Sweet sorghum bagasse (SSB) and citric acid (CA) were used as sustainable raw materials in the development of environmentally friendly particleboard. Sucrose was added to improve the mechanical and physical properties of the particleboard. The effects of the weight ratio between CA and sucrose on the physical properties of the particleboards were investigated. The mechanical properties of particleboards bonded with adhesives at 15/85 and 10/90 wt.% ratios of CA to sucrose were superior to particleboard with other ratios. The thickness swelling of the particleboard increased with an increasing sucrose ratio. Moreover, the physical properties of the particleboard were comparable to those of particleboard bonded using phenol formaldehyde (PF) resin and satisfied the requirements of the type 18 JIS A 5908 (2003) standard. Also, the brittleness of the particleboard was decreased by adding sucrose. Low formaldehyde emission and biological durability against termites and decay were obtained by particleboard under suitable ratios of CA to sucrose. According to the results from thermal analysis and infrared spectra measurement, reactions leading to ester linkages occurred among the CA, sucrose, and SSB components.

Incorporating antimicrobial components into food packaging materials can prevent microbial contamination. Fungus combs could be an alternative source of natural antimicrobial agents. In this study, n-hexane, ethyl acetate, methanol, and water extracts were obtained from fungus combs isolated from Indomalayan termite (Macrotermes gilvus Hagen) mound. Their antibacterial and antifungal activities against food spoilage microorganisms including Escherichia coli ATCC 25922, Pseudomonas aeruginosaATCC 27853, Staphylococcus aureus ATCC 25923, Aspergillus flavus, and Aspergillus niger were evaluated by Kirby–Bauer disc diffusion and microdilution. Results showed that ethyl acetate extract formed the largest diameter inhibition zone for all tested bacteria and fungi, exhibited antibacterial activity against all tested bacteria with minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) values of 0.39 and 0.78 mg/mL, respectively, and suppressed A. flavus and A. niger with an MIC value of 0.78 mg/mL. This extract contained guaiacol and syringol, which were predicted as the main antimicrobial components in fungus comb. n-Hexane extract only inhibited Gram-positive bacteria. S. aureus ATCC 25923 was the most sensitive to all the extracts, and A. flavus was more sensitive than A. niger. All these fungus comb extracts exhibited antimicrobial activity against E. coli ATCC 25922, P. aeruginosa ATCC 27853, S. aureus ATCC 25923, A. flavus, and A. niger. This study revealed that fungus comb extracts, especially ethyl acetate, could be considered as a new antimicrobial agent. Graphical Abstract

The objective of this study was to evaluate various physical and mechanical properties of experimental particleboard panels made from Asian giant bamboo (Dendrocalamus asper). Single layer panels having a density level of 0.75 g/cm³ from coarse and fine particles were used within the scope of this study. Thickness swelling, water absorption, surface roughness, and wettability characteristics of the samples were tested as physical properties while bending, internal bond strength, and screw withdrawal strength of the panels were considered for their mechanical properties. Resistance of the panels against termite and fungus were also determined. Based on the findings in the work both physical and mechanical properties of the panels made from coarse particles resulted in higher values than those made from fine particles with the exception of their internal bond strength. It appears that using fine particles in the panels enhanced their overall surface quality as well as wettability. Regarding biological deterioration of the samples, those made with coarse particles had better resistance. It seems that giant bamboo as a non-wood lignocellulosic species would have potential to be used as raw material to the manufacture value added particleboard with accepted characteristics.

The objective of this work was to investigate the resistance of three Indonesian wood species to termite attack. Samples from sengon (Falcataria moluccana), mangium (Acacia mangium), and pine (Pinus merkusii) were treated with polystyrene at loading levels of 26.0%, 8.6%, and 7.7%, respectively. Treated and untreated samples were exposed to environmental conditions in the field for 3 months. Untreated specimens of sengon, mangium, and pine had resistance ratings of 3.0, 4.6, and 2.4, respectively, based on a 10-point scale from 0 (no resistance) to 10 (complete or near-complete resistance). Corresponding resistance values of 7.8, 7.2, and 8.2 were determined for specimens treated with polystyrene. Overall weight loss values of 50.3%, 23.3%, and 66.4% were found for untreated sengon, mangium, and pine samples, respectively; for treated samples, the values were 7.6%, 14.4%, and 5.1%, respectively. Based on the findings in this study, overall resistance to termite attack was higher for treated samples compared to untreated samples.

Standardized laboratory testing of wood and wood-based products against subterranean termites in Indonesia (SNI 01.7207-2006) (SNI) has no requirement for the inclusion of a comparative reference species of wood (reference control). This is considered a weakness of the Indonesian standard. Consequently, a study was undertaken to identify a suitable Indonesian species of community wood that could be used as a reference control. Four candidate species of community woods: Acacia mangium, Hevea brasiliensis, Paraserianthes falcataria and Pinus merkusii were selected for testing their susceptibility to feeding by Coptotermes formosanus. Two testing methods (SNI and the Japanese standard method JIS K 1571-2004) were used to compare the susceptibility of each species of wood. Included in the study was Cryptomeria japonica, the reference control specified in the Japanese standard. The results of the study indicated that P. merkusii is a suitable reference species of wood for inclusion in laboratory tests against subterranean termites, conducted in accordance with the Indonesian standard (SNI 01.7207-2006).

The population of South Jakarta, a city within the Province of Jakarta Capital Region, is increasing annually, and the development of land into building causes termite diversity loss. The aim of this research was to determine the diversity of subterranean termite species and their distribution in South Jakarta and to evaluate the soil profile termite habitat. This study was conducted in South Jakarta and was carried out at four residential areas representing four randomly selected sub-districts. Specimens were collected with a baiting system. At each residence, as many as 25–30 stakes of pine wood (Pinus merkusii) sized 2 cm × 2 cm × 46 cm were placed for termite sampling. Soil samples were also collected from each residence for testing of their texture, pH, soil water content, and C-organic. Three species of subterranean termites were identified, including Coptotermes curvignathus, Microtermes insperatus, and Macrotermes gilvus, with area-specific variations in occurrence. The soil and weather conditions in the studied areas provided suitable habitat for termites, and M. insperatus was the most commonly found species.