PtM/C (M = Co, Ni, Cu, Ru) catalysts were prepared by wet-synthesis methods. The composition and structure of the synthesized materials were estimated by TXRF, XRD, TEM, HAADF-STEM, EDX, and TGA/DSC methods. According to the CV and LSV methods, the PtCu/C material is characterized by the highest activity in the ORR compared to the other materials studied. The PtRu/C catalysts also exhibit the highest activity in the MOR. Studying the durability of the obtained bimetallic catalysts using accelerated stress testing has allowed for the detection of the most promising materials, whose characteristics would be superior to those of the commercial Pt/C analog. This study has shown that wet-synthesis methods allow obtaining bimetallic catalysts characterized by higher activity and enhanced durability. This research also indicates that special attention should be given to the possibility of scaling these synthesis techniques, which makes the aforementioned catalysts promising for commercial applications.

A carbon supported PtCu_x/C catalyst, which demonstrates high activity in the oxygen electroreduction and methanol electrooxidation reactions in acidic media, has been obtained using a method of chemical reduction of Pt (IV) and Cu (2+) in the liquid phase. It has been found that the potential range of the preliminary voltammetric activation of the PtCu_x/C catalyst has a significant effect on the de-alloyed material activity in the oxygen electroreduction reaction (ORR). High-resolution transmission electron microscopy (HRTEM) demonstrates that there are differences in the structures of the as-prepared material and the materials activated in different potential ranges. In this case, there is practically no difference in the composition of the PtCu_x-y/C materials obtained after activation in different conditions. The main reason for the established effect, apparently, is the reorganized features of the bimetallic nanoparticles’ surface structure, which depend on the value of the limiting anodic potential in the activation process. The effect of the activation conditions on the catalyst’s activity in the methanol electrooxidation reaction is less pronounced.

New highly active electrocatalysts were obtained by depositing bimetallic Pt-Cu nanoparticles on the surface of an N-doped carbon support. The structural–morphological characteristics and electrochemical behavior of the catalysts were studied. Using current stress testing protocols, their resistance to degradation was assessed in comparison with that of a commercial Pt/C material. A combined approach to catalyst synthesis that consists in alloying platinum with copper and doping the support makes it possible to obtain catalysts with a uniform distribution of bimetallic nanoparticles on the carbon surface. The obtained catalysts exhibit high activity and durability.

This review considers the features of the catalysts with different nanoparticle structures architecture transformation under the various pre-treatment types. Based on the results of the publications analysis, it can be concluded that the chemical or electrochemical activation of bimetallic catalysts has a significant effect on their composition, microstructure, and catalytic activity in the oxygen reduction reaction. The stage of electrochemical activation is recommended for use as a mandatory catalyst pre-treatment to obtain highly active de-alloyed materials. The literature is studied, which covers possible variants of the structural modification under the influence of thermal treatment under different processing conditions. Additionally, based on the literature data analysis, recommendations are given for the thermal treatment of catalysts alloyed with various d-metals.