In this work, metal-doped titanium dioxide (TiO₂) was synthesised with the aim of improving photocatalytic degradation and antimicrobial activities; TiO₂ was doped with copper (Cu) ranging from 0.1 to 1.0 wt%. The physical and chemical properties of the Cu-doped TiO₂ nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), the Brunauer–Emmett–Teller method (BET) and diffuse reflection spectroscopy (DRS). The results revealed that the anatase phase of TiO₂ was maintained well in all the Cu-doped TiO₂ samples. No significant difference in the particle sizes or the specific surface areas was caused by increasing Cu doping. However, the band gap decreased continuously from 3.20 eV for undoped TiO₂ to 3.12 eV for 1.0 wt.% Cu-doped TiO₂. In addition, the 0.1 wt.% Cu-doped TiO₂ displayed a much greater photocatalytic degradation of methylene blue (MB) and excellent antibacterial ability for Escherichia coli (E. coli) compared to undoped TiO₂. On the other hand, the high Cu doping levels had negative impacts on the surface charge of nanoparticles and charge transfer for OH• generation, resulting in decreasing MB degradation and E. coli photokilling for 1.0 wt.% Cu-doped TiO₂.

This study utilized MIKE 11 to quantify the spatio-temporal dynamics of water quality parameters (Biochemical Oxygen Demand (BOD₅), Dissolved Oxygen (DO) and temperature) in the Long Xuyen Quadrangle area of the Vietnamese Mekong Delta. Calibrated for the year of 2019 and validated for the year of 2020, the developed model showed a significant agreement between the observed and simulated values of water quality parameters. Locations near to cage culture areas exhibited higher BOD₅ values than sites close to pond/lagoon culture areas due to the effects of numerous point sources of pollution, including upstream wastewater and out-fluxes from residential and tourism activities in the surrounding areas, all of which had a direct impact on the quality of the surface water used for aquaculture. Moreover, as aquacultural effluents have intensified and dispersed over time, water quality in the surrounding water bodies has degraded. The findings suggest that the effective planning, assessment and management of rapidly expanding aquaculture sites should be improved, including more rigorous water quality monitoring, to ensure the long-term sustainable expansion and development of the aquacultural sector in the Long Xuyen Quadrangle in particular, and the Vietnamese Mekong Delta as a whole.

The properties and photocatalytic performance of anatase nanoparticles of pure TiO₂ and a core–shell structure of TiO₂ on calcined vetiver grass leaves have been compared. Samples were fabricated by sol‐gel and heating at 450 °C for 5h.The comparison was based on data for X‐ray diffraction(XRD), UV‐Vis spectrophotometry, photoluminescence, transmission electron microscopy, specific surface area measurement, pore volume assessment, and methylene blue degradation testing. The results showed that the pure TiO2 consisted of agglomerated equiaxed nanoparticles of individual grain sizes in the range 10–20 nm. In contrast, the TiO₂‐vetiver composite exhibited a core–shell structure consisting of a carbonaceous core and TiO₂ shell of thickness 10–15nm. These features influenced the photocatalytic performance in such a way that the lower crosssectional area, greater surface area, and higher pore volume of the TiO₂ shell increased the number of active sites, reduced the charge carrier diffusion distance, and reduced the recombination rate, thereby improving the photocatalytic activity. This improvement derived from morphological characteristics rather than crystallographic, semiconducting, or optical properties. The improved performance of the TiO₂‐vetiver core–shell was unexpected since the X‐ray diffraction data showed that the crystallinity of the TiO₂ was lower than that of the pure TiO₂. These outcomes are attributed to the reducing effect of the carbon on the TiO₂ during heating, thereby facilitating the formation of oxygen vacancies, which enhance charge separation and hence photocatalysis by TiO₂.

This work demonstrates a novel method to deposit an antibacterial TiO₂ thin film on a polymer substrate at room temperature. A combination of sol–gel and photon assistance was used in the experiment in order to avoid any thermal processes of thin film crystallization. The morphological photograph of samples indicated that the TiO₂ thin film was perfectly coated on the PVC substrate without any cracks or pinholes. Chemical analysis by EDS and XPS reported that the thin film consisted of titanium (Ti), oxygen (O), and carbon (C). The Raman spectrum proved that the thin film was the anatase phase of TiO₂ and, furthermore, that it was contaminated with carbon remaining from the photon assistance process. In addition, the optical band gap of the thin film was 3.35 eV, suggesting that the photocatalytic activity of TiO₂ should occur under UV-A radiation. The bacteria viability assay was examined using E. coli and S. typhimurium as indicator strains under UV-A irradiation (365 nm) at different times. The data from OD and CFU count revealed that >97% of bacteria were killed after 60 min of irradiation, and the bacteria were completely killed at 120 min for E. coli and 180 min for S. typhimurium.