This study assessed the impact of alkali treatment of hemp and flax fibers on mechanical properties (determined by means of the uniaxial tensile test, impact tensile strength test and hardness test), processing properties (the course of the extrusion and injection process) and usable properties (shrinkage of molded pieces, degree of water absorption) of biocomposites on the base of poly (3-hydroxybutyric-co-3-hydroxyvaleric acid) (PHBV) biopolymer. For this purpose, 1 mm of length flax and hemp fibers was surface-modified by means of aqueous solution of NaOH (sodium hydroxide) with concentrations of 2%, 5% and 10%. The composites were made using the extrusion technology. The test specimens were produced by injection molding technology. In total, eight types of biocomposites with modified and non-modified fibers were produced, and each biocomposite contained the same filler content (15 wt.%). Their properties were compared in some cases with pure PHBV polymer. In the case of biocomposites filled with hemp fibers, it was noted that an increase of the alkalizing solution concentration improved most of the tested properties of the obtained biocomposites. On the other hand, in the case of flax fibers, there was a significant decrease in most of the mechanical properties tested for the composite containing fibers etched by 10% NaOH solution. The obtained results were verified by examining fibers and the destroyed specimens with a scanning electron microscope (SEM) and an optical microscope, which confirmed, especially, the significant geometry changes of the flax fibers etched by 10% NaOH solution. This procedure also resulted in a significant change of processing properties—a composite of this fiber type required about 20 °C lower temperature during the extrusion and injection molding process in order to obtain the right product. These results lead to the important conclusion that for each filler of the plant-origin and polymer matrix, the fiber alkalization method should be selected individually in order to improve the specific properties of biocomposites.

This work is inspired by the current European policies that aim to reduce plastic waste. This is especially true of the packaging industry. The biocomposites developed in the work belong to the group of environmentally friendly plastics that can reduce the increasing costs of environmental fees in the future. Three types of short fibers (flax, hemp and wood) with a length of 1 mm each were selected as fillers (30% mass content in PHBV). The biocomposites were extruded and then processed by the injection molding process with the same technical parameters. The samples obtained in this way were tested for mechanical properties and quality of the molded pieces. A significant improvement of some mechanical properties of biocomposites containing hemp and flax fibers and quality of molded pieces was obtained in comparison with pure PHBV. Only in the case of wood–PHBV biocomposites was no significant improvement of properties obtained compared to biocomposites with other fillers used in this research. The use of natural fibers, in particular hemp fibers as a filler in the PHBV matrix, in most cases has a positive effect on improving the mechanical properties and quality of molded pieces. In addition, it should be remembered that the obtained biocomposites are of natural origin and are fully biodegradable, which are interesting and desirable properties that are a part of the current trend regarding the production and commercialization of modern biomaterials.

The development of batteries used in electric vehicles towards sustainable development poses challenges to designers and manufacturers. Although there has been research on the analysis of the environmental impact of batteries during their life cycle (LCA), there is still a lack of comparative analyses focusing on the first phase, i.e., the extraction and processing of materials. Therefore, the purpose of this research was to perform a detailed comparative analysis of popular electric vehicle batteries. The research method was based on the analysis of environmental burdens regarding the ecological footprint of the extraction and processing of materials in the life cycle of batteries for electric vehicles. Popular batteries were analyzed: lithium-ion (Li-Ion), lithium iron phosphate (LiFePO₄), and three-component lithium nickel cobalt manganese (NCM). The ecological footprint criteria were carbon dioxide emissions, land use (including modernization and land development) and nuclear energy emissions. This research was based on data from the GREET model and data from the Ecoinvent database in the OpenLCA programme. The results of the analysis showed that considering the environmental loads for the ecological footprint, the most advantageous from the environmental point of view in the extraction and processing of materials turned out to be a lithium iron phosphate battery. At the same time, key environmental loads occurring in the first phase of the LCA of these batteries were identified, e.g., the production of electricity using hard coal, the production of quicklime, the enrichment of phosphate rocks (wet), the production of phosphoric acid, and the uranium mine operation process. To reduce these environmental burdens, improvement actions are proposed, resulting from a synthesized review of the literature. The results of the analysis may be useful in the design stages of new batteries for electric vehicles and may constitute the basis for undertaking pro-environmental improvement actions toward the sustainable development of batteries already present on the market.

Spent coffee grounds (SCG) have potential as a sustainable bio-filler in poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) composites, offering an environmentally friendly approach to waste utilization. This study investigated the effect of SCG content on the mechanical, thermal, and morphological properties of PHBV biocomposites and compared them with those of composites containing wood flour and hemp fibers. The biocomposites were fabricated via extrusion and injection molding, followed by the characterization of their mechanical performance, thermal behavior, and microstructure. The results indicated that SCG increased the stiffness of PHBV but did not enhance its tensile strength due to the weak interfacial adhesion between the filler and matrix. Unlike other lignocellulosic fillers, SCG requires lower processing temperatures, which is advantageous for thermally sensitive applications. SEM analysis revealed well-dispersed SCG particles at low concentrations, but visible aggregation and interfacial voids at higher loadings. While SCG serves as an effective and cost-efficient filler for improving the stiffness of PHBV, it does not reinforce the material in the conventional sense.

The paper presents a comparative analysis of two extrusion methods of biocomposites with a poly(3-hydroxybutyrate-co-3-hydroxyvalerate acid) (PHBV) matrix filled with flax and hemp fibers in terms of biopolymer production, its processing in the further injection process, and an evaluation of the mechanical and functional properties of the products. Biocomposites containing 15% by weight of the filler were produced using single- and twin-screw extruders. The biocomposites were then processed by injection molding and then, among other things, the pressures in the mold cavity during processing were analyzed. The produced samples were tested by means of the following tests: uniaxial tensile strength, hardness, and impact tensile strength. The biocomposite’s microstructure was also analyzed using scanning electron microscopy (SEM), as were the shrinkage and water absorption of the manufactured products. In addition, thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC) tests were performed. It was found that the extrusion method changed significantly the geometry of the filler fibers and the processing capabilities of the manufactured materials. Significant differences in the mechanical and functional properties of the obtained biocomposite products were also found. On their basis, the advantages and disadvantages of both extrusion methods were discussed. Most of the obtained properties of injection products indicate the choice of single-screw extrusion. The products were characterized by slightly better mechanical properties and lower processing shrinkage. In turn, composites obtained by the screw method were characterized by lower water absorption and lower viscosity of the composite during injection molding.

This paper aims to experimentally determine the properties of the poly [(3-hydroxybutyrate)-co-(3-hydroxyvalerate)]—(PHBV)—30% hemp fiber biocomposite, which is important in terms of numerical simulations of product manufacturing, and to evaluate the mechanical properties by means of micromechanical modeling. The biocomposite was manufactured using a single-screw extruder. Specimens for testing were produced by applying the injection molding technology. Utilizing the simulation results of the plastic flow, carried out by the Moldflow Insight 2016 commercial software and the results of experimental tests, the forecasts of selected composite mechanical properties were performed by means of both numerical and analytical homogenization methods. For this purpose, the Digimat software was applied. The necessary experimental data to perform the calculations for the polymer matrix, fibers, and the biocomposite were obtained by rheological and thermal studies as well as elementary mechanical tests. In the paper, the method of determining selected properties of the biocomposite and the method of forecasting its other properties are discussed. It shows the dependence of the predicted, selected properties of the biocomposite on the filler geometry assumed in the calculations and the homogenization method adopted for the calculations. The results of the work allow for the prediction of properties of the PHBV biocomposites—hemp fiber for any amount of filler used. Moreover, the results allow for the estimation of the usefulness of homogenization methods for the prediction of properties of the PHBV-hemp fiber biocomposites. Furthermore, it was found that for the developed and tested biocomposites, the most effective possibility of mechanical properties prediction is using the Mori-Tanaka homogenization model, which unfortunately has some limitations.