In this paper, we examined the dielectric properties of CaCu₃Ti₄O₁₂ (CCTO) ceramics fabricated by various routes and discussed the most important conditions affecting their dielectric behavior. We prepared feedstock powder using a molten salt route and compared it with a commercial powder. Both powders were sintered using SPS. For some samples, annealing was applied after sintering. Other samples were obtained by high-pressure forming and conventional sintering, using both powders. Phase composition, porosity and microhardness were evaluated in comparison with the literature. The results showed that a sintering temperature just below or equal to 1000 °C should be set for the SPS process. However, the best dielectric characteristics were obtained in samples prepared by high-pressure forming and conventional sintering, which showed a relative permittivity of 22,000 and a loss tangent of 0.13 at 1 MHz.