Polylactic acid (PLA) is one of the most extensively used biodegradable aliphatic polyester produced from renewable resources, such as corn starch. Due to its qualities, PLA is a leading biomaterial for numerous applications in medicine as well as in industry, replacing conventional petrochemical–based polymers. The purpose of this paper is to highlight the fracture behavior of pure PLA specimens in comparison with PLA particle insertions, (copper, aluminum and Graphene), after evaluation the mechanical properties, as well as the influence of filament angle deposition on these properties. In order to check if the filling density of the specimen influences the ultimate tensile stress (UTS), three different filling percentages (60%, 80%, and 100%) have been chosen in the experimental tests. A hierarchy concerning elongation / fiber heights after tensile testing was done. So, the highest elongation values were for simple PLA (about 4.1%), followed by PLA + Al insertion (3.2%–4%), PLA + graphene insertion (2.6%–4%) and the lowest values being for PLA with copper insertion (1.8%–2.7%). Regarding the fiber heights after fracture, the hierarchy was: the highest values was for PLA, then PLA + Al, PLA + grapheme and PLA + Cu. Finally, a correlation between fracture surfaces appearance and mechanical properties were established, being formulated the mechanism of fracture in according with filament angle deposition. Also, it was proposed a new method of evaluation of the fractured surface by measuring the dimensions of the filaments after printing Fused Deposition Modeling (FDM) and tensile testing.

This paper presents the biodegradation and cavitational erosion behavior of new zinc alloys in the ZnMgFe system. The alloys were heat-treated through homogenization at 300 °C and 400 °C, with maintenance times of 5 and 10 h each. The experimental research consisted of characterizing the structure and mechanical properties of the newly made alloys in different structural states, as well as determining their biodegradation and cavitation behavior. Biodegradability was achieved using laboratory tests in SBF, with different immersion durations (3, 7, 14, 21, or 35 days). The cavitation behavior was assessed by performing tests on a piezoceramic crystal vibrator in compliance with ASTM G32-2016, thus constructing the curves of the erosion velocity MDER(t) and the cumulative average erosion depth MDE(t). The analyses performed on the mechanical properties, microscopic images, and the cavitation parameters MDER and MDEmax (results at the end of the cavitation attack) showed the effect of the heat treatments on the structure and structural resistance to cyclic loadings of the cavitation. The double alloying of zinc with magnesium and iron may increase either the mechanical properties or the corrosion resistance to cavitation and can control the biodegradability of the resulting ZnMgFe alloy. The best heat treatment for improving these properties is homogenization at 400 °C/10 h, which may increase the cavitation erosion of zinc by up to seven times. The experimental results demonstrate that the new alloys from the ZnMgFe system are a good option for manufacturing biodegradable implants with functional in vitro properties.