This paper investigates how the use of construction and demolition waste can affect the durability and affect the mechanical performance of concrete. tests such as compressive strength, tensile strength by diametral compression and modulus of elasticity were performed. Regarding durability, tests such as water immersion, void content and specific mass, water absorption by capillarity, electrical resistivity, the penetration depth of chloride ions, accelerated carbonation and a test evaluating the synergic effect of carbon dioxide and chloride ion penetration were performed. The coarse natural aggregate was replaced with coarse recycled aggregate in concrete mixes at the following ratios: 30%, 50%, 70%, and 100%. The results indicate that the parameters of the concrete produced with recycled aggregate, especially up to 50% replacement level, meet the concrete quality requirements, regarding the mechanical properties and durability.

A escória de aciaria é coproduto siderúrgico, com comportamento expansivo, para cuja incorporação em produtos da construção civil necessita passar por processos de estabilização. O processo denominado BSSF (do inglês Baosteel Slag Short Flow – Fluxo Curto de Escória da Baosteel) é uma novidade tecnológica no Brasil, que consiste no resfriamento e estabilização de grandes montantes de material, em menor tempo quando comparado ao tratamento convencional. Embora se visualize tal processo como algo promissor, faltam, todavia, estudos que comprovem sua eficácia. Assim, este trabalho tem como objetivo investigar as propriedades mecânicas de concretos produzidos com a incorporação de agregados de escória de aciaria BSSF. Os traços de concreto foram desenvolvidos para classe de agressividade ambiental II, com resistência mínima de 25 MPa aos 28 dias. Como materiais, foram utilizados CP V-ARI, brita granítica, areia quartzosa, escória de aciaria BSSF e aditivo superplastificante. Assim, foram desenvolvidos cinco traços de concreto, com teores de substituição dos agregados naturais pela escória de aciaria BSSF de 0% (referência), 20%, 40%, 60% e 80%, em volume. Foram determinadas a consistência, massa específica e teor de ar incorporado. No estado endurecido, foram determinados a resistência à compressão axial (nas idades de 7, 28 e 91 dias) e o módulo de elasticidade estático (nas idades de 28 e 91 dias) dos concretos. Em geral, os concretos com escória de aciaria BSSF apresentaram desempenho mecânico superior ao traço de referência, com exceção do traço de 80% nas primeiras idades. Ademais, destaca-se o traço com 60% de escória, por ter alcançado os ganhos mais expressivos nas propriedades mecânicas.

Due to the high aggressiveness in which the concrete structures are exposed, many researches have been developed in this area and search for materials with superior mechanical performance and durability has been the target of the researchers of concrete technology. Therefore, concrete obtained from the microstructure engineering are needed. Being composites made of fine grain particles and a low water/binder ratio, these materials have dense matrix by optimizing the packing of granular materials. Thus, this paper uses the concept of particles packing in the design of special concretes, analyzing the durability of these materials by determining the water absorption by immersion and by capillary, and chloride ion penetration. The properties of concrete designed based on this concept are compared to high performance concrete designed from conventional methodology, indicating superior properties in terms of durability.

O pó de vidro incorporado ao concreto convencional vem sendo estudado em relação à sua influência na resistência mecânica e durabilidade. Este trabalho visa avaliar a durabilidade de compósitos cimentícios de ultra alto desempenho (CCUAD) com substituição parcial do cimento por vidro finamente moído, por meio do ensaio de migração de cloretos utilizando o método da NT Build 492. Para tanto foram moldados corpos de prova com teores de pó de vidro de 0%, 10%, 20%, 30% e 50% em relação ao volume de cimento e a avaliação foi feita na idade de 28 dias. Os resultados indicam que, em teores baixos, o pó de vidro não prejudica as propriedades dos compósitos e em teores mais altos os compósitos mantêm boas características mecânicas e de durabilidade.

The alkali-silica reaction (ASR) is one of the problems that can compromise concrete durability, as the chemical reactions between the reactive aggregate and concrete pore solution, specifically sodium (Na⁺), potassium (K⁺), calcium (Ca²⁺) and hydroxyl (OH^-) in the presence of moisture, trigger expansion and cracking of concrete elements. The use of pozzolanic materials, such as finely ground glass powder (particles smaller than 75μm), to partially replace cement has been widely studied and has demonstrated beneficial results. However, because the behavior of pozzolans towards ASR is not completely understood yet, this work evaluates the effect of incorporating ground glass powder into cementitious composites against ASR. To this end, 8% silica fume was used as a control admixture, and four levels of glass powder (10, 20, 30, and 50%) were incorporated into the cementitious mixture to partially replace cement. Expansion tests were carried out in accordance with NBR15577-4 (ABNT, 2018) on mortar bars using the accelerated test method to assess the mitigation of expansions. The results show that the expansions caused by ASR decreased with the increasing content of glass powder in the cement mixtures. Furthermore, only the 50% level reduced the expansions to a safe value according to the Brazilian standard.