Certain alkali metals (Na, K) at targeted loadings have been shown in recent decades to significantly promote the LT-WGS reaction. This occurs at alkali doping levels where a redshift in the C-H band of formate occurs, indicating electronic weakening of the bond. The C-H bond breaking of formate is the proposed rate-limiting step of the formate associative mechanism, lending support to the occurrence of this mechanism in H₂-rich environments of the LT-WGS stage of fuel processors. Continuing in this vein of research, 2%Pt/m-ZrO₂ was promoted with various levels of Cs in order to explore its influence on the rate of formate intermediate decomposition, as well as that of LT-WGS in a fixed bed reactor. In situ DRIFTS experiments revealed that Cs promoter loadings of 3.87% to 7.22% resulted in significant acceleration of the forward formate decomposition in steam at 130 °C. Of all of the alkali metals tested to date, the redshift in the formate ν(CH) band with the incorporation of Cs was the greatest. XANES difference experiments at the Pt L₂ and L₃ edges indicated that the electronic effect was not likely due to an enrichment of electronic density on Pt. CO₂ TPD experiments revealed that, unlike Na and K promoters, Cs behaves more like Rb in that the decomposition of the second intermediate in LT-WGS, carbonate species, is hindered due to (1) increased basicity of Cs, (2) the tendency of Cs to cover Pt sites that facilitate CO₂ decomposition, and (3) the tendency of Cs to increase Pt particle size as shown by EXAFS results, resulting in fewer Pt sites that facilitate CO₂ decomposition. As such, the LT-WGS rate was hindered overall and the rate-limiting step shifted to carbonate decomposition (CO₂ removal). Like its Rb counterpart, low levels of added Cs (e.g., 0.72%Cs) were found to improve the stability of the catalyst relative to the unpromoted catalyst; the stability comparison was made at similar CO conversion level as well as similar space velocity.

The decarboxylation pathway in ethanol steam reforming ultimately favors higher selectivity to hydrogen over the decarbonylation mechanism. The addition of an optimized amount of Cs to Pt/m-ZrO₂ catalysts increases the basicity and promotes the decarboxylation route, converting ethanol to mainly H₂, CO₂, and CH₄ at low temperature with virtually no decarbonylation being detected. This offers the potential to feed the product stream into a conventional methane steam reformer for the production of hydrogen with higher selectivity. DRIFTS and the temperature-programmed reaction of ethanol steam reforming, as well as fixed bed catalyst testing, revealed that the addition of just 2.9% Cs was able to stave off decarbonylation almost completely by attenuating the metallic function. This occurs with a decrease in ethanol conversion of just 16% relative to the undoped catalyst. In comparison with our previous work with Na, this amount is—on an equivalent atomic basis—just 28% of the amount of Na that is required to achieve the same effect. Thus, Cs is a much more efficient promoter than Na in facilitating decarboxylation.

The decomposition selectivity of formaldehyde during steam reforming was explored using unpromoted and sodium promoted Pt/m-ZrO₂ catalysts, and the Na content was varied (0.5%Na, 1%Na, 1.8%Na, 2.5%Na, and 5%Na). In situ DRIFTS experiments during temperature programmed reaction in flowing H₂O revealed that formaldehyde is adsorbed at reduced defect sites on zirconia, where it is converted to formate species through the addition of labile bridging OH species. Formate species achieve a maximum intensity in the range of 125–175 °C, where only slight changes in intensity are observed. Above this temperature, the formate decomposition reactivity strongly depends on the Na loading, with the optimum loadings being 1.8%Na and 2.5%Na. CO₂ temperature programmed desorption results, as well as a greater splitting observed between the formate ν_asym(OCO) and ν_sym(OCO) bands in infrared spectroscopy, indicate greater basicity is induced by the presence of Na. This strengthens the interaction between the formate -CO₂ functional group and the catalyst surface, weakening the formate C-H bond. A shift in the ν(CH) band of formate to lower wavenumbers was observed by addition of Na, especially at 1.8%Na and higher loadings. This results in enhanced decarboxylation and dehydrogenation of formate, as observed in in situ DRIFTS, temperature-programmed reaction/mass spectrometry experiments of the steam reforming of formaldehyde, and fixed bed reaction tests. For example, 2.5%Na addition of 2.5% increased the CO₂ selectivity from 83.5% to 99.5% and the catalysts achieved higher stable conversion at lower temperature than NiO catalysts reported in the open literature. At 5%Na loading, Pt sites were severely blocked, hindering H-transfer.