealed to have shape memory behaviors with a shape fixity of approximately 81%. The shape recovery ratio of the blends with 95 wt% PCL was approximately 78%.