Background: Poly lactic-co-glycolic acid (PLGA) has been widely investigated for various biomedical applications, such as craniofacial bone regeneration, wound dressing and tissue engineering. Electrospinning is a versatile technology used to produce micro/nanoscale fibers with large specific surface area and high porosity. Purpose: The aim of the current study is to prepare PLGA nanofibers using electrospinning for guided tissue regeneration/guided bone regeneration applications. The objective of this study is to determine the appropriate electrospinning parameters such as applied voltage, flow rate, spinneret-collector distance and polymer solution concentration for preparation of PLGA fibrous membrane and their effect on the mean fiber diameter of the electrospun fibers. Method: PLGA pellets were dissolved in Hexafluoroisopropanol (HFIP) in various concentrations overnight using a bench rocker. The resulting PLGA solution was then loaded into a syringe and electrospinning was done by maintaining the other parameters constant. Similarly, various fibrous mats were collected by altering the specific electrospinning parameter inputs such as applied voltage, flow rate and spinneret-collector distance. The morphology of the fibrous mats was characterized using Scanning Electron Microscope. The mean fiber diameter was assessed using ImageJ software and the results were compared using one-way ANOVA. Results: We obtained bead-free uniform fibers with various tested solution concentrations. One-way ANOVA analysis demonstrated significant variation in mean fiber diameter of the electrospun fibers with altering applied voltage, solution concentration, flow rate and spinneret-collector distance. Conclusion: The above-mentioned electrospinning parameters and solution concentration influence the mean fiber diameter of electrospun PLGA nanofibers.

All-ceramic fixed dental prostheses (FDPs) tend to fracture at the connector regions due to high stress concentration at these areas influenced by their design. This study was performed as an adjunct to an existing clinical study to evaluate the influence of the different radii of curvature of gingival embrasure on the stress distribution of a three-unit all-ceramic implanted supported FDP. Three three-dimensional (3D) models were created by scanning two titanium dental implants, their suitable zirconia abutments, and a patient-retrieved dental prosthesis using a micro-CT scanner. The radius of curvature of the gingival embrasure for the distal connector of the FDP was altered to measure 0.25 mm, 0.50 mm, and 0.75 mm. A finite element analysis (FEA) software (ABAQUS) was used to evaluate the impact of different connector designs on the distribution of stresses. Maximum Principal Stress data was collected from the individual components (veneer, framework, and abutments). The radius of curvature of gingival embrasure had a significant influence on the stress distribution at the assessed components. The tensile peak stresses at all structures were highest in the 0.25 mm model, while the 0.50 mm and 0.75 mm models presented similar values and more uniform stress distribution.

Polycaprolactone (PCL) micro- and nanoparticles produced using the electrospraying technique present high drug encapsulation capacity, a controllable surface area, and a good cost–benefit ratio. PCL is also considered a non-toxic polymeric material with excellent biocompatibility and biodegradability. All these characteristics make PCL micro- and nanoparticles a promising material for tissue engineering regeneration, drug delivery, and surface modification in dentistry. In this study, PCL electrosprayed specimens were produced and analyzed to determine their morphology and size. Three PCL concentrations (2, 4, and 6 wt%) and three solvent types (chloroform (CF), dimethylformamide (DMF), and acetic acid (AA)) with various solvent mixtures ratios (1:1 CF/DMF, 3:1 CF/DMF, 100% CF, 1:1 AA/CF, 3:1 AA/CF, and 100% AA) were used while keeping the remaining electrospray parameters constant. SEM images followed by ImageJ analysis showed a change in the morphology and size of the particles among various tested groups. A two-way ANOVA demonstrated a statistically significant interaction (p < 0.001) between PCL concentration and solvents on the size of the particles. With the increase in the PCL concentration, an increase in the number of fibers was observed among all the groups. The morphology and dimensions of the electrosprayed particles, as well as the presence of fibers, were significantly dependent on the PCL concentration, choice of solvent, and solvent ratio.

Our objective was to determine and optimize the significant parameters affecting mechanical properties and mean fiber diameter (MFD) of a novel GTR/GBR membrane composed of polycaprolactone (PCL) and chicken eggshell membrane (ESM). For this, we prepared electrospun membrane specimens (n = 16) with varying concentrations of PCL, ESM, nano-hydroxyapatite (HAp), and altered electrospinning parameters as generated by DOE++ software. After the determination of MFD and mechanical properties for all specimens, Taguchi orthogonal array L8 design was used to screen significant factors affecting the MFD and mechanical properties. PCL wt%, ESM wt%, HAp wt%, applied voltage (AV), flow rate (FR), and spinneret-collector distance (SCD) were the independent variables investigated. The response variables analyzed were MFD, tensile strength (TS), and elastic modulus. ANOVA outlined ESM wt%, HAp wt%, AV, FR, SCD, and an interactive effect between PCL wt% and AV to be the significant factors affecting modulus values of an electrospun PCL/ESM membrane (p < 0.05). Furthermore, concentrations of PCL and ESM were the significant factors affecting MFD (p < 0.05) and there were no significant factors affecting the TS values. Optimization using DOE++ software predicted that the maximal TS of 3.125 MPa, modulus of 278.168 MPa, and MFD of 882.75 nm could be achieved.