The global plastics crisis has recently focused scientists’ attention on finding technical solutions for the ever-increasing oversupply of plastic waste. Black plastic is one of the greatest contributors to landfill waste, because it cannot be sorted using industrial practices based on optical reflection. However, it can be readily upcycled into carbon nanotubes (CNTs) using a novel liquid injection reactor (LIR) chemical vapor deposition (CVD) method. In this work, CNTs were formed using black and white polystyrene plastics to demonstrate that off-the-shelf materials can be used as feedstock for growth of CNTs. Scanning electron microscopy analysis suggests the CNTs from plastic sources improve diameter distribution homogeneity, with slightly increased diameters compared with control samples. Slight improvements in quality, as determined by Raman spectroscopy of the D and G peaks, suggest that plastics could lead to increased quality of CNTs. A small device was constructed as a demonstrator model to increase impact and public engagement.

ZnO nanosheets are a relatively new form of nanostructure and have demonstrated potential as gas-sensing devices and dye sensitised solar cells. For integration into other devices, and when used as gas sensors, the nanosheets are often heated. Here we study the effect of vacuum annealing on the electrical transport properties of ZnO nanosheets in order to understand the role of heating in device fabrication. A low cost, mass production method has been used for synthesis and characterisation is achieved using scanning electron microscopy (SEM), photoluminescence (PL), auger electron spectroscopy (AES) and nanoscale two-point probe. Before annealing, the measured nanosheet resistance displayed a non-linear increase with probe separation, attributed to surface contamination. Annealing to 300 °C removed this contamination giving a resistance drop, linear probe spacing dependence, increased grain size and a reduction in the number of n-type defects. Further annealing to 500 °C caused the n-type defect concentration to reduce further with a corresponding increase in nanosheet resistance not compensated by any further sintering. At 700 °C, the nanosheets partially disintegrated and the resistance increased and became less linear with probe separation. These effects need to be taken into account when using ZnO nanosheets in devices that require an annealing stage during fabrication or heating during use.

Graphene’s novel electrical, optical, and mechanical properties are affected both by substrate interaction and processing steps required to fabricate contacts and devices. Annealing is used to clean graphene devices, but this can lead to doping and defect changes and strain effects. There is often disagreement about which of these effects are occurring and which result in observed changes in Raman spectra. The effects of vacuum annealing on mechanically exfoliated pristine, suspended, and attached thin and thick few-layer graphene on SiO₂/Si are investigated here using scanning electron microscopy (SEM), Raman spectroscopy, and atomic force microscopy (AFM). Before annealing, Raman shows that the differences in 2D and G band positions and the appearance of a disorder-induced D band of all regions were mainly because of compressive or tensile structural deformations emerging through mechanical exfoliation instead of charge doping. Annealing at low temperature is sufficient to eliminate most of the defects. However, compressive strain is induced in the sheet by annealing at high temperature, and for thin regions increased substrate conformation leads to the apparent disappearance of the sheets. The intensity ratio of the 2D and G bands also reduces with induced compressive strain, and thus should not be used to detect doping.