The thermal conductivity of alloys is gradually becoming appreciated. It is often assumed that heat treatment can improve the thermal conductivity of Al-Si-Mg-Cu alloys, but there has been little relevant research. This paper studies the effects of different casting processes and short T6 heat treatment (ST6) on the thermal conductivity and mechanical properties of Al-Si-Mg-Cu alloys. The results show that a microstructure with fine α-Al crystal grains can be obtained by semi-solid die casting (SSDC), improving the mechanical properties of the Al-Si-Mg-Cu alloy in the as-cast state. After SSDC, the size and aspect ratio of eutectic silicon can be reduced by ST6 treatment, effectively improving the thermal conductivity and mechanical properties of the alloy. Finally, the influence of eutectic silicon on electron transport is analyzed in detail. With the SSDC + ST6 processing technology, Al-Si-Mg-Cu alloys with excellent thermal conductivity and mechanical properties can be obtained.

In this paper, the effects of size, morphology and distribution of eutectic silicon on the thermal conductivity of Al-8Si alloy modified by Sr (0.04, 0.08, 0.12 wt.%) and Sb (0.1, 0.3, 0.5 wt.%) elements with T6 heat treatment were investigated. The results show that the modified fibrous eutectic silicon has a significant capability of improvement of thermal conductivity, while the amount of the modifier has a relatively weak effect on thermal conductivity. After T6 treatment, the fracture or spheroidization of the flake eutectic silicon and the disappearance of clustering phenomenon could raise thermal conductivity, but the coarsening of fibrous eutectic silicon is inconducive to thermal conductivity. Finally, the effect of eutectic silicon on electron transport is analyzed in detail, which could provide a reference for enhancing the thermal (or electrical) conductivity of hypoeutectic Al-Si alloy through effective microstructure control.

The high-temperature superplastic deformation behavior of rolled Mg-8Al-2Sn (AT82) and Mg-8Al-1Sn-1Zn (ATZ811) alloys were investigated in this study. During tensile deformation at 573 K, no obvious grain growth occurred in both alloys, because of the high-volume fraction of second phases located at grain boundaries. Meanwhile, texture weakening was observed, suggesting that grain boundary sliding (GBS) is the dominant superplastic deformation mechanism, which agreed well with the strain rate sensitivity (m) and the activation energy (Q) calculations. The microstructural evolution during tensile deformation manifested that there were more and larger cavities in AT82 than ATZ811 during high-temperature tensile deformation. Therefore, superior superplasticity was found in the ATZ811 alloy that presented a tensile elongation of ~510% under a strain rate of 10⁻³ s⁻¹ at 573 K, in contrast to the relatively inferior elongation of ~380% for the AT82 alloy. Meanwhile, good tensile properties at ambient temperature were also obtained in ATZ811 alloy, showing the ultimate tensile strength (UTS) of ~355 MPa, yield strength (YS) of ~250 MPa and elongation of ~18%. Excellent mechanical performance at both ambient and elevated temperatures can be realized by using economical elements and conventional rolling process, which is desirable for the industrial application of Mg alloy sheets.

The microstructure and mechanical properties of a Mg-6Al-1Zn-0.9Sn alloy processed by equal channel angular pressing (ECAP) at temperatures of 250 °C and 300 °C were investigated. It was found that the refinement of the microstructure was very dependent on the processing temperature. The main reason for the difference in grain refinement was the precipitation of secondary-phase particles. Texture information obtained by electron back-scatter diffraction (EBSD) showed the gradual formation of a 45° texture during the ECAP process, while the maximum intensity was different for processing temperatures at 250 °C and 300 °C. By calculating the contribution from different strengthening mechanisms, it was found that a 45° texture had a huge influence on grain boundary strengthening and thus the yield strength.

As the applications of heterogeneous materials expand, aluminum laminates of similar materials have attracted much attention due to their greater bonding strength and easier recycling. In this work, an alloy design strategy was developed based on accumulative roll bonding (ARB) to produce laminates from similar materials. Twin roll casting (TRC) sheets of the same composition but different cooling rates were used as the starting materials, and they were roll bonded up to three cycles at varying temperatures. EBSD showed that the two TRC sheets deformed in distinct ways during ARB processes at 300 °C. Major recrystallizations were significant after the first cycle on the thin sheet and after the third cycle on the thick sheet. The sheets were subject to subsequent aging for better mechanical properties. TEM observations showed that the size and distribution of nano-precipitations were different between the two sheet sides. These nano-precipitations were found to significantly promote precipitation strengthening, and such a promotive effect was referred to as hetero-deformation induced (HDI) strengthening. Our work provides a new promising method to prepare laminated heterogeneous materials with similar alloy TRC sheets.

It has been well known that electric pulse can be utilized to enhance the plasticity of metals, which is attributed to the change of dislocation dynamics, e.g., localized planar slip to homogeneous wavy slip. Here, we show another effect of pulse current, which facilitates texture weakening through room-temperature dynamic recrystallization and additionally improve the plasticity of a polycrystalline Mg-3Al-1Sn-1Zn alloy. By conducting a tensile test under electrical pulse, we found that the peak flow stress and fracture strain depend strongly on current density. As peak current densities increases, the flow stress drops and the fracture strain increases. Our Electron Backscatter Diffraction results suggest that dynamic recrystallization occurs at room temperature, which develops a weakened texture. Our work provides a new insight into electroplasticity mechanism in Mg alloys.