In this work, the effect of secondary-phase precipitation on the microstructure, mechanical properties, and corrosion resistance of 00Cr27Ni7Mo5N hyper-duplex stainless steel (HDSS) during solution treatment was investigated. The results reveal that σ-phase precipitates at the interface between the α and γ phase when the solution treatment temperature is lower than 1070 °C. It is not only brittle, but also prone to create a Cr-depleted zone, which significantly deteriorates the mechanical properties and corrosion resistance. With the increase in the solution treatment temperature, the volume fraction of ferrite gradually increases. The yield strength and tensile strength increase slightly, but the elongation decreases. At the same time, the impact toughness shows a trend of first increasing and then decreasing. When the solution treatment temperature is higher than 1130 °C, Cr₂N precipitates in the ferrite. The precipitation of Cr₂N causes a decrease in the plastic toughness, but it does not deteriorate the mechanical properties as significantly as the σ phase. However, it can also cause the formation of a Cr-depleted zone that significantly decreases the corrosion resistance. There is no secondary-phase precipitation in the sample after solution treatment at 1100 °C, which shows the best mechanical properties and corrosion resistance.

Capacitance-based methods are widely used to evaluate lubricant film thickness in machine elements where direct optical access is unavailable, especially in rolling bearings and other multi-contact components. This review examines the physical basis, historical development, and modern methodological routes of capacitance-based film thickness determination, with emphasis on four coupled interpretive layers: film geometry, dielectric response, electrical topology, and parasitic/background effects. The literature shows that the field has evolved from simple dielectric-gap conversion toward more strongly constrained interpretation using elastohydrodynamic lubrication priors, dielectric identification, network-aware reduction, and frequency-domain information, particularly under grease lubrication, starvation, and transient conditions. Across these studies, capacitance-derived film thickness is not a methodologically uniform quantity but an inferred result whose meaning depends on what is prescribed, what is estimated, and what ambiguity remains unresolved. The main unresolved challenges are geometry–dielectric non-uniqueness, parasitic and topology uncertainty, and limited validation under realistic operating conditions. Overall, capacitance-based film thickness determination in practical machine elements is best understood as a constrained electromechanical inference problem, and future progress will depend on stronger identifiability, more informative broadband measurements, and clearer reporting of assumptions, inference targets, and validation basis.