This study investigates the retention load (RL) between ZrO₂ primary crowns and secondary polyetheretherketone (PEEK) crowns made by different fabrication methods with three different tapers. Standardized primary ZrO₂ crowns were fabricated with three different tapers: 0°, 1°, and 2° (n = 10/group). Ten secondary crowns were fabricated (i) milled from breCam BioHPP blanks (PM); (ii) pressed from industrially fabricated PEEK pellets (PP) (BioHPP Pellet); or (iii) pressed from granular PEEK (PG) (BioHPP Granulat). One calibrated operator adjusted all crowns. In total, the RL of 90 secondary crowns were measured in pull-off tests at 50 mm/min, and each specimen was tested 20 times. Two- and one-way ANOVAs followed by a Scheffé’s post-hoc test were used for data analysis (p < 0.05). Within crowns with a 0° taper, the PP group showed significantly higher retention load values compared with the other groups. Among the 1° taper, the PM group presented significantly lower retention loads than the PP group. However, the pressing type had no impact on the results. Within the 2° taper, the fabrication method had no influence on the RL. Within the PM group, the 2° taper showed significantly higher retention load compared with the 1° taper. The taper with 0° was in the same range value as the 1° and 2° tapers. No impact of the taper on the retention value was observed between the PP groups. Within the PG groups, the 0° taper presented significantly lower RL than the 1° taper, whereas the 2° taper showed no differences. The fabrication method of the secondary PEEK crowns and taper angles showed no consistent effect within all tested groups.

The aim of this work was to evaluate the influence of specimen preparation and test method on the flexural strength results of monolithic zirconia. Different monolithic zirconia materials (Ceramill Zolid (Amann Girrbach, Koblach, Austria), Zenostar ZrTranslucent (Wieland Dental, Pforzheim, Germany), and DD Bio zx² (Dental Direkt, Spenge, Germany)) were tested with three different methods: 3-point, 4-point, and biaxial flexural strength. Additionally, different specimen preparation methods were applied: either dry polishing before sintering or wet polishing after sintering. Each subgroup included 40 specimens. The surface roughness was assessed using scanning electron microscopy (SEM) and a profilometer whereas monoclinic phase transformation was investigated with X-ray diffraction. The data were analyzed using a three-way Analysis of Variance (ANOVA) with respect to the three factors: zirconia, specimen preparation, and test method. One-way ANOVA was conducted for the test method and zirconia factors within the combination of two other factors. A 2-parameter Weibull distribution assumption was applied to analyze the reliability under different testing conditions. In general, values measured using the 4-point test method presented the lowest flexural strength values. The flexural strength findings can be grouped in the following order: 4-point < 3-point < biaxial. Specimens prepared after sintering showed significantly higher flexural strength values than prepared before sintering. The Weibull moduli ranged from 5.1 to 16.5. Specimens polished before sintering showed higher surface roughness values than specimens polished after sintering. In contrast, no strong impact of the polishing procedures on the monoclinic surface layer was observed. No impact of zirconia material on flexural strength was found. The test method and the preparation method significantly influenced the flexural strength values.

In prosthetic dentistry, double crown systems have proved their suitability as retainers for removable partial dentures. However, investigations in this context, regarding polyetheretherketone, are scarce. Therefore, the aim of this study was to test the retention force (RF) between polyetheretherketone (PEEK) primary and cobalt-chromium (CoCr), zirconia (ZrO₂) and galvanic (GAL) secondary crowns with three different tapers. Primary PEEK-crowns were milled with the tapers 0°, 1°, and 2° (n = 10/taper, respectively). Afterwards, 90 secondary crowns were fabricated: (i) 30 CoCr-crowns milled from Ceramill Sintron (AmannGirrbach, Koblach, Austria) (n = 10/taper), (ii) 30 ZrO₂-crowns milled from Ceramill ZI (AmannGirrbach, Koblach, Austria) (n = 10/taper), and (iii) 30 GAL-crowns made using electroforming (n = 10/taper). RF was measured in a pull-off test (20 pull-offs/specimen) and data were analyzed using 2-/1-way Analysis of Variance (ANOVA) followed by the Tukey-Honestly Significant Difference (HSD) post hoc test and linear regression analyses (p < 0.05). The measured mean RF values ranged between 9.6 and 38.2 N. With regard to the 0°, 1°, and 2° tapered crowns, no statistically significant differences between CoCr and ZrO₂ were observed (p > 0.141). At 0° taper, no differences in retention forces between GAL, CrCr, and ZrO₂ crowns were found (p = 0.075). However, at 1° and 2° taper, lower RF for GAL-crowns were observed (p < 0.009, p < 0.001, respectively). According to this laboratory study, PEEK might be a suitable material for primary crowns, regardless of the taper and the material of secondary crown. Long-term results, however, are still necessary.

Introduction: Continuous positive airway pressure (CPAP) is currently the treatment of choice for sleepiness in patients with obstructive sleep apnoea (OSA); however, adherence is often thought to be suboptimal. We investigated the effects of suboptimal CPAP usage on objective and subjective sleepiness parameters in patients with OSA.Material and methods: In this 2-week, parallel, double-blind, randomised controlled trial we enrolled moderate-to-severe OSA patients with excessive pre-treatment daytime sleepiness (Epworth sleepiness scale (ESS) score >10 points) who had suboptimal CPAP adherence over ≥12 months (mean nightly usage time 3–4 h). Patients were allocated through minimisation to either subtherapeutic CPAP (“sham CPAP”) or continuation of CPAP (“therapeutic CPAP”). A Bayesian analysis with historical priors calculated the posterior probability of superiority.Results: Between May, 2016 and November, 2018, 57 patients (aged 60±8 years, 79% male, 93% Caucasian) were allocated in total, and 52 who completed the study (50% in each arm) were included in the final analysis. The unadjusted ESS score increase was 2.4 points (95% CI 0.6–4.2, p=0.01) in the sham-CPAP group when compared to continuing therapeutic CPAP. The probability of superiority of therapeutic CPAP over sham CPAP was 90.4% for ESS, 90.1% for systolic blood pressure and 80.3% for diastolic blood pressure.Conclusions: Patients with moderate-to-severe OSA and daytime sleepiness are still getting a substantial benefit from suboptimal CPAP adherence, albeit not as much as they might get if they adhered more. Whether a similar statement can be made for even lower adherence levels remains to be established in future trials.