In this study chemical and enzymatic treatment of hemp biomass were optimized to obtain maximum ethanol production. In the first stage, physical and chemical pretreatment of hemp biomass was carried out. It was found that the Tygra variety is susceptible to alkaline treatment at an optimum concentration of 2% NaOH. Next, the effect of NaOH on the value of reducing sugars and the chemical composition of the solid fraction before and after the treatment was determined. Hemp biomass before and after the chemical treatment was analysed by FTIR spectra and SEM. The effect of enzymatic hydrolysis, i.e., substrate content, temperature, time, pH and dose of enzyme by means of Response Surface Methodology on glucose content was determined. The highest glucose value was observed at 50 °C, in time process between 48 and 72 h, and the dose of enzyme was not less than 20 FPU·g⁻¹. After the optimization of enzymatic hydrolysis two processes of ethanol fermentation from hemp biomass, SHF and SSF, were carried out. In the SHF process a 40% higher concentration of ethanol was obtained (10.51 g/L). In conclusion, hemp biomass was found to be an interesting and promising source to be used for bioethanol production.

The study investigated the effectiveness of the combination of chemical and physical methods of natural fibers’ modification. The long flax fibers were subjected to various types of modification. These were silanization, plasma modification and a combination of these methods. For the silanization process, two types of silanes were used: amino- and vinylsilane. The application of structurally different compounds allowed us to acquire knowledge about the effect of the modifier structure on its properties. Various properties of flax fibers were investigated, comparing the results before and after different modification processes. The flammability of prepared samples were tested by pyrolysis combustion flow calorimeter (PCFC). In the effect of the natural fibers’ modifications, flammability was reduced even by 30%. The thermal stability of modified fibers increased. The FTIR tests of the gases released during thermal degradation of the tested fibers allowed us to determine the important compounds and prove a lower degree of flax-fiber decomposition after modification. Flax fibers were also tested to evaluate their physical properties (linear mass, average diameter, aspect ratio and hygroscopicity). Changes in surface morphology were observed by scanning electron microscope (SEM). The properties of natural fibers improved significantly, thus contributing to an increase in their suitability for the use in composites.

Due to the threat posed by the spread of invasive plant species, there is an urgent need to develop effective methods of eradicating and managing their biomass. The aim of the study was to examine selected invasive plants in terms of their use for energy purposes and to find out whether they can be a raw material for the production of second-generation biofuels. First, their chemical compositions were determined. The higher heating value (HHV) and lower heating value (LHV) were also calculated. High values of the higher heating value, ranging from 18.490 MJ∙kg⁻¹ to 19.900 MJ∙kg⁻¹, indicate the possibility of using the biomass of invasive plants for energy purposes (combustion). All investigated invasive plant species were also subjected to the process of obtaining ethanol. This included an alkaline pretreatment with 1% sodium hydroxide, followed by a simultaneous saccharification and fermentation (SSF) process. The highest ethanol yield per ha of plants was obtained at 2.6 m³∙ha⁻¹ for the Reynoutria × bohemica biomass. The remaining species showed an ethanol yield below 2 m³∙ha⁻¹. The conducted research allows for the conclusion that the studied invasive plants can be a promising raw material for the production of bioethanol.

Due to growing popularity of composites, modification methods to obtain the best properties are searched for. The aim of the study is to reduce the flammability of textile materials using nanocomposite polymer back‐coating. Different types of carbon nanotubes (single‐ and multiwalled) and different phosphorus flame retardants (ammonium polyphosphates and melamine polyphosphate) were introduced into the resin and then the fabrics were covered by the obtained composites. Homogeneous dispersion of multiwalled carbon nanotubes in the polyurethane resin was obtained by sonification, which was confirmed by scanning electron microscopy. Flammability tests of fabrics coated by modified polyurethane resin were carried out using pyrolysis combustion flow calorimeter (PCFC) and thermal stability of textiles was evaluated. Also, organoleptic estimation of coatings was conducted (flexibility and fragility). The use of polymer nanocomposites with phophorus flame retardants as a back‐coating for textiles effectively reduces flammability and improves thermal stability of the fabric. Furthermore, the synergistic effect beetwen carbon nanotubes and phosphorous compound occurs. The resulting coatings are flexible and do not crack or change the feel of fabrics.

Currently, fossil fuels are used to produce fuels and electricity, which are finite sources and have a negative impact on the natural environment. An excellent alternative to these fuels is biofuels, such as bioethanol from waste forest biomass. Pine needles are one of the most important available forest biomass materials with s significant impact on local understory vegetation. Forest waste biomass, which is a rich source of lignocellulose, can be used in various ways, such as for the eco-economical production of bioethanol. The aim of this study was to analyze the possibilities of bioethanol production from pine needle biomass obtained from forest land following different soil preparations and logging residue management. The pine needle dry matter yield, chemical components of pine needle biomass (cellulose, hemicellulose, lignin), and the amount of ethanol yield per hectare were evaluated. The highest average yield pine needle equal to 6.17 Mg∙ha⁻¹ was observed. Bioethanol yield per hectare from this biomass was the highest for plowing with the LPZ-75 plow and was 1.08 m³∙ha⁻¹. The discussed results were confirmed by detailed statistical analysis. To sum up, the researched pine needle biomass turned out to be an interesting raw material with the potential for bioethanol production.

The effect of the surface modification of carbon nanotubes on their dispersion in the epoxy matrix: Functionalization of multi-walled carbon nanotubes (MWCNTs) has an effect on the dispersion of MWCNT in the epoxy matrix. Samples based on two kinds of epoxy resin and different weight percentage of MWCNTs (functionalized and non-functionalized) were prepared. Epoxy/carbon nanotubes composites were prepared by different mixing methods (ultrasounds and a combination of ultrasounds and mechanical mixing). CNTs modified with different functional groups were investigated. Surfactants were used to lower the surface tension of the liquid, which enabled easier spreading and reducing the interfacial tension. Solvents were also used to reduce the liquid viscosity. Some of them facilitate homogeneous dispersion of nanotubes in the resin. The properties of epoxy/nanotubes composites strongly depend on a uniform distribution of carbon nanotubes in the epoxy matrix. The type of epoxy resin, solvent, surfactant and mixing method for homogeneous dispersion of CNTs in the epoxy matrix was evaluated. The effect of CNTs functionalization type on their dispersion in the epoxy resins was evaluated on the basis of viscosity and microstructure studies.