Activated carbon is the preferred adsorbent for gas and water treatment in various industry across the world due to its efficiency, reliability, and accessibility. Recently, in Malaysia, studies are mainly focused on the fabrication of activated carbon from lignocellulosic biomass-based precursors from agricultural waste such as coconut shell, rice husk, and palm kernel shell. Activated carbon fabrication is a two-step process; the precursor will first undergo carbonization, then, activation is carried out either physically or chemically to develop its porous surface for adsorption purposes. The main benefit of activated carbon is the customizable pore structure for different utilization, which can be easily achieved by the chemical activation process. The types and concentration of chemicals used for activation, pre-treatment of precursor, duration of the activation process, and the mass ratio of precursor to chemicals are proven to effectively influence the resulting pore structure. However, the chemicals used in the activation process can be harmful to the environment. Thus, the chemical recovery process is necessary after the activation process. Nonetheless, more in-depth research on producing activated carbon from abundant biomass materials with bio-based chemical agents for activation is needed to achieve an ecological and sustainable manufacturing process.

The use of bio-based polymers in place of conventional polymers gives positives effects in the sense of reduction of environmental impacts and the offsetting of petroleum consumption. As such, in this study, jatropha oil was used to prepare epoxidized jatropha oil (EJO) by the epoxidation method. The EJO was used to prepare a shape memory polymer (SMP) by mixing it with the curing agent 4-methylhexahydrophthalic anhydride (MHPA) and a tetraethylammonium bromide (TEAB) catalyst. The resulting bio-based polymer is slightly transparent and brown in color. It has soft and flexible properties resulting from the aliphatic chain in jatropha oil. The functionality of SMP was analyzed by Fourier transform infrared (FTIR) spectroscopy analysis. The thermal behavior of the SMP was measured by thermogravimetric analysis (TGA), and it showed that the samples were thermally stable up to 150 °C. Moreover, the glass transition temperature characteristic was obtained using differential scanning calorimetry (DSC) analysis. The shape memory recovery behavior was investigated. Overall, EJO/MHPA was prepared by a relatively simple method and showed good shape recovery properties.