The interlamellar spacing of layered double hydroxides (LDHs) was enlarged by dodecyl sulfonate ions firstly, and then, (3-aminopropyl)triethoxysilane (APS) was chemically grafted (APS/LDHs). The structural characteristics and thermal stability of these prepared samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), reflectance Fourier transform infrared spectrometer (FTIR), thermogravimetric analysis (TG), and elemental analysis (EA) respectively. The CO2 adsorption performance was investigated adopting TG and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). The results presented that the CO2 adsorption capacity on APS/LDHs was as high as 90 mg/g and showed no obvious reduction during a five cyclic adsorption-desorption test, indicating its superior performance stability. The DRIFTS results showed that both carbamates and weakly bounded CO2 species were generated on APS/LDHs. The weakly adsorbed species was due to the different local chemical environment for CO2 capture provided by the surface moieties of LDHs like free silanol and hydrogen bonds.

Moisture control is an important part of effective maintenance program for gas-insulated switchgear (GIS). Herein, hexagonal mesoporous silica (HMS) materials were synthesized by adopting dodecylamine as a structure directing agent, which was then employed as a host for supporting polyethylenimine (PEI) without further calcinations or extraction treatment. The physicochemical properties of the silica support and composites were characterized, and the moisture adsorption capacity of these composites was determined. The reserved template agents resulted in a dramatic improvement in moisture adsorption amount. Among them, 50PEI/DHMS showed the highest adsorption value. The enhanced adsorption could be attributed to the generated hydrogen bonding between amino groups and H2O molecules and the improved diffusion of moisture into the bulk networks of PEI polymers due to its better spatial dispersion imposed by the long alkyl chains of template agents, which was confirmed by thermogravimetry results and hydrogen efficiency analysis. Moreover, the maintained terminal amino groups of templates could also function as active sites for moisture adsorption. The results herein imply that the PEI/DHMS composites could be appealing materials for capturing moisture in GIS.