Efficient holmium fiber lasers have been studied as attractive laser sources operating around 2.1 μm. We report on holmium-doped silica fibers prepared by the modified chemical vapor deposition in combination with either a solution-doping method or a nanoparticle-doping method. A set of 15 fibers with various compositions was characterized and compared with respect to their fluorescence lifetime, laser slope efficiency and laser threshold. This set of fibers in wide concentration ranges allowed us to assess reliably the influence of material composition and the influence of doping method. The best-performance fibers exhibited slope efficiency 83.1%, laser threshold 155 mW and a record value of upper laser level lifetime of 1.35 ms. These results were achieved in fibers with holmium concentration lower than 800 molar ppm and Al/Ho molar ratio greater than 70. Significant differences between fibers prepared by solution doping and nanoparticle doping were not observed. The behavior of $\text{Al}_2 \text{O}_3$ nanoparticles during fiber preparation is discussed in details.

Laser sources emitting in the infrared range at around 2 µm are attracting great interest for a variety of applications like processing of transparent thermoplastic polymers in industry as well as plenty of applications in medicine, spectroscopy, gas sensing, nonlinear frequency conversion to the mid-infrared, to mention a few. Of late, fiber lasers compared to other kinds of lasers benefit from their all-fiber design, leading to a compact, robust, and well thermally manageable device. Particularly, thulium- and holmium-doped fiber lasers are the first choice in fiber lasers emitting light around 2 µm. In this paper, we give an overview of our recent results in the research on thulium- and holmium-doped optical fibers, fiber lasers, and related research topics in the 2-µm spectral range. In particular, we present, to our knowledge, the first results of improvement of pump absorption in double-clad fibers thanks to the fiber twist frozen during drawing. Finally, a brief demonstration of material processing by thulium all-fiber laser operating at 2 µm is presented.

We report on high-power thulium-doped fiber amplifiers built using a nanoparticle-doped double-clad, pedestal-style large mode area fiber. The applied nanoparticle doping technique allowed achieving uniform high doping concentrations of Al ₂ O ₃ and Tm ₂ O ₃ across the fiber core. The fiber outer layer was fluorine-doped providing a decrease in pump radiation interaction with the coating, thereby enhancing the reliability of the entire laser system under high-power operation. The laser system operating at a wavelength of 2034 nm delivered an output power of up to 441 W with a slope efficiency of 57.4%, and the electro-optical conversion efficiency of the amplifier was 25%. The 1940-nm-wavelength all-fiber amplifier seeded with a narrowband Tm-doped fiber laser provided an output power of up to 273 W with a slope efficiency as high as 61.8%. In both cases the output spectrum was characterized by a 3-dB spectral bandwidth below 160 pm. Moreover, a special splicing procedure for large mode area fibers transmitting high power radiation was proposed and successfully demonstrated.

Nanoparticle doping is an alternative approach the conventional solution doping method allowing the preparation of active optical fibers with improved optical and structural properties. The combination of the nanoparticle doping with MCVD process has brought new technological challenges. We present the preparation of fiber lasers doped with Er-doped yttrium aluminum garnet (Er:YAG) nanocrystals. These nanocrystals, prepared by a hydrothermal reaction, were analyzed by several structural methods to determine the mean nanocrystal size and an effective hydrodynamic radius. The nanocrystals were incorporated into silica frits with various porosity made by the conventional MCVD process. The Er:YAG-doped silica frits were processed into preforms, which were drawn into optical fibers. We studied the effect of the nanocrystal size and frit’s porosity on the final structural and optical properties of prepared preforms and optical fibers. Selected optical fibers were tested as an active medium in a fiber ring laser setup and the characteristics of the laser were determined. Optimal laser properties were achieved for the fiber length of 7 m. The slope efficiency of the fiber laser was about 42%. Presented method can be simply extended to the deposition of other ceramic nanomaterials.