Nanostructured mesoporous titanium dioxide (TiO2) particles with high specific surface area and average crystallite domain sizes within 2 nm and 30 nm have been prepared via the sol-gel and hydrothermal procedures. The characteristics of produced nanoparticles have been tested using X-Ray Diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area analysis, Scanning Electron Microscopy (SEM), Fourier Transform Infra-Red (FTIR), and Raman Spectroscopy as a function of temperature for their microstructural, porosity, morphological, structural and absorption properties. The as-synthesized TiO2 nanostructures were attempted as catalysts in Rhodamine B and Sudan III dyes' photocatalytic decomposition in a batch reactor with the assistance of Ultra Violet (UV) light. The results show that for catalysts calcined at 300 °C, ∼100 % decomposition of Sudan III dye was observed when Hydrothermal based catalyst was used whiles ∼94 % decomposition of Rhodamine B dye was observed using the sol-gel based catalysts. These synthesized TiO2 nanoparticles have promising potential applications in the light aided decomposition of a wide range of dye pollutants.

Oil is a major source of energy in the industrial world. Exploitation of oil and rigging activities, transportation via sea, and many other mechanical failures lead to oil spills into the marine environment. In view of these, the suitability and effectiveness of oil spill response methods have always been a topical discussion worldwide. It has become necessary, now than ever, for existing spill response methods used to remove oil from the environment to be improved upon and more importantly, develop new response materials that are sustainable and environmentally friendly. There exist surfactants in nature that are non-toxic and biodegradable, which can be explored to produce potential dispersants to help remove oil safely from the surface of marine water. This review comprises of the works and resourceful materials produced by various researchers and agencies in the field of oil spill response, placing emphasis on the use of dispersants in the marine environment.

This paper presents the effect of modified halloysite nanotubes on the sustained drug release mechanisms of sodium salicylate. Acid treatment and composite polymer-halloysite modification techniques were adopted in this study. After each modification, sodium salicylate drug was loaded, and in vitro release properties were evaluated and compared with the raw unmodified halloysite nanotubes. The results obtained from SEM, TEM and FTIR analyses indicate that both acid treatment and composite formation have no effect on the tubular structure and morphology of halloysite. However, modification of the halloysite nanotubes did influence the drug release rate. In the acid treatment modification, there was an improved loading of sodium salicylate drug which resulted in the sustain release of large amount of the sodium salicylate. In the polymer/halloysite composite formation, a consistent layer of polymer was formed around the halloysite during the composite formation and thus delayed release providing sustained release of sodium salicylate drug over a longer period of time as compared to the acid treated and unmodified halloysite. The results from the invitro release were best fitted with the Higuchi and the Koresymer-Peppas models.

Synthesis scheme of the Ag ₃ PO ₄ –TiO ₂ nanocomposite.