Spent coffee grounds (SCG) have potential as a sustainable bio-filler in poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) composites, offering an environmentally friendly approach to waste utilization. This study investigated the effect of SCG content on the mechanical, thermal, and morphological properties of PHBV biocomposites and compared them with those of composites containing wood flour and hemp fibers. The biocomposites were fabricated via extrusion and injection molding, followed by the characterization of their mechanical performance, thermal behavior, and microstructure. The results indicated that SCG increased the stiffness of PHBV but did not enhance its tensile strength due to the weak interfacial adhesion between the filler and matrix. Unlike other lignocellulosic fillers, SCG requires lower processing temperatures, which is advantageous for thermally sensitive applications. SEM analysis revealed well-dispersed SCG particles at low concentrations, but visible aggregation and interfacial voids at higher loadings. While SCG serves as an effective and cost-efficient filler for improving the stiffness of PHBV, it does not reinforce the material in the conventional sense.

Monotonic behaviour of typical Al-Cu-Mg alloy pre-strained at elevated temperature

The paper presents an investigation that was conducted to determine the possibility of the occurrence of the process of dynamic recrystallization in 2024 alloy during monotonic tensile and creep tests at the elevated temperatures of 100 °C, 200 °C, and 300 °C. As-extruded material was subjected to creep process with constant force at elevated temperatures, until two varying degrees of deformation were reached. After cooling at ambient temperature, the pre-deformed material was subjected to monotonic and fatigue tests as well as metallographic analysis. The process of dynamic recrystallization was determined in monotonic tests to occur at low strain rate (0.0015/s) only at the temperature of 300 °C. However, in the creep tests, this process occurred with varying efficiency, both during creep at 200 °C and 300 °C. Dynamic recrystallization was indicated to have a significant influence on the monotonic and cyclic properties of the material.

The paper is focused on creep-rupture tests of samples made of the 2024 alloy in the T3511 temper under uniaxial tensile stress conditions. The basic characteristics of the material at the temperatures of 100, 200 and 300 °C were determined, such as the Young’s modulus E, yield point σ_y, ultimate tensile strength σ_c and parameters K and n of the Ramberg–Osgood equation. Creep tests were performed for several different levels of nominal axial stress (load) at each temperature. It was observed that in the process of creep to failure at 200 and 300 °C, as the stress decreases, the creep time increases and, at the same time, the strain at rupture increases. However, such a regularity is maintained until a certain transition stress value σ_t is reached. Reducing the stress below this value results in a decreased value of the strain at rupture. A simple model of creep damage accumulation was proposed for the stress range above the transient value. In this model, the increase in the isotropic damage state variable was made dependent on the value of axial stress and the increase in plastic axial strain. Using the results of experimental creep-rupture tests and the failure condition, the parameters of the proposed model were determined. The surface of fractures obtained in the creep tests with the use of SEM technology was also analyzed.