This article describes the observed and examined effect of crumb rubber on the strength (compressive, bending and splitting tensile) of concrete. The tests have shown that the change in the strength of concrete with crumb rubber waste additives can be forecasted from exponential equations. These relationships enable to foresee the regularities of strength properties when a certain amount of crumb rubber of a certain size fraction is added to concrete. The obtained exponential equations show that concrete compressive, flexural and splitting tensile strengths decrease with increasing crumbed rubber additive amount. The testing has also shown that the addition of a small amount of crumbed rubber slightly increases (7%) the tensile splitting strength. The reason is better adhesion of the cement stone with rubber particles compared to the adhesion of sand, which was replaced by crumbed rubber. With higher content of crumbed rubber additive in the concrete, the tensile splitting strength decreases due to the significant increase of entrained air content and lower density.

This paper analyzes concrete fine aggregate (sand) modification by scrap tire rubber particles-fine crumb rubber (FCR) and coarse crumb rubber (CCR) of fraction 0/1 mm. Such rubberized concrete to get better bonding properties were modified by car-boxylated styrene butadiene rubber (SBR) latex and to gain the strength were modified by glass waste. The following tests—slump test, fresh concrete density, fresh concrete air content, compressive strength, flexural strength, fracture energy, freezing-thawing, porosity parameter, and scanning electron microscope—were conducted for rubberized concretes. From experiments, we can see that fresh concrete properties decreased when crumb rubber content has increased. Mostly it is related to crumb rubber (CR) lower specific gravity nature and higher fineness compared with changed fine aggregate-sand. In this research, we obtained a slight loss of compressive strength when CR was used in concrete However, these rubberized concretes with a small amount of rubber provided sufficient compressive strength results (greater than 50 MPa). Due to the pozzolanic reaction, we see that compressive strength results after 56 days in glass powder modified samples increased by 11–13% than 28 days com-pressive strengths, while at the same period control samples increased its compressive strength about 2.5%. Experiments have shown that the flexural strength of rubberized concrete with small amounts of CR increased by 3.4–15.8% compared to control mix, due the fact that rubber is an elastic material and it will absorb high energy and perform positive bending toughness. The test results indicated that CR can intercept the tensile stress in concrete and make the deformation more plastic. Fracturing of such conglomerate concrete is not brittle, there is no abrupt post-peak load drop and gradually continues after the maximum load is exceeded. Such concrete requires much higher fracture energy. It was obtained that FCR particles (lower than A300) will entrap more micropores content than coarse rubbers because due to their high specific area. Freezing-thawing results have confirmed that Kf values can be conveniently used to predict freeze-thaw resistance and durability of concrete. The test has shown that modification of concrete with 10 kg fine rubber waste will lead to similar mechanical and durability properties of concrete as was obtained in control concrete with 2 kg of prefabricated air bubbles.

This paper analyzes the efficiency of shrinkage reducing additives for the shrinkage deformations of ordinary Portland cement (OPC) concrete and its mechanical properties. OPC concrete was modified with an organic compound-based shrinkage reducing additive (SRA), quicklime, polypropylene fiber, and hemp fiber. It was found that a combination of 2.5% quicklime and 1.5% SRA led to the highest reduction in shrinkage deformations in concrete, and the values of shrinkage reached up to 40.0%. On the contrary, compositions with 1.5% SRA were found to have a significant reduction in compressive strength after 100 freeze-thaw cycles. Hemp fiber did not show a significant shrinkage reduction, but it is an environmentally friendly additive, which can improve OPC concrete flexural strength. Polypropylene fiber can be used in conjunction with shrinkage reducing additives to improve other mechanical properties of concrete. It was observed that 3.0 kg/m³ of polypropylene fiber in concrete could increase flexural strength by 11.7%. Moreover, before degradation, concrete with polypropylene fiber shows high fracture energy and decent residual strength of 1.9 MPa when a 3.5 mm crack appears. The tests showed a compressive strength decrease in all compositions with shrinkage reducing additives and its combinations after 28 days of hardening.

The construction industry’s growth is causing a surge in CO₂ emissions, driven by increased demand for concrete and other building materials. There is a growing demand for more sustainable building materials, including alkali-activated materials. This study investigates the impact of varying ratios of Na₂SiO₃ and NaOH on the mechanical properties and microstructure of metakaolin (MKW) and ceramic brick waste (CBW) based geopolymer binder. Geopolymer binder precursors were made of three main CBW/MKW ratios: 100/0%wt. (C100), 50/50%wt. (C50M50), and 0/100%wt. (M100). Alkaline activator solutions had three different Na₂SiO₃/NaOH ratios: 0.5, 1.0, and 2.0. The investigation into the geopolymer binder mechanical properties was conducted using a range of analytical methods, including compressive strength, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). The findings of the study indicate that the Na₂SiO₃/NaOH ratio alone is inadequate for evaluating geopolymer mechanical properties when different AS/P ratios are employed, given its influence on other parameters, such as the W/S ratio and the total Na₂O content. CBW-based geopolymer binders demonstrate limited capacity to attain substantial compressive strengths because they contain high amounts of unreacted CBW particles, as shown by XRD analysis. The incorporation of MKW precursor resulted in enhanced reactivity and intensified geopolymerization reaction. After the evaluation of all essential ratios, the most favorable Na₂SiO₃/NaOH ratio is 1.0. This determination was based on the highest strengths observed in designs that contained ≥50% of MKW precursor, attributed to predominance of goosecreekite and N-A-S-H gels, as evidenced by XRD and FT-IR analysis.