This work aimed to theoretically determine the high-energy-photon-shielding properties of flexible wood/natural rubber (NR) and NR composites containing photon protective fillers, namely Pb, Bi₂O₃, or Bi₂S₃, using XCOM. The properties investigated were the mass attenuation coefficient (µ_m), linear attenuation coefficient (µ), and half value layer (HVL) of the composites, determined at varying photon energies of 0.001–5 MeV and varying filler contents of 0–1000 parts per hundred parts of rubber by weight (phr). The simulated results, which were in good agreement with previously reported experimental values (average difference was 5.3%), indicated that overall shielding properties increased with increasing filler contents but decreased with increasing incident photon energies. The results implied the potential of bismuth compounds, especially Bi₂O₃, to replace effective but highly toxic Pb as a safer high-energy-photon protective filler, evidenced by just a slight reduction in µ_m values compared with Pb fillers at the same filler content and photon energy. Furthermore, the results suggested that the addition of 20 phr wood particles, primarily aimed to enhance the rigidity and dimensional stability of Pb/NR, Bi₂O₃/NR, and Bi₂S₃/NR composites, did not greatly reduce shielding abilities; hence, they could be used as dimensional reinforcers for NR composites. Lastly, this work also reported the optimum Pb, Bi₂O₃, or Bi₂S₃ contents in NR and wood/NR composites at photon energies of 0.1, 0.5, 1, and 5 MeV, with 316–624 phr of filler being the recommended contents, of which the values depended on filler type and photon energy of interest.

Due to rapid increases in the utilization of radiation and nuclear technologies, effective and suitable radiation-shielding materials have become one of the most sought-after options to protect users and the public from excessive exposure to the radiation. However, most radiation-shielding materials have greatly reduced mechanical properties after the addition of fillers, resulting in their limited useability and shortened lifetime. Therefore, this work aimed to alleviate such drawbacks/limitations by exploring a possible method to simultaneously enhance both the X-ray shielding and mechanical properties of bismuth oxide (Bi₂O₃)/natural rubber (NR) composites through multi-layered structures, with varying (1–5) layers and a total combined thickness of 10 mm. To correctly determine the effects of the multi-layered structures on the properties of NR composites, the formulation and layer configuration for all multi-layered samples were tailored such that their theoretical X-ray shielding properties were equal to those of a single-layered sample that contained 200 phr Bi₂O₃. The results indicated that the multi-layered Bi₂O₃/NR composites with neat NR sheets on both outer layers (sample-D, sample-F, sample-H, and sample-I) had noticeably higher tensile strength and elongation at break than those of the other designs. Furthermore, all multi-layered samples (sample-B to sample-I), regardless of the layer structure, had enhanced X-ray shielding properties compared to those with a single layer (sample-A), as shown by their higher values of the linear attenuation coefficient (µ) and lead equivalence (Pb_eq) and the lower value of the half-value layer (HVL) in the former. This work also determined the effects of thermal aging on relevant properties for all samples, with the results revealing that all the thermal-aged composites had higher values for the tensile modulus but lower values for the swelling percentage, tensile strength, and elongation at break, compared with the non-aged composites. Hence, based on the overall outcomes from this work, it could be concluded that the worrisome decreases in mechanical properties of the common single-layered NR composites after the addition of Bi₂O₃ could be prevented/reduced by introducing appropriate multi-layered structures, which would not only widen potential applications but also prolong the lifetime of the composites.

Due to the increasing demands for improved radiation safety and the growing concerns regarding the excessive use of plastics, this work aimed to develop effective and eco-friendly thermal-neutron-shielding materials based on recycled high-density polyethylene (r-HDPE) composites containing varying surface-treated gadolinium oxide (Gd₂O₃) contents (0, 5, 10, 15, and 20 wt%). The results indicate that the overall thermal-neutron-shielding properties of the r-HDPE composites were enhanced with the addition of Gd₂O₃, as evidenced by large reductions in I/I₀, HVL, and TVL, as well as the substantial increases in ∑_t and ∑_t/ρ of the composites. Furthermore, the results reveal that the values for tensile properties initially increased up to 5–15 wt% of Gd₂O₃ and then gradually decreased at higher contents. In addition, the results show that the addition of Gd₂O₃ particles generally increased the density (ρ), the remaining ash at 600 °C, and the degree of crystallinity (%XC) of the composites. This work also determined the effects of gamma irradiation on relevant properties of the composites. The findings indicate that following gamma aging, the tensile modulus slightly increased, while the tensile strength, elongation at break, and hardness (Shore D) showed no significant (p < 0.05) differences, except for the sample containing 5 wt% of Gd₂O₃, which exhibited a noticeable reduction in elongation at break. Furthermore, by comparing the neutron-shielding and mechanical properties of the developed r-HDPE composites with common borated polyethylene (PE) containing 5 wt% and 15 wt% of boron, the results clearly indicate the superior shielding and tensile properties in the r-HDPE composites, implying the great potential of r-HDPE composites to replace virgin plastics as effective and more eco-friendly shielding materials.

In this work, paraffin and paraffin/bitumen composites with additions of boron oxide (B₂O₃) were prepared to evaluate the viscosity, flexural, and thermal neutron shielding properties for uses as thermal neutron shielding materials. The results showed that the addition of 3 wt% or 9 wt% bitumen to paraffin increased the overall flexural properties with the content of 9 wt% bitumen having the highest values. The improvement in flexural properties made the composites less brittle, stiffer, and longer-lasting. Furthermore, different contents of B₂O₃ (0, 7, 14, 21, 28, and 35 wt%) were added to paraffin and paraffin/bitumen composites to investigate the effects of the B₂O₃ contents. The results indicated that an increase in B₂O₃ contents improved the shielding properties but slightly reduced the flexural properties. Specifically for 5-mm paraffin and 5-mm paraffin/bitumen samples with 35 wt% of B₂O₃, both samples could reduce neutron flux by more than 70%. The overall results suggested that the paraffin and paraffin/bitumen composites with additions of B₂O₃ showed improved properties for utilization as effective thermal neutron shielding materials.