Lithium-ion capacitors (LICs) are considered to be one of the most promising energy storage devices which have the potential of integrating high energy of lithium-ion batteries and high power and long cycling life of supercapacitors into one system. However, the current LICs could only provide high power density at the cost of low energy density due to the sluggish Li⁺ diffusion and/or low electrical conductivity of the anode materials. Moreover, the serious capacity and kinetics imbalances between anode and cathode result in not only inferior rate performance but also unsatisfactory cycling stability. Therefore, designing high-power and structure stable anode materials is of great significance for practical LICs. Under this circumstance, graphene-based materials have been intensively explored as anodes in LICs due to their unique structure and outstanding electrochemical properties and attractive achievements have been made. In this review, the recent progresses of graphene-based anode materials for LICs are systematically summarized. Their synthesis procedure, structure and electrochemical performance are discussed with a special focus on the role of graphene. Finally, the outlook and remaining challenges are presented with some constructive guidelines for future research.

As an emerging energy storage technology, Na-CO₂ batteries with high energy density are drawing tremendous attention because of their advantages of combining cost-effective energy conversion and storage with CO₂ clean recycle and utilization. Nevertheless, their commercial applications are impeded by unsatisfactory electrochemical performance including large overpotentials, poor rate capability, fast capacity deterioration, and inferior durability, which mainly results from the inefficient electrocatalysts of cathode materials. Therefore, novel structured cathode materials with efficient catalytic activity are highly desired. In this review, the latest advances of catalytic cathode materials for Na-CO₂ batteries are summarized, with a special emphasis on the electrocatalysts for CO₂ reduction and evolution, the formation and decomposition of discharge product, as well as their catalytic mechanism. Finally, an outlook is also proposed for the future development of Na-CO₂ batteries.

Lithium-ion capacitors (LICs) are attracting increasing attention because of their potential to bridge the electrochemical performance gap between batteries and supercapacitors. However, the commercial application of current LICs is still impeded by their inferior energy density, which is mainly due to the low capacity of the cathode. Therefore, tremendous efforts have been made in developing novel cathode materials with high capacity and excellent rate capability. Graphene-based nanomaterials have been recognized as one of the most promising cathodes for LICs due to their unique properties, and exciting progress has been achieved. Herein, in this review, the recent advances of graphene-based cathode materials for LICs are systematically summarized. Especially, the synthesis method, structure characterization and electrochemical performance of various graphene-based cathodes are comprehensively discussed and compared. Furthermore, their merits and limitations are also emphasized. Finally, a summary and outlook are presented to highlight some challenges of graphene-based cathode materials in the future applications of LICs.

The catalytic transformation of biomass-based furan compounds (furfural and HMF) for the synthesis of organic chemicals is one of the important ways to utilize renewable biomass resources. Among the numerous high-value products, cyclopentanone derivatives are a kind of valuable compound obtained by the hydrogenation rearrangement of furfural and HMF in the aqueous phase of metal–hydrogen catalysis. Following the vast application of cyclopentanone derivatives, this reaction has attracted wide attention since its discovery, and a large number of catalytic systems have been reported to be effective in this transformation. Among them, the design and synthesis of metal catalysts are at the core of the reaction. This review briefly introduces the application of cyclopentanone derivatives, the transformation mechanism, and the pathway of biomass-based furan compounds for the synthesis of cyclopentanone derivatives. The important progress of metal catalysts in the reaction since the first report in 2012 up to now is emphasized, the characteristics and catalytic performance of different metal catalysts are introduced, and the critical role of metal catalysts in the reaction is discussed. Finally, the future development of this transformation process was prospected.

The hydrogenation of furan ring in the biomass-derived furans is of great importance for the conversion of biomass to valuable chemicals. Fabrication of high activity and selectivity catalyst for this hydrogenation under mild conditions was one of the focuses of this research. In this manuscript, UiO-66-v, in which vinyl bonded to the benzene ring, was first prepared. Then, the uniformly distributed vinyl was used as the reductant for the preparation of Pd/UiO-66-v. The catalyst was characterized by X-ray diffraction, thermogravimetric, N₂ physical adsorption/desorption, X-ray photoelectron spectroscopy, scanning electron microscope, transmission electron microscopy, energy dispersive spectrometer elemental mappings, and inductively coupled plasma atomic emission spectroscopy to find the Pd/UiO-66-v had a narrow palladium nanoparticles size of 3–5 nm and maintained the structure and thermal stability of UiO-66-v. The Pd/UiO-66-v was used for the hydrogenation of furfuryl alcohol to tetrahydrofurfuryl alcohol in water. 99% conversion of furfuryl alcohol was obtained with 90% selectivity to tetrahydrofurfuryl alcohol after reacted at 0.5 MPa H₂, 303 K for 12 h. The Pd/UiO-66-v was proved to be effective for the hydrogenation of furan ring in furans and could be used for at least five times.

The growing demand for high performance from supercapacitors has inspired the development of porous nanocomposites using renewable and naturally available materials. In this work, a formaldehyde-free phenolic resin using monosaccharide-based furfural was synthesized to act as the carbon precursor. One dimensional halloysite nanotube (HNT) with high porosity and excellent cation/anion exchange capacity was mixed with the phenol-furfural resin to fabricate carbonaceous nanocomposite HNT/C. Their structure and porosity were characterized. The effects of the halloysite nanotube amount and carbonization temperature on the electrochemical properties of HNT/C were explored. HNT/C exhibited rich porosity, involving a large specific surface area 253 m²·g⁻¹ with a total pore volume of 0.27 cm³·g⁻¹. The electrochemical performance of HNT/C was characterized in the three-electrode system and showed enhanced specific capacitance of 146 F·g⁻¹ at 0.2 A g⁻¹ (68 F·g⁻¹ for pristine carbon) in electrolyte (6 mol·L⁻¹ KOH) and a good rate capability of 62% at 3 A g⁻¹. It also displayed excellent cycle performance with capacitance retention of 98.5% after 500 cycles. The symmetric supercapacitors with HNT/C-1:1.5-800 electrodes were fabricated, exhibiting a high energy density of 20.28 Wh·Kg⁻¹ at a power density of 100 W·Kg⁻¹ in 1 M Na₂SO₄ electrolyte. The present work provides a feasible method for preparing composite electrode materials with a porous structure from renewable phenol-furfural resin and HNT. The excellent supercapacitance highlights the potential applications of HNT/C in energy storage.