Geopolymer concrete (GPC), also known as an earth friendly concrete, has been under continuous study due to its environmental benefits and potential as a sustainable alternative to conventional concrete construction. However, there is still a lack of comprehensive studies focusing on the influence of all the design mix variables on the fresh and strength properties of GPC. GPC is still a relatively new material in terms of field application and has yet to secure international acceptance as a construction material. Therefore, it is important that comprehensive studies be carried out to collect more reliable information to expand this relatively new material technology to field and site applications. This research work aims to provide a comprehensive study on the factors affecting the fresh and hardened properties of ambient cured fly ash and slag based geopolymer concrete (FS-GPC). Industrial by-products, fly ash from thermal power plants, and ground granulated blast furnace slag from steel industries were utilized to produce ambient cured FS-GPC. A series of experiments were conducted to study the effect of various parameters, i.e., slag content (10%, 20%, 30%, and 50%), amount of alkaline activator solution (AAS) (35% and 40%), sodium silicate (SS) to sodium hydroxide (SH) ratio (SS/SH = 2.0, 2.5 and 3.0), sodium hydroxide concentration (10 M, 12 M, and 14 M) and addition of extra water on fresh and mechanical properties of FS-GPC. The workability of the fresh FS-GPC mixes was measured by the slump cone test. The mechanical properties of the mixes were evaluated by compressive strength, split tensile strength, flexure strength, and static modulus tests. The results revealed that workability of FS-GPC is greatly reduced by increasing slag content, molarity of NaOH solution, and SS/SH ratio. The compressive strength was improved with an increase in the molarity of NaOH solution and slag content and a decrease in AAS content from 40% to 35%. However, the influence of SS/SH ratio on mechanical properties of FS-GPC has a varying effect. The addition of extra water to enhance the workability of GPC matrix caused a decrease in the compressive strength. The validity of the equations suggested by previous studies to estimate the tensile and flexural strength and elastic modulus of FS-GPC mixes were also evaluated. Based on the test results of this study, empirical equations are proposed to predict the splitting tensile strength, flexural strength, and elastic modulus of ambient cured FS-GPC. The optimal mixtures of FS-GPC in terms of workability and mechanical properties were also proposed for the field applications.

In this study, bentonite (a naturally occurring pozzolana) was incorporated as a partial replacement (up to 20%) for high-calcium fly ash (HCFA)-based geopolymeric natural aggregate concrete (GNAC) and geopolymeric recycled aggregate concrete (GRAC). The mechanical (compressive strength and splitting tensile strength), durability (chloride migration coefficient, water absorption, and acid attack resistance), and rheological properties (slump test, fresh density, and workability) were investigated. The results revealed that incorporation of bentonite (10 wt % with ordinary Portland cement) showed appreciable improvement in the strength and durability of both the GNAC and GRAC, though its effect is more significant for GRAC than the GNAC.

Pakistan has experienced several devastating earthquakes, including the 2005 Kashmir earthquake, which resulted in significant loss of life and damage. Mingora City, located in Seismic Zone 3, is particularly vulnerable and requires seismic evaluations and retrofitting of buildings to prevent future casualties and building collapses. Due to the high costs and complexity of seismic assessments, it is impractical to assess all buildings. This study used the FEMA P-154 Rapid Visual Screening (RVS) method to assess 210 buildings. The study also examined local residents’ risk perceptions through interviews. Findings revealed that most buildings had plan and vertical irregularities, such as short columns or soft storeys, and over 90% of buildings fall within damage grades 4 and 5, highlighting the urgent need for retrofitting. Poor construction quality and lack of maintenance were also noted, with 37% of buildings showing damage. Public awareness of earthquake safety was low, and 89.5% of residents agreed on the need for better education. The study highlights the need for public awareness campaigns on earthquake risks and safety.

The purpose of this research is to study the effects of quarry rock dust (QRD) and steel fibers (SF) inclusion on the fresh, mechanical, and microstructural properties of fly ash (FA) and ground granulated blast furnace slag (SG)-based geopolymer concrete (GPC) exposed to elevated temperatures. Such types of ternary mixes were prepared by blending waste materials from different industries, including QRD, SG, and FA, with alkaline activator solutions. The multiphysical models show that the inclusion of steel fibers and binders can enhance the mechanical properties of GPC. In this study, a total of 18 different mix proportions were designed with different proportions of QRD (0%, 5%, 10%, 15%, and 20%) and steel fibers (0.75% and 1.5%). The slag was replaced by different proportions of QRD in fly ash, and SG-based GPC mixes to study the effect of QRD incorporation. The mechanical properties of specimens, i.e., compressive strength, splitting tensile strength, and flexural strength, were determined by testing cubes, cylinders, and prisms, respectively, at different ages (7, 28, and 56 days). The specimens were also heated up to 800 °C to evaluate the resistance of specimens to elevated temperature in terms of residual compressive strength and weight loss. The test results showed that the mechanical strength of GPC mixes (without steel fibers) increased by 6–11%, with an increase in QRD content up to 15% at the age of 28 days. In contrast, more than 15% of QRD contents resulted in decreasing the mechanical strength properties. Incorporating steel fibers in a fraction of 0.75% by volume increased the compressive, tensile, and flexural strength of GPC mixes by 15%, 23%, and 34%, respectively. However, further addition of steel fibers at 1.5% by volume lowered the mechanical strength properties. The optimal mixture of QRD incorporated FA-SG-based GPC (QFS-GPC) was observed with 15% QRD and 0.75% steel fibers contents considering the performance in workability and mechanical properties. The results also showed that under elevated temperatures up to 800 °C, the weight loss of QFS-GPC specimens persistently increased with a consistent decrease in the residual compressive strength for increasing QRD content and temperature. Furthermore, the microstructure characterization of QRD blended GPC mixes were also carried out by performing scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectroscopy (EDS).

Bentonite is one of the SiO₂-rich pozzolanic clay types that has been enormously employed as a cost-effective and eco-friendly supplementary cementitious material in ordinary Portland cement (OPC) concrete. However, the use of bentonite in geopolymer concrete (GPC) has not been explored very widely. Further, the research available on the effect of utilizing treated bentonite in GPC is limited. The practical application of GPC is also very limited due to its significant shrinkage and high brittleness compared to OPC concrete. There are several studies available that have highlighted the use of polypropylene fibers (PPF) in improving the mechanical properties of GPC by reducing drying shrinkage and enhancing ductility. However, the effect of PPF on the durability properties of GPC needs to be addressed. Further, the effect of the combined integration of bentonite and PPF on the mechanical and durability properties of GPC has not been reported yet. The aim of this study is, therefore, to investigate the individual and combined effect of bentonite and PPF on the workability, mechanical properties, and durability of fly ash (FA)-based GPC. Bentonite replaced 10% of FA, and PPF was added at varying proportions (0.5%, 0.75%, and 1%) for raw and treated bentonite. Slump test was used to assess workability, while compressive, tensile, and flexural tests were utilized to evaluate the mechanical properties. Water absorption, acid attack, and abrasion resistance tests were used to evaluate durability. The results showed that bentonite and PPF significantly enhance mechanical properties, especially when combined with treated bentonite, with the highest improvement observed for mixtures with 1% PPF. The compressive strength was improved by an extent of 10% and 18% for raw bentonite-GPC and treated bentonite-GPC, respectively, compared to the control mix without bentonite. The durability test results revealed that water absorption of raw and treated bentonite-GPC mixtures at the age of 90 days was decreased by 16% and 21%, respectively, compared to the control mix (without bentonite). The mass loss of raw and treated bentonite-GPC mixtures in sulphuric acid solution was 5% and 10% lower, respectively, than the control mix (without bentonite). The mass loss of raw and treated bentonite-GPC mixtures in abrasion resistance tests was 6% and 12% lower, respectively, than the control mix (without bentonite). For durability performance, mixtures with 0.5% PPF perform the best, while higher PPF contents negatively impact the GPC durability.

This study presents the performance of quarry rock dust (QRD) incorporated fly ash (FA) and slag (SG) based geopolymer concretes (QFS-GPC) exposed to ambient and elevated temperatures. A total of five QFS-GPC mix types were prepared. The quantity of FA (50%) was kept constant in all the mixes, and SG was replaced by 5%, 10%, 15%, and 20% of QRD. The fresh, hardened properties of the QFS-GPC mixes, viz., workability, compressive strength, splitting tensile strength, and flexural strengths, and XRD for identification of reaction phases were evaluated. The prepared mixes were also heated up to 800 °C to evaluate the residual compressive strength and weight loss. The workability of the QFS-GPC mixes was observed to be reduced by increasing the dosage (0 to 20%) of QRD. Superplasticizer (SP) was used to maintain the medium standard of workability. The compressive, tensile, and flexural strengths were increased by replacing SG with QRD up to 15%, whereas a further higher dosage (20%) of QRD reduced the mechanical strengths of the QFS-GPC mixes. The strength of the QFS-GPC specimens, heated to elevated temperatures up to 800 °C, was reduced persistently with the increased contents of QRD from 0 to 20%. It was concluded from the study that QFS-GPC can be used to achieve 30 MPa strength of concrete.