Polydimethylsiloxane (PDMS) is one of the most promising elastomers due its remarkable proprieties such as good thermal stability, biocompatibility, corrosion resistance, flexibility, low cost, ease of use, chemically inertia, hyperplastic characteristics, and gas permeability. Thus, it can be used in areas such as microfluidic systems, biomedical devices, electronic components, membranes for filtering and pervaporation, sensors, and coatings. Although pure PDMS has low mechanical properties, such as low modulus of elasticity and strength, it can be improved by mixing the PDMS with other polymers and by adding particles or reinforcements. Fiber-reinforced PDMS has proved to be a good alternative to manufacturing flexible displays, batteries, wearable devices, tactile sensors, and energy harvesting systems. PDMS and particulates are often used in the separation of liquids from wastewater by means of porosity followed by hydrophobicity. Waxes such as beeswax and paraffin have proved to be materials capable of improving properties such as the hydrophobic, corrosion-resistant, thermal, and optical properties of PDMS. Finally, when blended with polymers such as poly (vinyl chloride-co-vinyl acetate), PDMS becomes a highly efficient alternative for membrane separation applications. However, to the best of our knowledge there are few works dedicated to the review and comparison of different PDMS composites. Hence, this review will be focused on PDMS composites, their respective applications, and properties. Generally, the combination of elastomer with fibers, particles, waxes, polymers, and others it will be discussed, with the aim of producing a review that demonstrates the wide applications of this material and how tailored characteristics can be reached for custom applications.

Polydimethylsiloxane (PDMS) is a polymer that has attracted the attention of researchers due to its unique properties such as transparency, biocompatibility, high flexibility, and physical and chemical stability. In addition, PDMS modification and combination with other materials can expand its range of applications. For instance, the ability to perform superhydrophobic coating allows for the manufacture of lenses. However, many of these processes are complex and expensive. One of the most promising modifications, which consists of the development of an interchangeable coating, capable of changing its optical characteristics according to some stimuli, has been underexplored. Thus, we report an experimental study of the mechanical and optical properties and wettability of pure PDMS and of two PDMS composites with the addition of 1% paraffin or beeswax using a gravity casting process. The composites’ tensile strength and hardness were lower when compared with pure PDMS. However, the contact angle was increased, reaching the highest values when using the paraffin additive. Additionally, these composites have shown interesting results for the spectrophotometry tests, i.e., the material changed its optical characteristics when heated, going from opaque at room temperature to transparent, with transmittance around 75%, at 70 °C. As a result, these materials have great potential for use in smart devices, such as sensors, due to its ability to change its transparency at high temperatures.

Polydimethylsiloxane (PDMS) is one of the best known elastomers and has been used in several areas of activity, due to its excellent characteristics and properties, such as biocompatibility, flexibility, optical transparency and chemical stability. Furthermore, PDMS modified with other materials promotes the desired changes to broaden its range of applications in various fields of science. However, the heating, mixing and degassing steps of the manufacturing process have not received much attention in recent years when it comes to blending with solid materials. For instance, PDMS has been extensively studied in combination with waxes, which are frequently in a solid state at room temperature and as a result the interaction and manufacturing process are extremely complex and can compromise the desired material. Thus, in this work it is proposed a multifunctional vacuum chamber (MVC) with the aim to improve and accelerate the manufacturing process of PDMS composites combined with additives, blends and different kinds of solid materials. The MVC developed in this work allows to control the mixing speed parameters, temperature control and internal pressure. In addition, it is a low cost equipment and can be used for other possible modifications with different materials and processes with the ability to control those parameters. As a result, samples fabricated by using the MVC can achieve a time improvement over 133% at the heating and mixing step and approximately 200% at the last degassing step. Regarding the complete manufacturing process, it is possible to achieve an improvement over 150%, when compared with the conventional manufacturing process. When compared to maximum tensile strength, specimens manufactured using the MVC have shown a 39% and 65% improvement in maximum strain. The samples have also shown a 9% improvement in transparency at room temperature and 12% at a temperature of about 75 °C. It should be noted that the proposed MVC can be used for other blends and manufacturing processes where it is desirable to control the temperature, agitation speed and pressure.