Custom mouthguards are used in various sports disciplines as a protection for teeth, temporomandibular joints, and soft tissues of the oral cavity from impact forces. The purpose of this research was to evaluate the mechanical properties of flexible polymeric 3D-printable materials and to select a material with the most favourable physical properties for making intraoral protectors. Four 3D-printable polymeric materials were selected for the evaluation: IMPRIMO LC IBT (Scheu-Dental, Iserlohn, Germany), Keyortho IBT (EnvisionTEC, Gladbeck, Germany), IBT (Formlabs, Somerville, MA, USA), and Ortho IBT (NextDent, Utrecht, Netherlands). A total of 176 samples (44 from each material) was 3D-printed using the stereolitography (SLA) technique. Tensile strength, flexural strength, notch-toughness, Shore hardness, sorption, and solubility tests were conducted. The materials were compared using a series of analyses of variance (one-way ANOVA) with Bonferroni post hoc tests. Statistical analyses were performed with the use of IBM SPSS Statistics 28.0.0 software (IBM, New York, NY, USA). Each material was assigned a score from 1 to 4 depending on the individual test results, and tests were given indexes according to the significance of the parameter in the mouthguard protective function. The number of points obtained by each material in each test was then multiplied by the test index, and the results were tabulated. The material with the highest result among the ones studied—most suitable for the application in mouthguard fabrication—was Keyortho IBT from EnvisionTEC.

Combat sports training involves a high risk of head injury. Previously published research on head trauma exposure in MMA evaluated only the knockouts (KO), without calculating all head strikes. The aim of the research was to evaluate the total head trauma exposure during MMA competitions among male and female fighters. Two thousand four hundred and eighty-eight MMA fights from all numbered UFC events between 2000 and 2021 were analyzed. A database containing the results from officially published scorecards with information such as the outcome of a fight, its duration, number of strikes (significant and total amount of hits) depending on location and knockdowns was created. Additional video verification of the knockout technique was carried out. The athletes received an average of 2.41 significant head strikes out of a total of 6.30 head strikes per minute. Head strikes were more common in female fights than in male. Women executed more total and significant head strikes per minute than men. Head trauma caused the ending of 31.6% of all fights—more often in male fights (32.2%) than female (23.1%). It was the most common cause of knockouts—88.1%. Professional fights in mixed martial arts involve high exposure to head trauma. A careful evaluation of the risk involved in training in such a discipline is necessary to provide adequate prevention methods.

Background: During prosthodontic treatment, the averaged values of the transversal condylar inclination (TCI) and the sagittal condylar inclination (SCI) are used for articulator settings. This study evaluated different parameters of measurable mandibular movements according to skeletal classes. Methods: Seventy-five patients (mean age 30.8 ± 5.49) had a condylography using the Cadiax Compact device (Gamma Dental, Klosterneuburg, Austria) and cephalometric analysis performed. Statistical analysis was performed using R statistical software. Results: There was no statistical evidence to state that the value of SCI angle is different in I compared to II Skeletal Class. There were no statistically significant differences when comparing the I vs. III and II vs. III Skeletal Class. The lowest mean SCI angle values were found in subjects with Skeletal Class III. There were statistically significant differences in left-sided TCI between Class I and II. There was a statistically significant linear relationship between ANB angle value and SCI value. Conclusions: Due to the wide individual variation in SCI and TCI values, it is advisable to use individual measurable parameters of mandibular movements during prosthetic reconstructions. The statistically significant relationship between SCI and ANB angle can be used to individualize the articulating parameters, especially in significant skeletal disproportions.

Endotracheal intubation is a procedure performed during general anaesthesia with the use of an endotracheal tube in order to maintain a patent airway. This routinely used procedure is connected with a risk of complications within the region of the masticatory system. Trauma of teeth, their surrounding structures and the soft tissue of the oral cavity is observed in app. 1.38 per 1000 procedures. The main causes of this damage are the surgical skills and experience of the surgeon, the anatomical conditions present and the mode of conducting the procedure. In order to reduce the risk of postoperative complications, patients with a high risk of sustaining an injury during endotracheal intubation should be equipped with elastic mouthguards, which reduces the possibility of damage. The scoring in a scale of endotracheal intubation difficulty should be used for qualification for the use of such mouthguards.

Purpose: Mouthguards are commonly used in the prevention of head and mouth injuries in many sport disciplines. Elastic polymeric materials used in their fabrication absorb the energy of impact. However, decontamination procedures may cause damage to their surface causing deterioration of their properties and favouring pathogen colonization. The aim of the study was to determine the impact of different cleaning methods on mouthguard materials, surface quality. Methods: The material for the research consisted of 81 samples made from polymeric materials used for custom mouthguard fabrication - Impak, Corflex Orthodontic and Erkoflex. Samples were viewed under a scanning electron microscope after exposure to different cleaning methods. Results: Statistical analysis of tested decontamination procedures and disinfecting agents showed statistically important (p < 0.05) results for the presence of small and big separated pieces, grooves and holes. Out of all the cases the lowest indicator for occurrence was in the disinfecting spray - Aftermat. Conclusions: Considering the importance of the surface material of the mouthguard, disinfection should be the method of choice for maintaining its hygiene. Impak material samples, cleaned with the Aftermat spray, showed the lowest range of damage.

This in vitro study aimed to evaluate the hardness and color change of an ethylene-vinyl-acetate copolymer (EVA) material for mouthguards after exposition to different cleaning agent solutions and isotonic drinks. Four hundred samples were prepared and divided into four equinumerous groups (n = 100), in which there were 25 samples from each color of EVA (red, green, blue and white). The hardness, using the digital durometer, and the color coordinates (CIE L*a*b*), using the digital colorimeter, were measured before the first exposition and after 3 months of exposition to spray disinfection and incubation in the oral cavity temperature, or immersion in isotonic drinks. The values of Shore A hardness (HA) and color change (ΔE—calculated by Euclidean distance) were statistically analyzed using the Kolmogorov–Smirnov test, multiple comparison ANOVA/Kruskal–Wallis and appropriate post-hoc tests. Statistically significant changes in color and hardness between the tested groups were demonstrated after the use of agents predestined for disinfecting the surface of mouthguards on the tested samples. There were no statistically significant differences in color and hardness between the groups immersed in isotonic sport drinks potentially consumed by competitors practicing combat sports using mouthguards. Despite the changes in color and hardness after the use of disinfectants, the deviations were minor and limited to specific colors of the EVA plates. The intake of isotonic drinks practically did not change either the color or the hardness of the samples, regardless of the tested color of the EVA plates.