Understanding the dissolution of hemicellulose in ionic liquids (ILs) is important in order to explore efficient utilization of ILs for fractionating lignocellulose and extracting hemicellulose. In this study, three ILs, namely 1-butyl-3-methylimidazolium chloride (BmimCl), 1-butyl-3-methylimidazol-ium bromide (BmimBr), and 1-butyl-3-methylimidazolium iodide (BmimI), were used as solvents to dissolve bamboo hemicellulose over the temperature range of 80 °C to 150 °C. Representative hemicellulose with a solubility higher than 9.0 g/100 g IL was regenerated and characterized. The interaction between the hemicellulose and ILs was evaluated using carbon-13 nuclear magnetic resonance. The results showed that the solubility of hemicellulose in the ILs was in the following order: BmimCl > BmimBr > BmimI. Though moderate degradation of the hemicellulose possibly occurred during dissolution, the main chain of the hemicellulose was almost unchanged. The enhanced solubility of the hemicellulose was because of the formation of hydrogen bonds between the hydroxyl proton of the hemicellulose and anion of the ILs.

Although metal-organic frameworks (MOFs) are advantageous to the removal of organic pollutants, the general MOFs in powder form is disadvantageous to their practical applications. In-situ MOF synthesis in alginate gel is a good way to fabricate an MOF composite for many applications, which is different from blending MOF particles with polymers. In-situ synthesis of Zeolitic Imidazolate Framework-8 (ZIF-8) in alginate gel is in the form of beads with rough wrinkles and has many pores inside. When used as an absorbent, in-situ synthesis of ZIF-8 in alginate gel could remove 97.7±0.9% of ofloxacin from ofloxacin solution and the equilibrium adsorption capacity is up to 160.6±1.3 mg/g. During the adsorption, ofloxacin is first brought into the gel by the solvent exchange and gel microchannel adsorption, and it can then be absorbed by in-situ ZIF-8. Moreover, the adsorption efficiency can reach 85.5% even after four cycles of adsorption. We believe that in-situ synthesis of ZIF-8 in alginate gel will be an appropriate material for the removal of ofloxacin in the wastewater. GRAPHICAL ABSTRACT

Superhydrophobic surfaces possess low mechanical strength, and can be easily contaminated by fluids with low surface tension, such as oil; this hinders their practical applications. In this study, fluorinated epoxy was prepared through the thiol-ene click reaction at first. The superhydrophobic surface with high oil-repellency was prepared by the addition of unmodified nano-SiO₂ and micron-SiO₂ to the fluorinated epoxy. The effect of the ratio of micro- and nano-silica particles on the morphology and wettability of the coating was investigated. It was shown that a re-entrant structure appears and FEP-S coating has good liquid repellency when the amounts of nano-SiO₂ and micro-SiO₂ are equal. The contact angles of the FEP-S coating (coating with the best liquid repellent performance) for water, glycerol, ethylene glycol, and diiodomethane were 158.6° ± 1.1°, 152.4° ± 0.9°, 153.4° ± 1.3°, and 140.7° ± 0.9°, respectively. In addition, the superhydrophobic coatings possess excellent mechanical and chemical durability, excellent performance in self-cleaning, corrosion resistance, and anti-icing properties. The preparation method of superhydrophobic coating is relatively simple; therefore, it has a wide range of applications and can also be applied to various substrates.