Limbal Stem Cell Deficiency (LSCD) is a very serious and painful disease that often results in impaired vision. Cultivation of limbal stem cells for clinical application is usually performed on carriers such as amniotic membrane or surgical fibrin gel. Transplantation of these grafts is associated with the risk of local postoperative infection that can destroy the graft and devoid therapeutic benefit. For this reason, electrospun scaffolds are good alternatives, as proven to mimic the natural cells surroundings, while their fabrication technique is versatile with regard to polymer functionalization and scaffolds architecture. This study considers the development of poly(ε-caprolactone) (PCL) immune-compatible and biodegradable electrospun scaffolds, comprising cefuroxime (CF) or titanium dioxide (TiO₂) active components, that provide both bactericidal activity against eye infections and support of limbal stem cells growth in vitro. The PCL/CF scaffolds were prepared by blend electrospinning, while functionalization with the TiO₂ particles was performed by ultrasonic post-processing treatment. The fabricated scaffolds were evaluated in regard to their physical structure, wetting ability, static and dynamic mechanical behaviour, antimicrobial efficiency and drug release, through scanning electron microscopy, water contact angle measurement, tensile testing and dynamic mechanical analysis, antimicrobial tests and UV-Vis spectroscopy, respectively. Human limbal stem cells, isolated from surgical remains of human cadaveric cornea, were cultured on the PCL/CF and PCL/TiO₂ scaffolds and further identified through immunocytochemistry in terms of cell type thus were stained against p63 marker for limbal stem cells, a nuclear transcription factor and cytokeratin 3 (CK3), a corneal epithelial differentiation marker. The electrospun PCL/CF and PCL/TiO₂ successfully supported the adhesion, proliferation and differentiation of the cultivated limbal cells and provided the antimicrobial effect against Pseudomonas aeruginosa, Staphylococcus aureus and Candida albicans.

Cells grown on bioactive matrices have immensely advanced many aspects of biomedical research related to drug delivery and tissue engineering. Our main objective was to perform simple evaluation of the structural and biotic qualities of cell scaffolds made of affordable biomaterials for liver cell line (HepG2) cultivation in vitro. In this work the electrospun matrix made of synthetic polyester poly(ε-caprolactone) (PCL) was compared with the natural protein-based extracellular matrix isolated from porcine liver (ECM). Mechanical and structural analysis showed that ECM was about 12 times less resistant to tensile stress while it had significantly larger pore size and twice smaller water contact angle than PCL. Bioactivity assessment included comparison of cell growth and transfection efficiency on cell-seeded scaffolds. Despite the differences in composition and structure between the two respective matrices, the rate of cell spreading and the percentage of transfected cells on both scaffolds were fairly comparable. These results suggest that in an attempt to produce simple, cell carrying structures that adequately simulate the natural scaffold, one can rely on PCL electrospun mats.

Since only few reported studies propose anti-vascular endothelial growth factor (anti-VEGF) delivery through electrospun scaffolds, this study greatly contributes to the potential prevention of patient’s vision loss, as it explores electrospun polycaprolactone (PCL) coated with anti-VEGF for the blockage of abnormal cornea vascularization. In terms of physicochemical properties, the biological component increased the PCL scaffold fiber diameter (by ~24%) and pore area (by ~82%), while ut slightly reduced its total porosity as the anti-VEGF solution filled the voids of the microfibrous structure. The addition of the anti-VEGF increased the scaffold stiffness almost three-fold at both strains of 5 and 10%, as well as its biodegradation rate (~36% after 60 days) with a sustained release profile after Day 4 of phosphate buffered saline incubation. In terms of scaffold application function, the PCL/Anti-VEGF scaffold proved to be more favorable for the adhesion of cultured limbal stem cells (LSCs); this was confirmed by the SEM images, where the cells showed flat and elongated conformations. Further support of the LSC growth and proliferation was confirmed by the identified p63 and CK3 markers after cell staining. These results demonstrate the advantageous effect of the surface-adsorbed anti-VEGF to stop vision loss and help damaged corneal tissue repair.

Limbal stem cells (LSCs) are of paramount importance in corneal epithelial tissue repair. The cornea becomes opaque in case of limbal stem cell deficiency (LSCD), which may cause serious damage to the ocular visual function. There are many techniques to restore damaged epithelium, one of which is the transplantation of healthy cultured LSCs, usually onto a human amniotic membrane or onto bio-based engineered scaffolds in recent years. In this study, melt electrospun polylactic acid (PLA) was modified by silk fibroin or gelatin and further cultured with LSCs originating from three different donors. In terms of physicochemical properties, both modifications slightly increased PLA scaffold porosity (with a significantly larger pore area for the PLA/gelatin) and improved the scaffolds’ swelling percentage, as well as their biodegradation rate. In terms of the scaffold application function, the aim was to detect/visualize whether LSCs adhered to the scaffolds and to further determine cell viability (total number), as well as to observe p63 and CK3 expressions in the LSCs. LSCs were attached to the surface of microfibers, showing flattened conformations or 3D spheres in the formation of colonies or agglomerations, respectively. All scaffolds showed the ability to bind the cells onto the surface of individual microfibers (PLA and PLA/gelatin), or in between the microfibers (PLA/silk fibroin), with the latter showing the most intense red fluorescence of the stained cells. All scaffolds proved to be biocompatible, while the PLA/silk fibroin scaffolds showed the highest 98% viability of 2.9 × 10⁶ LSCs, with more than 98% of p63 and less than 20% of CK3 expressions in the LSCs, thus confirming the support of their growth, proliferation and corneal epithelial differentiation. The results show the potential of these bio-engineered scaffolds to be used as an alternative clinical approach.

This study focuses on the behavior of electrospun polyurethane fibers filled with nano, micro spheres and nanotube TiO₂, thus nTiO₂, mTiO₂ or TiNT, under real time ultraviolet (UV) radiation. Analyses were conducted using scanning electron microscopy (SEM), attenuated total reflection-Fourier transform infrared spectroscopy (ATR-FTIR), thermogravimetric analysis and differential scanning calorimetry (DSC) techniques. Significant changes of thermoplastic polyurethane (TPU) + 0.5% nTiO₂ and TPU + 0.5% mTiO₂ fibers morphology, that is, agglomerated TiO₂ particles, were observed on material surfaces due to TPU fiber degradation, also supported by FTIR spectra given as reduction in the peaks intensities after UV radiation, especially in the case of TPU + 0.5% nTiO₂. Further, after UV radiation, the initial degradation temperature reduction of the hard segment for all materials was up to 40℃. A significant reduction in the final degradation temperature (from 397.8℃ to 274.1℃) was noticed for the mTiO₂ filled fibers, suggesting their photocatalytic activity, while T_g was increased up to 20℃ for almost all fillers added to TPU, thus indicating lower molecular chain mobility upon UV radiation.