Corrosion-induced maintenance is a significant cost driver and availability degrader for aircraft structures. Although well-established analyses enable assessing the corrosion impact on structural integrity, this is not the case for fatigue nucleation and crack growth. This forces fleet managers to directly address detected corrosion to maintain flight safety. Corrosion damage occurs despite protection systems, which inevitably degrade. In particular, pitting corrosion is a common potential source of fatigue. Corrosion pits are discontinuities whose metrics can be used to predict the impact on the fatigue lives of structural components. However, a damage tolerance (DT) approach would be more useful and flexible. A potential hindrance to DT has been the assumption that corrosion-induced fatigue nucleation transitions to corrosion fatigue, about which little is known for service environments. Fortunately, several sources indicate that corrosion fatigue is rare for aircraft, and corrosion is largely confined to ground situations because aircraft generally fly at altitudes with low temperature and humidity Thus, it is reasonable to propose the decoupling of corrosion from the in-flight dynamic (fatigue) loading. This paper presents information to support this proposition, and provides an example of how a DT approach can allow deferring corrosion maintenance to a more opportune time.

Aircraft full-scale fatigue tests are expensive and time-consuming to conduct but are a critical item on the certification path of any aircraft design or modification. This paper outlines a proposal that trades cycling hours for increased detail in the teardown of a metallic test article. A method for determining the equivalent demonstrated crack size (and crack growth curve) at the mandated test life utilising the lead crack framework is demonstrated. It is considered that the test duration can be significantly reduced, whilst still achieving all the desired outcomes of a certification program.

Maintaining aircraft airworthiness to ensure the fleet's safe operation and maintain its readiness is critically dependent on accurate modelling and reliable predictions of fatigue crack growth. In this process a knowledge of the representative initial discontinuity sizes that cause fatigue crack nucleation and early growth in aircraft is essential. Here the effective pre-crack size of aluminium alloy 2024, from samples of aircraft production material and tested under aircraft spectra, are considered.