In this work, the implementation of advanced functional coatings based on the combination of two compatible nanofabrication techniques such as electrospinning and dip-coating technology have been successfully obtained for the design of antifungal surfaces. In a first step, uniform and beadless electrospun nanofibers of both polyethylene oxide (PEO) and polyethylene (PEO)/chitosan (CS) blend samples have been obtained. In a second step, the dip-coating process has been gradually performed in order to ensure an adequate distribution of silver nanoparticles (AgNPs) within the electrospun polymeric matrix (PEO/CS/AgNPs) by using a chemical reduction synthetic process, denoted as in situ synthesis (ISS). Scanning electron microscopy (SEM) has been used to evaluate the surface morphology of the samples, showing an evolution in average fiber diameter from 157 ± 43 nm (PEO), 124 ± 36 nm (PEO/CS) and 330 ± 106 nm (PEO/CS/AgNPs). Atomic force microscopy (AFM) has been used to evaluate the roughness profile of the samples, indicating that the ISS process induced a smooth roughness surface because a change in the average roughness Ra from 84.5 nm (PEO/CS) up to 38.9 nm (PEO/CS/AgNPs) was observed. The presence of AgNPs within the electrospun fiber mat has been corroborated by UV-Vis spectroscopy thanks to their characteristic optical properties (orange film coloration) associated to the Localized Surface Plasmon Resonance (LSPR) phenomenon by showing an intense absorption band in the visible region at 436 nm. Energy dispersive X-ray (EDX) profile also indicates the existence of a peak located at 3 keV associated to silver. In addition, after doping the electrospun nanofibers with AgNPs, an important change in the wettability with an intrinsic hydrophobic behavior was observed by showing an evolution in the water contact angle value from 23.4° ± 1.3 (PEO/CS) up to 97.7° ± 5.3 (PEO/CS/AgNPs). The evaluation of the antifungal activity of the nanofibrous mats against Pleurotus ostreatus clearly indicates that the presence of AgNPs in the outer surface of the nanofibers produced an important enhancement in the inhibition zone during mycelium growth as well as a better antifungal efficacy after a longer exposure time. Finally, these fabricated electrospun nanofibrous membranes can offer a wide range of potential uses in fields as diverse as biomedicine (antimicrobial against human or plant pathogen fungi) or even in the design of innovative packaging materials for food preservation.

In this work, an optical fiber sensor based on the localized surface plasmon resonance (LSPR) phenomenon has been designed for the detection of two different chemical species (mercury and hydrogen peroxide) by using Layer-by-Layer Embedding (LbL-E) as a nanofabrication technique. In the first step, silver nanoparticles (AgNPs) and gold nanoparticles (AuNPs) have been synthesized by using a chemical protocol as a function of the strict control of three main parameters, which were polyelectrolyte concentration, a loading agent, and a reducing agent. In the second step, their incorporation into nanometric thin films have been demonstrated as a function of the number of bilayers, which shows two well-located absorption peaks associated to their LSPR in the visible region at 420 nm (AgNPs) and 530 nm (AuNPs). Finally, both plasmonic peaks provide a stable real-time reference measurement, which can be extracted from the spectral response of the optical fiber sensor, which shows a specific sensing mechanism as a function of the analyte of study.

This work reports the design and characterization of functional photocatalytic coatings based on the combination of two different deposition techniques. In a first step, a poly(acrylic acid) + β-Cyclodextrin (denoted as PAA+ β-CD) electrospun fiber mat was deposited by using the electrospinning technique followed by a thermal treatment in order to provide an enhancement in the resultant adhesion and mechanical resistance. In a second step, a layer-by-layer (LbL) assembly process was performed in order to immobilize the metal oxide particles onto the previously electrospun fiber mat. In this context, titanium dioxide (TiO₂) was used as the main photocatalytic element, acting as the cationic element in the multilayer LbL structure. In addition, two different metal oxides, such as tungsten oxide (WO₃) and iron oxide (Fe₂O₃), were added into PAA anionic polyelectrolyte solution with the objective of optimizing the photocatalytic efficiency of the coating. All of the coatings were characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM) images, showing an increase in the original fiber diameter and a decrease in roughness of the mats because of the LbL second step. The variation in the wettability properties from a superhydrophilic surface to a less wettable surface as a function of the incorporation of the metal oxides was also observed by means of water contact angle (WCA) measurements. With the aim of analyzing the photocatalytic efficiency of the samples, degradation of methyl blue (MB) azo-dye was studied, showing an almost complete discoloration of the dye in the irradiated area. This study reports a novel combination method of two deposition techniques in order to obtain a functional, homogeneous and efficient photocatalytic coating.

The machinability of Waspaloy, a nickel-based superalloy widely used in aerospace applications due to its excellent mechanical and thermal properties, presents significant challenges during machining processes. This study experimentally investigates the influence of two heat treatment conditions (solution annealing and age hardening) as well as the effect of coolant pressure (conventional and high-pressure cooling) on cutting forces, tool wear, and chip morphology during the turning of Waspaloy. Quantitative and qualitative analyses were performed on tool wear types including rake face, flank, and notch wear, while chip morphology was also evaluated to gain deeper insight into the machinability behavior. The results show that high pressure cooling (HPC) improves machinability by reducing cutting forces and minimizing wear, particularly in solution-annealed, large grain samples. In contrast, age-hardened specimens with conventional cooling exhibited the highest wear and cutting forces due to increased hardness and insufficient thermal dissipation. Overall, the findings highlight that both coolant pressure and heat treatment significantly influence the wear mechanisms and cutting performance, with HPC and lower hardness conditions enhancing the machinability of Waspaloy. This work uniquely combines the effects of dual heat treatments and cooling pressures to comprehensively evaluate their combined impact on Waspaloy machinability, providing new insights into optimizing cutting performance and tool life for this challenging superalloy.

This work presents a comparative study related to the photocatalytic efficiency associated with wettability measurements and organic dye degradation, as well as other relevant properties (i.e., corrosion resistance, roughness, wettability, and adhesion to a substrate). The photocatalytic precursors are titanium dioxide nanoparticles (TiO₂ NPs) which are dispersed onto a polymeric electrospun fiber matrix by using three different deposition techniques such as electrospraying, spraying, and dip-coating, respectively. In this work, the host electrospun matrix is composed of poly(acrylic acid) fibers crosslinked with cyclodextrin (β-CD), which shows a good chemical affinity and stability with the other deposition techniques which are responsible for incorporating the TiO₂ NPs. In order to evaluate the efficacy of each coating, the resultant photocatalytic activity has been monitored by two different tests. Firstly, the reduction in the water contact angle is appreciated, and secondly, the degradation of an organic dye (Rhodamine B) is observed under UV irradiation. In addition, the final roughness, adherence, and pitting corrosion potential have also been controlled in order to determine which solution provides the best combination of properties. Finally, the experimental results clearly indicate that the presence of TiO₂ NPs deposited by the three techniques is enough to induce a super hydrophilic behavior after UV irradiation. However, there are notable differences in photocatalytic efficiency on the Rhodamine B as a function of the selected deposition technique.

The accurate prediction of weld bead geometry is crucial for ensuring the quality and consistency of wire and arc additive manufacturing (WAAM), a specific form of directed energy deposition (DED) that utilizes arc welding. Despite advancements in process control, predicting the shape and dimensions of weld beads remains challenging due to the complex interactions between process parameters and material behavior. This paper addresses this challenge by exploring the application of symmetrical neural networks to enhance the accuracy and reliability of geometric predictions in WAAM. By leveraging advanced machine learning techniques and incorporating the inherent symmetry of the welding process, the proposed models aim to precisely forecast weld bead geometry. The use of neuronal networks and experimental validation demonstrate the potential of symmetrical neural networks to improve prediction precision, contributing to more consistent and optimized WAAM outcomes.