Silver diamine nitrate (SDN) is expected to help control caries similar to silver diamine fluoride (SDF). The aim of this study was to determine the mineral precipitation in demineralized dentin and the cytotoxicity of SDN and SDF to dental pulp cells. Demineralized dentin specimens were prepared, and SDF, SDN, or water (control) was applied. The specimens were then remineralized in simulated body fluid for 2 weeks. The mineral precipitation in the specimens was examined using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). Additionally, the cytotoxicity of SDF and SDN to human dental pulp stem cells was analyzed using an MTT assay. The increase in FTIR spectra attributable to apatite formation in demineralized dentin in the SDF group was significantly higher compared to the SDN and control groups (p < 0.05). Dentinal tubule occlusion by the precipitation of silver salts was detected in both SDF and SDN groups. The mineral density as shown in SRXTM images and cytotoxicity of both SDN and SDF groups were comparable (p > 0.05). In conclusion, SDF demonstrated superior in vitro apatite formation compared to SDN. However, the degree of mineral precipitation and cytotoxic effects of both were similar.

This paper elucidates the influence of borax decahydrate addition on the flexural and thermal properties of 10 mm thin fly ash/ladle furnace slag (FAS) geopolymers. The borax decahydrate (2, 4, 6, and 8 wt.%) was incorporated to produce FAB geopolymers. Heat treatment was applied with temperature ranges of 300 °C, 600 °C, 900 °C, 1000 °C and 1100 °C. Unexposed FAB geopolymers experienced a drop in strength due to a looser matrix with higher porosity. However, borax decahydrate inclusion significantly enhanced the flexural performance of thin geopolymers after heating. FAB2 and FAB8 geopolymers reported higher flexural strength of 26.5 MPa and 47.8 MPa, respectively, at 1000 °C as compared to FAS geopolymers (24.1 MPa at 1100 °C). The molten B₂O₃ provided an adhesive medium to assemble the aluminosilicates, improving the interparticle connectivity which led to a drastic strength increment. Moreover, the borax addition reduced the glass transition temperature, forming more refractory crystalline phases at lower temperatures. This induced a significant strength increment in FAB geopolymers with a factor of 3.6 for FAB8 at 900 °C, and 4.0 factor for FAB2 at 1000 °C, respectively. Comparatively, FAS geopolymers only achieved 3.1 factor in strength increment at 1100 °C. This proved that borax decahydrate could be utilized in the high strength development of thin geopolymers.

The focus of this study is the fabrication of innovative and sustainable ceramic-based geopolymer with improved low temperatures performances. Kaolin was mixed with liquid sodium silicate (Na₂SiO₃) and 12M of sodium hydroxide (NaOH) solution using alkali activator ratio of 0.24 and solid-to-liquid ratio of 1:1 to synthesize kaolin geopolymer. The effect of the sintering profile on the microstructure, pore evolution and flexural strength were investigated. The heating exposure aided consolidation and created a fairly uniform microstructure, resulting in a smooth surface texture. In comparison to the unheated geopolymer, 3D pore distribution showed a significant increase in the range size of ~30 µm with the appearance of isolated and intergranular pores. The flexural strength at 1200 °C with a heating rate of 5 °C/min and was increased by 146.4% to 85.4 MPa, as compared to the heating rate of 2 °C/min. The sintering process has an impact on the final microstructure formation thus improving the characteristic of geopolymer-based nepheline ceramic.

Silver diamine fluoride (SDF) is a cost-effective method for arresting active dental caries. However, the limited cooperation of patients may lead to an SDF application time that is shorter than the recommended 1–3 min for carious lesions. Therefore, the aim of this study was to assess the effect of different application times of SDF on the degree of mineral precipitation in demineralized dentin. Demineralized dentin specimens from permanent maxillary molars were treated by applying 38% SDF for 30, 60, or 180 s. Water was applied in the control group. The specimens were immersed in simulated body fluid for 2 weeks, and the mineral precipitation in demineralized dentin was then analyzed using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). The FTIR-ATR results showed a significant increase in mineral precipitation in the 180 s group after 1 week. However, after 2 weeks, the SRXTM images indicated comparable mineral density between the 30, 60, and 180 s groups. The precipitation of silver chloride and calcium phosphate crystals that occluded dentinal tubules was similar in all experimental groups. In conclusion, an application time of either 30, 60, or 180 s promoted a comparable degree of mineral precipitation in demineralized dentin.

This study developed a sustainable super-disintegrant derived from Dioscorea hispida Dennst. var. hispida starch for use in immediate-release pharmaceutical tablets. Native starch (NS) was extracted and chemically modified via carboxymethylation to obtain carboxymethyl starch (CMS), followed by phosphate cross-linked to yield modified starch (MS). Physicochemical properties demonstrated that MS exhibited superior water uptake, swelling, and viscosity compared to NS and CMS. Scanning Electron Microscopy (SEM) revealed smaller and more uniform granules in MS, confirming enhanced structural modification. Preliminary tablet trials with dicalcium phosphate showed that 4% w/w MS achieved the fastest disintegration (16.5 s). In paracetamol tablets prepared by wet granulation, MS significantly improved hydration and disintegration performance relative to NS and CMS. Although commercial sodium starch glycolate (SSG) provided slightly faster disintegration, dissolution profiles of tablets containing MS and SSG were statistically equivalent (f₁ = 7, f₂ = 63), confirming comparable efficacy. Porosity analysis using synchrotron radiation X-ray tomography (SR-XTM) indicated that wet-granulated tablets possessed higher intra- and inter-granular porosity than direct compression tablets, facilitating rapid water penetration and disintegration. In contrast, denser direct compression tablets exhibited greater friability and lower mechanical integrity. Modified Dioscorea hispida starch demonstrated excellent disintegration efficiency, eco-friendliness, and local availability, presenting a promising natural alternative to synthetic super-disintegrants in immediate-release tablet formulations.

Ancient potteries found at Ban Muang Bua, located in northeastern Thailand, associate with Thung Kula Ronghai culture. Most of them are products used in daily life and grave goods. The potsherds were examined using techniques based on X-ray spectroscopy. Elemental composition and morphology were analyzed using proton-induced X-ray emission spectroscopy (PIXE) and scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM-EDS). Three-dimensional analysis was performed using X-ray tomographic microscopy based on synchrotron radiation (SR XTM). Irregular plate-like particles of composites with a wide range of size distribution were found in the potsherds. The major (O, Si, and Al), minor (C, Fe, Ca, and K), and trace elements (P, S, Ti, Na, Mg, and Zn) which were observed can provide the information about raw materials and production of pottery. The 3D tomographic images show the internal feature of these samples. The combination of SEM-EDS, PIXE, and SR XTM is a powerful tool for archaeological research especially in terms of composition and internal structure. The results imply that the raw materials of pottery were sandy soil derived from marine sands, clays, and salt deposits that were mostly iron-rich-kaolin clay. The production was carried out with low firing temperatures (~600–900 °C) in open-air kilns.