Nanoscale thermometers with high sensitivity are needed in domains which study quantum and classical effects at cryogenic temperatures. Here, we present a micrometer sized and nanometer thick chromium selenide cryogenic temperature sensor capable of measuring a large domain of cryogenic temperatures down to tenths of K. Hexagonal Cr-Se flakes were obtained by a simple physical vapor transport method and investigated using scanning electron microscopy, energy dispersive X-ray spectrometry and X-ray photoelectron spectroscopy measurements. The flakes were transferred onto Au contacts using a dry transfer method and resistivity measurements were performed in a temperature range from 7 K to 300 K. The collected data have been fitted by exponential functions. The excellent fit quality allowed for the further extrapolation of resistivity values down to tenths of K. It has been shown that the logarithmic sensitivity of the sensor computed over a large domain of cryogenic temperature is higher than the sensitivity of thermometers commonly used in industry and research. This study opens the way to produce Cr-Se sensors for classical and quantum cryogenic measurements.

Composites of magnetite (Fe₃O₄) nanoparticles dispersed in a polydimethylsiloxane (PDMS) matrix were prepared by a molding process. Two types of samples were obtained by free polymerization with randomly dispersed particles and by polymerization in an applied magnetic field. The magnetite nanoparticles were obtained from magnetic micrograins of acicular goethite (α-FeOOH) and spherical hematite (α-Fe₂O₃), as demonstrated by XRD measurements. The evaluation of morphological and compositional properties of the PDMS:Fe₃O₄ composites, performed by SEM and EDX, showed that the magnetic particles were uniformly distributed in the polymer matrix. Addition of magnetic dispersions promotes an increase of thermal conductivity compared with pristine PDMS, while further orienting the powders in a magnetic field during the polymerization process induces a decrease of the thermal conductivity compared with the un-oriented samples. The shape of the magnetic dispersions is an important factor, acicular dispersions providing a higher value for thermal conductivity compared with classic commercial powders with almost spherical shapes.

A dual strategy for the electrochemical detection for 20S proteasome (20S) is proposed, based on the oriented immobilization of a capture monoclonal antibody (Abβ) on a self-assembled monolayer of 4-mercaptophenylboronic acid (4-MPBA) on gold electrodes, which led to the Au/4-MPBA/Abβ immunosensor. The methodology comprises the correlation of 20S concentration with (i) its proteolytic activity toward the Z-LLE-AMC substrate, using the Au/4-MPBA/Abβ/20S, and (ii) the enzymatic activity of an alkaline phosphatase (AlkP) from the AlkP-labeled secondary antibody (Ab_core-AlkP), which involves the conversion of aminophenylphosphate to the electroactive aminophenol using Au/4-MPBA/Abβ/20S/Ab_core-AlkP. The step-by-step construction of the immunosensor and the interactions at its surface were evaluated by surface plasmon resonance and gravimetric analysis with quartz crystal microbalance, showing a high affinity between both antibodies and 20S. Morphological analysis by scanning electron microscopy demonstrated a pattern of parallel lines upon immobilization of Abβ on 4-MPBA and morphological changes to a well-organized granular structure upon binding of 20S. A voltametric and impedimetric characterization was performed after each step in the immunosensor construction. The two detection strategies were evaluated. It was shown that the immunosensor responds linearly with 20S concentration in the range between 5 and 100 µg mL⁻¹, which corresponds to proteasome levels in serum in the case of diverse pathological situations, and LoD values of 1.4 and 0.2 µg mL⁻¹ were calculated for the detection strategies. The immunosensor was applied to the detection of 20S in serum samples with recovery values ranging from 101 to 103%.

The deposition of a ferromagnetic layer can affect the properties of high-temperature superconductors underneath. We investigated the influence of ferromagnetic CaRuO₃ on the properties of YBa₂Cu₃O_7-x (YBCO) superconducting thin films when the layers are either in direct contact or separated by a barrier layer of 5 nm SrTiO₃. Detailed measurements of the magnetic moment of the superconductor and ferromagnet as a function of temperature and magnetic field have been performed using SQUID magnetometry. Magnetometry and relaxation measurements show that the modification of the superconducting properties of YBCO strongly depends on the interaction with the ferromagnetic layer on top. The barrier layer has a significant impact on both the supercon-ducting properties of the YBCO film and the ferromagnetic ordering of CaRuO₃. The physical properties mentioned above were discussed in correlation with the materials’ structure determined by XRD analysis.