This research reports the manufacturing and characterization of green composites made from recycled polypropylene obtained from the remnants of polypropylene non-woven fabrics used in the textile industry and further reinforced with short hemp fibers (SHFs). To improve the interaction of the reinforcing fibers with the recycled polymeric matrix, two types of compatibilizing agents (maleic anhydride grafted, PP-g-MA, and maleinized linseed oil, MLO) were added during melt-processing, the percentage of which had to remain constant concerning the amount of fiber loading to ensure complete reactivity. Standardized test specimens were obtained by injection molding. The composites were characterized by mechanical (tensile, impact, and hardness), thermal (DSC, TGA), thermomechanical, FTIR, and FESEM microscopy tests. In addition, color and water uptake properties were also analyzed. The results show that the addition of PP-g-MA to rPP was satisfactory, thus improving the fiber-matrix interaction, resulting in a marked reinforcing effect of the hemp fibers in the recycled PP matrix, which can be reflected in the increased stiffness of the samples. In parallel to the compatibilizing effect, a plasticizing effect was obtained by incorporating MLO, causing a decrease in the glass transition temperature of the composites by approximately 6 °C and an increase in ductility compared to the unfilled recycled polypropylene samples.

The main aim of the present work is to evaluate and characterize the mechanical, morphological and thermal properties of wastes coming from the textile industry, mainly composed of cotton and polyester. These wastes will be thereafter implemented in commodity plastic such as polyamide, in order to develop new formulations of environmentally friendly materials. The composites were produced by extrusion and injection-molded processes in amounts between 15 wt.% and 60 wt.% of textile waste. With the objective of improving the properties of the materials, silanes were used as a compatibilizer between the textile fibers and the polymeric matrix. The effect of the compatibilizer in the composites was studied together with the effect of the amount of textile fiber added to the composites. Mechanical, thermal, morphological and wettability properties were analyzed for each composite. The results show that the use of silanes improves the interaction especially in those composites with a higher amount of textile waste, offering a balanced mechanical behavior with significantly high quantities. On the other hand, the melting temperature does not vary significantly with the introduction of silanes and textile waste content, although the incorporation of textile waste slightly reduces up to 23% the degradation temperature of the resulting composites. The wettability of the composites is also increased up to 16% with the incorporation of textile waste. Finally, the appearance of the composites with textile waste is strongly influenced by the incorporation of the reinforcement, offering shades close to dark brown in the whole range of compositions.