A method to bond silicon wafers directly at room temperature was developed. In this method, surfaces of two silicon samples are activated by argon atom beam etching and brought into contact in a vacuum. By the infrared microscope and KOH etching method, no void at the bonded interface was detected in all the specimens tested. In the tensile test, fracture occurred not at the interface but mainly in the bulk of silicon. From these results, it is concluded that the method realizes strong and tight bonding at room temperature and is promising to assemble small parts made by the silicon wafer process.

Thin copper (Cu) films of 80 nm thickness deposited on a diffusion barrier layered 8 in. silicon wafers were directly bonded at room temperature using the surface activated bonding method. A low energy Ar ion beam of 40–100 eV was used to activate the Cu surface prior to bonding. Contacting two surface-activated wafers enables successful Cu–Cu direct bonding. The bonding process was carried out under an ultrahigh vacuum condition. No thermal annealing was required to increase the bonding strength since the bonded interface was strong enough at room temperature. The chemical constitution of the Cu surface was examined by Auger electron spectroscope. It was observed that carbon-based contaminations and native oxides on copper surface were effectively removed by Ar ion beam irradiation for 60 s without any wet cleaning processes. An atomic force microscope study shows that the Ar ion beam process causes no surface roughness degradation. Tensile test results show that high bonding strength equivalent to bulk material is achieved at room temperature. The cross-sectional transmission electron microscope observations reveal the presence of void-free bonding interface without intermediate layer at the bonded Cu surfaces.

Using Ar beam etching in vacuum, strong bonding of Si wafers is attained at room temperature. With appropriate etching time, the bonding occurs spontaneously without any load to force two wafers together. However, surface roughness of the wafers increases during Ar beam etching. Because surface roughness has a strong influence on wafer bonding, long etching time degrades the bonding strength. Using atomic force microscope, we measured surface roughness enhancement caused by Ar beam etching, and investigated the relationship between surface roughness and bonding properties such as strength and interfacial voids. The results agree well with theoretical predictions using elastic theory and energy gain by bond formation. A guideline for successful room-temperature bonding is proposed from these results.