Increased demand of advanced material like B4C DRMM Al composite due to its excellent mechanical, thermal properties puts the pressure on manufacturing sector because of its machining complication. In this research study, the B4C reinforced Al composite with 15% volume fraction has been developed with stir casting route. Micro holes ranging from diameter 0.38mm have been made over the composite specimen of thickness 0.4 & 0.5mm for which Micro Electro chemical Machine was employed. Totally nine experiments were conducted based on L9 orthogonal array emphasized by Taguchi's technique and the optimum levels were predicted based on the average S/N graph method. During the experiments frequency, voltage, current and electrolytic concentration were considered as the process variables, thereby considering the machining time as the response variable. Additionally, the analysis of variance (ANOVA) has been applied to determine the most significant factor to influence the response. In order to enhance the degree of validation, unconventional optimization tool of fuzzy logic was also employed to compare the results of the optimized model. Results of fuzzy logic and Taguchi's method were deviate in zero tolerance

The effect of crump rubber on the dry sliding wear behavior of epoxy composites is investigated in the present study. Wear tests are carried out for three levels of crump rubber (10, 20, and 30 vol.%), normal applied load (30, 40, and 50 N), and sliding distance (1, 3, and 5 km). The wear behavior of crump rubber–epoxy composites is investigated against EN31 steel discs. The hybrid mathematical approach of Taguchi-coupled Grey Relational Analysis (GRA)—Principal Component Analysis (PCA) is used to examine the influence of crump rubber on the tribological response of composites. Mathematical and experimental results reveal that increasing crump rubber content reduces the wear rate of composites. Composites also show a significant decrease in specific wear values at higher applied loads. Furthermore, the coefficient of friction also shows a decreasing trend with an increase in crump rubber content, indicating the effectiveness of reinforcing crump rubber in a widely used epoxy matrix. Analysis of Variance (ANOVA) results also reveal that the crump rubber content in the composite is a significant parameter to influence the wear characteristic. The post-test temperature of discs increases with an increase in the applied load, while decreasing with an increase in filler loading. Worn surfaces are analyzed using scanning electron microscopy to understand structure–property correlations. Finally, existing studies available in the literature are compared with the wear data of the present study in the form of a property map.

The present work aimed to analyze the roll of carbon nano tubes and graphene nano fillers on the mechanical and thermal characteristics of hollow glass microsphere reinforced epoxy composites. Composites with varying content of hollow glass microballoons (2, 4, 6, 8, and 10 wt %) reinforced in epoxy matrix were fabricated. Additionally, two more types of composites, one with graphene nano fillers and the other with carbon nano tube at a constant 0.5 wt %, were fabricated with varying weight percentages of hollow glass microballoons (2, 4, 6, 8, and 10%). The composites were fabricated using an open mold casting process. Composites were tested for thermal and mechanical properties. The tensile and flexural moduli were found to rise as the HGM concentration increased. Graphene-filled HGM/epoxy composites revealed the highest modulus compared with HGM/epoxy and HGM/CNT/epoxy composites. The impact strength of all composite types decreased as the HGM content increased. Neat epoxy specimens revealed low response as compared with all the composites tested. Further, the thermal conductivity of HGM/epoxy composites was lower as compared with other compositions and neat epoxy. Scanning electron microscopy was used to analyze the surface morphological behavior of the composites subjected to flexural test. It was found that HGM/G/E composites with 10% of HGM and 0.5% of graphene by weight in epoxy matrix were the optimum.

The development of aluminium composite with the inclusion of advanced materials is a continuous research process due to the increasing industrial demand for advanced hybrid materials. To cater for this need, this research work focuses on the development of Al 7075 alloy reinforced with TiB₂ and graphene and on the evaluation of its strengthening mechanism. Two different modes of improving the strength of the hybrid composite have been followed; one is by the inclusion of graphene at three levels of 0.1, 0.2 and 0.3%, and another by the processing route, squeeze casting technique by compression of the molten hybrid composite slurry before casting. The microstructure and characterisation of the composite material are examined and analysed with the help of XRD, SEM, EDAX and chemical spectroscopy. A microstructure evaluation is employed to justify the homogenous dispersal and the existence of reinforced particles. A tensile test is conducted at room temperature and high temperature environments to assess the tensile strength. The research outcome affirms that a significant improvement in tensile and hardness has been noted in comparison with base alloy. The fracture-morphology results affirm the change in fracture mode from brittle to ductile when the tensile testing environment changes from room temperature to high temperature. Finally, the dispersion strengthening mechanism is validated with an empirical approach.