In tissue engineering, design of biomaterial with a micro/nano structure is an essential step to mimic extracellular matrix (ECM) and to enhance biomineralization as well as cell biocompatibility. Composite polymeric nanofiber with iron particles/ions has an important role in biomineralization and collagen synthesis for bone tissue engineering. Herein, we report development of polymeric cellulose acetate (CA) nanofibers (17 wt.%) and traces of iron acetates salt (0.5 wt.%) within a polymeric solution to form electrospinning nanofibers mats with iron nanoparticles for bone tissue engineering applications. The resulting mats were characterized using field emission scanning electron microscopy (FESEM), transmission electron microscope (TEM), Fourier transform infrared (FTIR), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The resulted morphology indicated that the average diameter of CA decreased after addition of iron from (395 ± 30) to (266 ± 19) nm and had dense fiber distributions that match those of native ECM. Moreover, addition of iron acetate to CA solution resulted in mats that are thermally stable. The initial decomposition temperature was 300 °C of CA/Fe mat > 270 °C of pure CA. Furthermore, a superior apatite formation resulted in a biomineralization test after 3 days of immersion in stimulated environmental condition. In vitro cell culture experiments demonstrated that the CA/Fe mat was biocompatible to human fetal-osteoblast cells (hFOB) with the ability to support the cell attachment and proliferation. These findings suggest that doping traces of iron acetate has a promising role in composite mats designed for bone tissue engineering as simple and economically nanoscale materials. Furthermore, these biomaterials can be used in a potential future application such as drug delivery, cancer treatment, and antibacterial materials.

Multifunctional membrane technology has gained tremendous attention in wastewater treatment, including oil/water separation and photocatalytic activity. In the present study, a multifunctional composite nanofiber membrane is capable of removing dyes and separating oil from wastewater, as well as having antibacterial activity. The composite nanofiber membrane is composed of cellulose acetate (CA) filled with zinc oxide nanoparticles (ZnO NPs) in a polymer matrix and dipped into a solution of titanium dioxide nanoparticles (TiO₂ NPs). Membrane characterization was performed using transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), and Fourier transform infrared (FTIR), and water contact angle (WCA) studies were utilized to evaluate the introduced membranes. Results showed that membranes have adequate wettability for the separation process and antibacterial activity, which is beneficial for water disinfection from living organisms. A remarkable result of the membranes’ analysis was that methylene blue (MB) dye removal occurred through the photocatalysis process with an efficiency of ~20%. Additionally, it exhibits a high separation efficiency of 45% for removing oil from a mixture of oil–water and water flux of 20.7 L.m⁻² h⁻¹ after 1 h. The developed membranes have multifunctional properties and are expected to provide numerous merits for treating complex wastewater.